Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 12.0 - 15.0 GPa | 1740 - 2180 ksi | Injection; ISO 178 |
Raschig Group 6502 DAIP Diallyl Phthalate (DAP), Cast, Mineral Filler Glass-fiber reinforced diallyl isophthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensi.. |
|||
Flexural Modulus | 10.0 - 15.0 GPa | 1450 - 2180 ksi | Injection; ISO 178 |
Raschig Group 6552 DAIP Glass-fiber reinforced diallyl isophthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensi.. |
|||
Flexural Modulus | 12.0 - 15.0 GPa | 1740 - 2180 ksi | Injection and Compression; ISO 178 |
Raschig Group EPOXIDUR® 3581 S ZC EP Epoxy Molding Compound Inorganically filled epoxy molding compound. Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures. Very good sealing connection on .. |
|||
Flexural Modulus | 1.27 - 15.0 GPa | 184 - 2180 ksi | Average value: 6.70 GPa Grade Count:6 |
Overview of materials for Thermoset Polyurethane Foam, Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Thermoset Polyurethane Foam, Glass Filled". Each property range of values reported is minimum and maximu.. |