Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 2.26 GPa | 328 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Cycolac® FR15U ABS Flame retardant ABS with excellent indoor UV properties and excellent processing. UL94 V-0/5VA rated. Elevated UL RTI rating (90-85-90) for all colors except for blue and green colors (60-60-60). |
|||
Flexural Modulus | 2.26 GPa | 328 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Cycolac® FR15U ABS (Asia Pacific) Flame retardant ABS. Excellent indoor UV properties. Excellent moldability. UL94 V-0/5VA rated.ing. |
|||
Flexural Modulus | 2.26 GPa | 328 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Cycolac® FR15U ABS (Europe-Africa-Middle East) CYCOLAC FR15U is a flame retardant ABS with good processability and good indoor UV properties. |
|||
Flexural Modulus | 2.26 - 3.50 GPa | 328 - 508 ksi | Average value: 2.85 GPa Grade Count:13 |
Overview of materials for Chlorinated PVC (CPVC) This property data is a summary of similar materials in the MatWeb database for the category "Chlorinated PVC (CPVC)". Each property range of values reported is minimum and maximum values of appropr.. |
|||
Flexural Modulus | 2.26 - 7.40 GPa | 328 - 1070 ksi | Average value: 4.50 GPa Grade Count:21 |
Overview of materials for Nylon 6, 20% Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 20% Mineral Filled". Specific grades with primary filler content between 15% and 24% are includ.. |
|||
Flexural Modulus | 2.26 GPa | 328 ksi | ASTM D790 |
Kotec Carbotex K-75E Polycarbonate, Extrusion Grade Features: Extrusion, High viscosity, Natural transparentApplications: Sheets FilmsInformation provided by Kotec Corporation |
|||
Flexural Modulus | 2.26 GPa | 328 ksi | ASTM D790 |
Kotec Carbotex K-75EUV Polycarbonate, Extrusion, UV Stability Grade Features: Extrusion, High viscosity, UV stability, Blue tintsApplications: Sheets FilmsInformation provided by Kotec Corporation |
|||
Flexural Modulus | 2.26 GPa | 328 ksi | ASTM D790 |
Kotec Carbotex KV-75FD Polycarbonate, Food Grade Features: Food contact, High viscosity, Mold release, TransparentApplications: Household appliance, Kitchenware, Food packaging/containersInformation provided by Kotec Corporation |
|||
Flexural Modulus | 2.26 GPa | 328 ksi | ASTM D790 |
Hannam Chemical Hanalac H-2938 ABS |
|||
Flexural Modulus | 2.26 GPa | 328 ksi | ASTM D790 |
LG Chemical TR-558NS Transparent ABS, Antistatic, Natural and Colored Pellets LG transparent ABS has excellent transparency, impact strength, stiffness, and processability. Since its properties are well balanced, it can be applied widely to a variety of electric and electron.. |
|||
Flexural Modulus | 2.26 GPa | 328 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics NORYL PX6120 PPE+PS Noryl PX6120 is an unfilled material with good flow, high Impact and chemical resistance against cleaners. Noryl PX6120 is developed for personal care appplications. |
|||
Flexural Modulus | 2.26 GPa | 328 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics NORYL PX6120 PPE+PS (Asia Pacific) Noryl PX6120 is an unfilled material with good flow, high Impact and chemical resistance against cleaners. Noryl PX6120 is developed for personal care appplications. |
|||
Flexural Modulus | 2.26 GPa | 328 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics NORYL PX6120 PPE+PS (Europe-Africa-Middle East) Noryl PX6120 is an unfilled material with good flow, high Impact and chemical resistance against cleaners. Noryl PX6120 is developed for personal care appplications. |
|||
Flexural Modulus | 2.26 GPa | 328 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP RP003 PA 66 LNP* LUBRICOMP* RP003 is a compound based on Nylon 66 resin containing 15% PTFE/Silicone. Added feature of this material is: Wear Resistant. |
|||
Flexural Modulus | 2.26 GPa | 328 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP RP004 PA 66 LNP LUBRICOMP* RP004 is a compound based on Nylon 66 resin containing 20% PTFE/Silicone. Added features of this material include: Wear Resistant. |
|||
Flexural Modulus | 2.26 GPa | 328 ksi | ISO 178 |
SABIC Innovative Plastics LNP LUBRILOY KL201 Acetal LNP LUBRILOY* KL201 is a compound based on Acetal resin containing Proprietary Lubricant. PTFE. Added feature of this material is: Wear Resistant. |
|||
Flexural Modulus | 2.26 GPa | 328 ksi | ISO 178 |
SABIC Innovative Plastics LNP LUBRILOY KL201 Acetal (Asia Pacific) LNP LUBRILOY* KL201 is a compound based on Acetal resin containing PTFE, Proprietary Lubricant. Added features of this material include: Internally Lubricated. |
|||
Flexural Modulus | 2.26 GPa | 328 ksi | ISO 178 |
SABIC Innovative Plastics LNP LUBRILOY KL201 Acetal (Europe-Africa-Middle East) LNP LUBRILOY* KL201 is a compound based on Acetal resin containing PTFE, Proprietary Lubricant. Added features of this material include: Internally Lubricated. |
|||
Flexural Modulus | 2.26 GPa | 328 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® HX215HP PBT High Flow, Unreinforced, Polybutylene Terephthalate (PBT). For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food conta.. |
|||
Flexural Modulus | 2.26 GPa | 328 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics NORYL GTX GTX942 PPE+PS+PA66 Noryl GTX* GTX942 Resin is a blend of Polyphenylene Ether(PPE) + Polyamide(PA) resin that is designed to have high melt flow for large part/thinwall injection molding. The material is designed to h.. |
|||
Flexural Modulus | 2.26 GPa | 328 ksi | ASTM D790 |
SABIC Innovative Plastics NORYL N190 PPE+HIPS (Asia Pacific) PPE/PS, 90 oC, FR V0 |
|||
Flexural Modulus | 2.26 GPa | 328 ksi | Tangent, chs 0.05 in/min; ASTM D790 |
Diamond Polymers ABS 3501 Description: Injection Molding Grade, High ImpactInformation provided by Diamond Polymers, Inc. |
|||
Flexural Modulus | 2.26 GPa | 328 ksi | Tangent, chs 0.05 in/min; ASTM D790 |
Diamond Polymers ABS 3501 Natural 1050 Description: Natural, Injection Molding Grade, High ImpactInformation provided by Diamond Polymers, Inc. |
|||
Flexural Modulus | 2.26 GPa | 328 ksi | Tangent, chs 0.05 in/min; ASTM D790 |
Diamond Polymers ABS 3502 Description: Injection Molding Grade, High ImpactInformation provided by Diamond Polymers, Inc. |
|||
Flexural Modulus | 2.26 GPa | 328 ksi | Tangent, chs 0.05 in/min; ASTM D790 |
Diamond Polymers ABS 3502E Description: Extrusion Grade, High ImpactInformation provided by Diamond Polymers, Inc. |
|||
Flexural Modulus | 2.26 GPa | 328 ksi | Tangent, chs 0.05 in/min; ASTM D790 |
Diamond Polymers ABS 3501 HF Description: High FlowInformation provided by Diamond Polymers, Inc. |