Polymer Property : Flexural Modulus = 1310 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Modulus 7.00 - 9.00 GPa
1020 - 1310 ksi
Injection; ISO 178
Raschig Group DECAL® 1760 Phenolic
Glass-fiber reinforced phenolic molding compound. Very good electrical properties, good chemical resistance and mechanical properties. This product meets the allowed upper limits for heavy metals an..
Flexural Modulus 6.00 - 9.00 GPa
870 - 1310 ksi
Compression; ISO 178
Raschig Group DECAL® 666/8 Phenolic
Glass-fiber reinforced phenolic molding compound with mineral fillers. High heat resistance, reduced mould shrinkage and post-shrinkage, good chemical resistance and mechanical properties. This prod..
Flexural Modulus 8.00 - 9.00 GPa
1160 - 1310 ksi
Injection and Compression; ISO 178
Raschig Group MELOPAS® 2010 MF Melamine
Organically and inorganically filled Melamine molding compound. Excellent surface hardness, good mechanical strength, good electrical properties. This product meets the allowed upper limits for heav..
Flexural Modulus 8.00 - 9.00 GPa
1160 - 1310 ksi
Injection and Compression; ISO 178
Raschig Group MELOPLAS® 150 MF
Wood flour-reinforced MF molding compound in dark colors. High surface hardness, high mechanical strength, good electrical properties. Self-extinguishing (V-O/1,6 according to UL 94), UL-listed. Fr..
Flexural Modulus 8.00 - 9.00 GPa
1160 - 1310 ksi
Injection and Compression; ISO 178
Raschig Group MELOPLAS® 152 MF
Cellulose-reinforced MF molding compound in white and colored shades. Very good electrical properties, high surface hardness, good abrasion- and UV-stability, very good resistance to chemicals - al..
Flexural Modulus 8.00 - 9.00 GPa
1160 - 1310 ksi
Injection and Compression; ISO 178
Raschig Group MELOPLAS® 152.7 MF
Cellulose-reinforced MF molding compound in white and colored shades. High surface hardness, very good UV stability, very good resistance to chemicals also to foodstuff ingredients, physiologically..
Flexural Modulus 7.00 - 9.00 GPa
1020 - 1310 ksi
Injection and Compression; ISO 178
Raschig Group MELOPLAS® 181 MF
Cellulose-reinforced, phenol-modified MF molding compound (MPF) in white and colored shades. High surface hardness, good electrical properties, good mechanical strength, high UV and heat resistanc..
Flexural Modulus 8.00 - 9.00 GPa
1160 - 1310 ksi
Injection and Compression; ISO 178
Raschig Group MELOPLAS® 181.5 MF
Cellulose-reinforced, phenol-modified MF molding compound (MPF) in white and colored shades. Very good electrical properties, high surface hardness, good mechanical strength, high UV and heat resis..
Flexural Modulus 7.00 - 9.00 GPa
1020 - 1310 ksi
Compression; ISO 178
Raschig Group MELOPLAS® 182 MF
Wood flour-reinforced and inorganically filled, phenol-modified MF molding compound (MPF) in dark colors. Improved dimensional stability and electrical properties as compared with MP 180, high surf..
Flexural Modulus 8.00 - 9.00 GPa
1160 - 1310 ksi
Injection and Compression; ISO 178
Raschig Group MELOPLAS® 183 MF
Cellulose-reinforced and inorganically filled, phenol-modified MF molding compound (MPF) in white and colored shades. Improved dimensional stability and electrical properties as compared with MP 18..
Flexural Modulus 7.00 - 9.00 GPa
1020 - 1310 ksi
Injection and Compression; ISO 178
Raschig Group MELOPLAS® 3025 MF
Cellulose-reinforced and inorganically filled MF molding compound in white and colored shades. High surface hardness, good UV and heat stability, very good resistance to chemicals - also to foodstu..
Flexural Modulus 6.00 - 9.00 GPa
870 - 1310 ksi
Compression; ISO 178
Raschig Group RALUPOL® 2100 UP Polyester
Organically and inorganically filled polyester molding compound. Low post-shrinkage, very good electrical values, good mechanical strength. This product meets the allowed upper limits for heavy meta..
Flexural Modulus 0.0130 - 9.03 GPa
1.89 - 1310 ksi
Average value: 0.356 GPa Grade Count:117
Overview of materials for Polyester Thermoplastic Elastomer
This property data is a summary of similar materials in the MatWeb database for the category "Polyester Thermoplastic Elastomer". Each property range of values reported is minimum and maximum values..
Flexural Modulus 0.373 - 9.00 GPa
54.0 - 1310 ksi
Average value: 4.01 GPa Grade Count:61
Overview of materials for Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled
This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled".Specific grades with glass content between 5% ..
Flexural Modulus 2.60 - 9.00 GPa
377 - 1310 ksi
Average value: 4.96 GPa Grade Count:18
Overview of materials for Polyetherimide (PEI), 10% Glass Fiber
This property data is a summary of similar materials in the MatWeb database for the category "Polyetherimide, 10% Glass Fiber". Specific grades with glass content between 5% and 14% are included. Ea..
Flexural Modulus 6.80 - 9.00 GPa
986 - 1310 ksi
Average value: 7.82 GPa Grade Count:31
Overview of materials for Phenolic, Novolac, Woodflour Filled
This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Woodflour Filled". Each property range of values reported is minimum and maximum valu..
Flexural Modulus 1.80 - 9.00 GPa
261 - 1310 ksi
Average value: 4.94 GPa Grade Count:10
Overview of materials for Nylon 6, Mineral Reinforced, Impact Grade
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Mineral Reinforced, Impact Grade". Each property range of values reported is minimum and maximu..
Flexural Modulus 2.76 - 9.00 GPa
400 - 1310 ksi
Average value: 5.00 GPa Grade Count:14
Overview of materials for Nylon 66, Mineral Filled, Impact Grade
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Mineral Filled, Impact Grade". Each property range of values reported is minimum and maximum v..
Flexural Modulus 7.50 - 9.00 GPa
1090 - 1310 ksi
ISO 178
Vyncolit 2923 W Novolac Phenolic
Mineral filled phenolic molding compound with excellent heat resistance and dimensional stability.Information provided by Vyncolit, a Sumitomo Bak Group
Flexural Modulus 7.00 - 9.00 GPa
1020 - 1310 ksi
ISO 178
Vyncolit 4451 XB Novolac Phenolic
Organic and mineral filled phenolic molding compound with excellent mechanical properties (highest notched impact strength).USES: Fuse holders, brush holders, circuit breakers, automotive ignition a..
Flexural Modulus 7.50 - 9.00 GPa
1090 - 1310 ksi
ISO 178
Vyncolit 2950 W Novolac Phenolic
Mineral and glass fiber filled phenolic molding compound with a very high strain to failure in flexure. UL listed.USES: Armature insulation.Information provided by Vyncolit, a Sumitomo Bak Group
Flexural Modulus 7.00 - 9.00 GPa
1020 - 1310 ksi
Injection and Compression; ISO 178
Raschig Group MELOPLAS® 180 MF
Wood flour-reinforced, phenol-modified MF molding compound (MPF) in dark colors. High surface hardness, good mechanical strength and electrical properties, good heat resistance. Self-extinguishing ..
Flexural Modulus 6.00 - 9.00 GPa

@Temperature 80.0 - 80.0 °C
870 - 1310 ksi

@Temperature 176 - 176 °F
Average value: 7.78 GPa Grade Count:9
Overview of materials for Polypropylene, Long Glass Fiber 50%
This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Long Glass Fiber 50%". Specific grades with glass content between 45% and 54% are include..
Flexural Modulus 0.239 - 9.00 GPa
34.7 - 1310 ksi
Average value: 2.42 GPa Grade Count:208
Overview of materials for Polypropylene, Mineral Reinforced
This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Mineral Reinforced". Each property range of values reported is minimum and maximum values..