Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 4.20 GPa @Temperature 23.0 °C |
609 ksi @Temperature 73.4 °F |
ISO 178 |
Polykemi AB POLYblend 45FS GKF2010 PC/ABS-Blend, Glass Fiber reinforced Information provided by Polykemi AB |
|||
Flexural Modulus | 4.20 GPa @Temperature 23.0 °C |
609 ksi @Temperature 73.4 °F |
ISO 178 |
Polykemi AB SCANAMID 66 A32^E Q30 Nylon 66, Mineral Reinforced Information provided by Polykemi AB |
|||
Flexural Modulus | 4.20 GPa | 609 ksi | STN EN ISO 178 |
Plastcom SLOVALEN PC 99 GF 30/1M Polypropylene reinforced with glass fiber, improved flowing Modified copolymer PP for injection molding, reinforced with 30% glass fiber, improved flowing. Applied in all industry branches. Delivered in natural mode and in the full RAL color scale.Informatio.. |
|||
Flexural Modulus | 4.20 GPa | 609 ksi | Bending Elasticity; ASTM D790 |
EVALCA EVAL® F100 Ethylene Vinyl Alcohol Copolymer Resin
(discontinued **) 32 mol % Ethylene.Data provided by EVALCA. Applications: Melt phase forming. EVOH is used in packaging applications because of its outstanding gas barrier properties.EVAL™ is now produced as a pa.. |
|||
Flexural Modulus | 4.20 GPa | 609 ksi | 2 mm/min; ISO 178 |
Inno-Comp INNOPOL® CS 1-2140 BLH 40% Talc-Filled Polypropylene Homopolymer INNOPOL® CS 1-2140 BLH is recommended especially for producing products, where high stiffness, low shrinkage, long term heat stability and excellent processability are required.All information pr.. |
|||
Flexural Modulus | 4.20 GPa | 609 ksi | ISO 178 |
Grupo Repol Dinalon® B1S25 G10B20 PA6 10% Glass Fiber, 20% Glass Beads Mechanical properties for Dry As Molded samplesInformation provided by Grupo Repol |
|||
Flexural Modulus | 4.20 GPa | 609 ksi | conditioned, 2 mm/min; ISO 178-A |
Lanxess Durethan® BKV 230 DUS008 000000 Nylon 6, 30% Glass Fiber PA 6, 30% glass fiber, injection molding, impact modified, heat-ageing stabilizedInformation provided by LANXESS. |
|||
Flexural Modulus | 4.20 GPa | 609 ksi | ISO 178 |
Kareline Oy PPMS5050 Natural Fiber Reinforced Polypropylene for injection molding Natural fiber reinforced thermoplastic composite for injection molding. Fiber ECF bleached softwood pulp. Matrix plastic polypropylen.Information provided by Kareline Oy Ltd |
|||
Flexural Modulus | 4.20 GPa | 609 ksi | |
Lehmann & Voss LUVOCOM® 1105-8127-1 PEEK, lubricant modified Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Chemical and hydrolysis resistance parts, non flammable.Improved friction and wear behavio.. |
|||
Flexural Modulus | 4.20 GPa | 609 ksi | ASTM D790 |
LG Chemical LUPOL HM-4354 Heat Resistant Polypropylene, 35% Glass Fiber/Mineral Filler Reinforced, High Strength, High Modulus LUPOL resins, based on polyolefin with a wide range of characteristics, are a family of low cost engineering plastics.Applications: Automotive: Bumper cover, instrument panel, glove box, air cleaner.. |
|||
Flexural Modulus | 4.20 GPa | 609 ksi | ISO 178 |
Solvay TECHNYL® A 218 V20 Black 21N PA66, 20% glass fiber, Conditioned Description: Polyamide PA66, reinforced with 20% of glass fiber, heat stabilized, for injection molding.Available in: EuropeProduct Applications: TECHNYL A 218 V20 is used in all sectors of industry.. |
|||
Flexural Modulus | 4.20 GPa | 609 ksi | ISO 178 |
Solvay TECHNYL® A 218C V10 PA66, 10% glass fiber, DRY Description: TECHNYL® A 218C V10 is a polyamide 66, reinforced with 10% of glass fiber, heat stabilized, for injection molding. This product is available in black color.Benefits: Due to specially.. |
|||
Flexural Modulus | 4.20 GPa | 609 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics NORYL GTX GTX985 PPE+PA66 (Asia Pacific) NORYL GTX985 is a 18% mineral filled material. This material combines high stiffness and excellent temperature resistance with conductivity for electrostatic painting. |
|||
Flexural Modulus | 4.20 GPa | 609 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics Xenoy® X5630 PC+PET Mineral filled PC/PET blend with high heat dimensional stability, low shrinkage and low CTE, especially for painted applicationsThis data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Modulus | 4.20 GPa | 609 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Xenoy® X5630 PC+PET (Asia Pacific) Mineral filled PC/PET blend with high heat dimensional stability, low shrinkage and low CTE, especially for painted applications |
|||
Flexural Modulus | 4.20 GPa | 609 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP AF002XXC ABS LNP THERMOCOMP* AF002XXC is a compound based on ABS resin containing 10% Glass Fiber. |
|||
Flexural Modulus | 4.20 GPa | 609 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP MFB44S PP (Europe-Africa-Middle East) LNP* THERMOCOMP* MFB44S is a compound based on Polypropylene resin containing Glass Fiber, Glass Beads. Added features include; Heat Stabilized, Cu-Stabilized. |
|||
Flexural Modulus | 4.20 GPa | 609 ksi | ISO 178 |
Solvay TECHNYL® A 216 V20 PA66, 20% glass fiber, Conditioned Description: Polyamide 66, reinforced with 20% of glass fiber, for injection molding.Available in: Europe Product Applications: TECHNYL® A 216 V20 is used in all sectors of industry, offering and.. |
|||
Flexural Modulus | 4.20 GPa | 609 ksi | ISO 178-93 |
Wellman Wellamid® T512-BK 15% Talc/Glass Reinforced, Dimensionally Stable Grade Nylon 6 Description: Talc/Glass Reinforced, Dimensionally Stable Grade Nylon 6Information provided by Wellman. |
|||
Flexural Modulus | 4.20 GPa | 609 ksi | ISO 178 |
Polyram PlusTek PB826G3 Nylon 6 for Injection Molding, 15% Glass-fiber Reinforced, Impact Modified and UV Stabilized 15% Glass fiber reinforced, impact modified and UV stabilized Nylon 6 for injection molding applications.Information provided by Polyram. |
|||
Flexural Modulus | 4.20 GPa @Temperature 180 °C |
609 ksi @Temperature 356 °F |
ISO 178 |
DSM Stanyl® OCD2100 BK27021 PA46-GF40 40% Glass Reinforced, Heat Stabilized |
|||
Flexural Modulus | 4.20 GPa | 609 ksi | ASTM D790 |
Cresset Powers Cress-Alon™ NF3040 4% Nano Clay Loaded, 3.0 r.v. Film Grade Nylon 6, Dry As Molded Low density, high rigidity, high heat distortion temperature, high retention of mechanical properties under humid conditions, flame retardant, recyclable and environmentally friendly, less glass fib.. |
|||
Flexural Modulus | 4.20 GPa | 609 ksi | ISO 178 |
BASF Ultramid® B3EG5 25% Glass Filled PA6 (Conditioned) Description: 25% glass-fiber reinforced injection-molding grade for industrial articles and electrical insulating partsInformation provided by BASF |
|||
Flexural Modulus | 4.20 GPa @Temperature 23.0 °C |
609 ksi @Temperature 73.4 °F |
DAM; ISO 178 |
DuPont Performance Polymers Zytel® 70GB30HSL NC010 Nylon 66 Zytel® 70GB30HSL NC010 is a 30% glass bead reinforced heat stabilized polyamide 66 resin.Information provided by DuPont Performance Polymers |
|||
Flexural Modulus | 4.20 GPa | 609 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Xenoy® X5630 PC+PET (Europe-Africa-Middle East) Mineral filled PC/PET blend with high heat dimensional stability, low shrinkage and low CTE, especially for painted applications |