Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 17.0 - 20.0 GPa | 2470 - 2900 ksi | Injection and Compression; ISO 178 |
Raschig Group EPOXIDUR® 3580 EP Epoxy Glass-fiber reinforced and mineral filled epoxy molding compound. Good mechanical strength, very good electrical isolation properties even with thin wall thicknesses and high temperatures. This prod.. |
|||
Flexural Modulus | 15.0 - 20.0 GPa | 2180 - 2900 ksi | Injection and Compression; ISO 178 |
Raschig Group EPOXIDUR® 3581 T-1 EP Epoxy, Molded, Glass Fiber Filler Glass-fiber reinforced and inorganically filled epoxy molding compound. Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures. Very .. |
|||
Flexural Modulus | 16.0 - 20.0 GPa | 2320 - 2900 ksi | Compression; ISO 178 |
Raschig Group RALUPOL® 4566 UP Polyester Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, good electrical values, excellent heat resistance, outstanding pourability. This product meets the allowed u.. |
|||
Flexural Modulus | 1.57 - 20.0 GPa | 228 - 2900 ksi | Average value: 2.34 GPa Grade Count:134 |
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant". Each property range of values rep.. |
|||
Flexural Modulus | 6.60 - 20.0 GPa | 957 - 2900 ksi | Average value: 11.5 GPa Grade Count:24 |
Overview of materials for Liquid Crystal Polymer (LCP), Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Liquid Crystal Polymer (LCP), Mineral Filled". Each property range of values reported is minimum and max.. |
|||
Flexural Modulus | 4.00 - 20.0 GPa | 580 - 2900 ksi | Average value: 9.89 GPa Grade Count:37 |
Overview of materials for Polyphenylene Sulfide (PPS) with 10% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 10% Glass Fiber Filler". Specific grades with glass content between 5% .. |
|||
Flexural Modulus | 3.00 - 20.0 GPa | 435 - 2900 ksi | Average value: 10.1 GPa Grade Count:21 |
Overview of materials for Nylon 12, Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12, Carbon Fiber Filled". Each property range of values reported is minimum and maximum values of .. |
|||
Flexural Modulus | 10.0 - 20.0 GPa | 1450 - 2900 ksi | Parallel to Plane |
Goodfellow Carbon-Carbon Composite Carbon Fiber - Carbon MatrixInformation provided by Goodfellow. |
|||
Flexural Modulus | 0.469 - 20.0 GPa | 68.0 - 2900 ksi | Average value: 4.97 GPa Grade Count:236 |
Overview of materials for Nylon 6, Heat Stabilized This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Heat Stabilized". Each property range of values reported is minimum and maximum values of appro.. |
|||
Flexural Modulus | 15.0 - 20.0 GPa | 2180 - 2900 ksi | Compression; ISO 178 |
Raschig Group RALUPOL® 8605 UP Polyester Glass fiber reinforced polyester molding compound. Resistant to hydrolysis. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU dire.. |