Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 6.20 GPa | 899 ksi | |
Plastcom SLOVALEN PH 69 GF 45 PP, 45% glass fibre FeaturesModified homopolymer PP for injection moulding, chemically reinforced with 45% glass fibre, contains the modifier of mechanical properties.Thermo stable. Increased strength in comparison wit.. |
|||
Flexural Modulus | 6.20 GPa | 899 ksi | |
Plastcom SLOVAMID 6 NG1 GF 20 HLS PA6, 20% glass fibre, combined stability FeaturesPA 6 for injection moulding, chemically strengthened with 20% glass fibre, heat and wheather stabilized. Stabilized against hydrolisys. Good surface finisch. Scratch resistent.Packaging, tra.. |
|||
Flexural Modulus | 6.20 GPa @Temperature 23.0 °C |
899 ksi @Temperature 73.4 °F |
ISO 178 |
Polykemi AB SCANBLEND P AP2060 F20 PBT/ASA, Glass Fiber Reinforced Information provided by Polykemi AB |
|||
Flexural Modulus | 6.20 GPa | 899 ksi | ASTM D790 |
Solvay Specialty Polymers Amodel® A-1115 HS Polyphthalamide (PPA) Resin, 15% Glass Reinforced, Dry As Molded
AMODEL A-1115 HS resin is a 15% glass reinforced, heat stabilized polyphthalamide (PPA) which exhibits a high deflection temperature, high flexural modulus, and high tensile strength. Excellent cre.. |
|||
Flexural Modulus | 6.20 - 6.43 GPa | 899 - 933 ksi | Average value: 6.26 GPa Grade Count:4 |
Overview of materials for PVC, 20% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "PVC, 20% Glass Fiber Reinforced". Specific grades with glass content between 15% and 24% are included. E.. |
|||
Flexural Modulus | 6.20 GPa | 899 ksi | 2mm/min; ASTM D790 |
Kingfa JH720 G20 20% Glass Fiber Reinforced PC Features:High mechanical strengthGood size stabilityLow tendency to warpGood surfaceSuitable for exact moldingApplications:Imaging equipment shellOA body frameElectrical equipmentComputer plug parts.. |
|||
Flexural Modulus | 6.20 GPa | 899 ksi | 2mm/min; ASTM D790 |
Kingfa JH710 G20 Flame Retardant & 20% Glass Fiber Reinforced PC Features:Environmental friendly flame retardantUL V-0 @ 1.6mmHigh mechanical strengthGood size stability, good surfaceSuitable for exact moldingApplications:CD-ROM, DVDPrinter, photocopier cabinetSc.. |
|||
Flexural Modulus | 6.20 GPa | 899 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Lubricomp GFL14 PSU LNP* Lubricomp* GFL14 is a compound based on Polysulfone containing Glass Fiber and PTFE Lubricant.This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Modulus | 6.20 GPa | 899 ksi | ASTM D790 |
SABIC Innovative Plastics LNP STAT-KON SE003 PA 12 (Asia Pacific) LNP* Stat-kon* SE003 is a compound based on Nylon 12 resin containing Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
Flexural Modulus | 6.20 GPa | 899 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP DF0049E PC (Asia Pacific) LNP* Thermocomp* DF0049E is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: Easy Molding, Flame Retardant. |
|||
Flexural Modulus | 6.20 GPa | 899 ksi | 2mm/min; ISO 178 |
Teijin Multilon DN-1520B Filler Reinforced Type, Halogen-Free Flame Resistant PC/ABS Polymer Alloy Halogen-free flame retardant PC/ABS polymer alloy, and is also antimony-free. It has improved stiffness through the addition of 20 % filler. Improved stiffness and high fluidity realizes a thin wall.. |
|||
Flexural Modulus | 6.20 GPa | 899 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP MF006AS PP LNP THERMOCOMP* MF006AS is a compound based on Polypropylene resin containing 30% Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
Flexural Modulus | 6.20 GPa | 899 ksi | ASTM D 790 |
SABIC Innovative Plastics LNP Thermocomp MF006ASJ PP LNP THERMOCOMP* MF006ASJ is a compound based on Polypropylene resin containing Glass Fiber. Added features of this material include: Heat Stabilized, Healthcare.This data was supplied by SABIC-IP f.. |
|||
Flexural Modulus | 6.20 GPa | 899 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP MF006S PP LNP* THERMOCOMP* MF006S is a compound based on Polypropylene resin containing 30% Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
Flexural Modulus | 6.20 GPa | 899 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP NF004 PC+ABS (Asia Pacific) LNP* Thermocomp* NF004 is a compound based on PC+ABS Blend resin containing Glass Fiber. |
|||
Flexural Modulus | 6.20 GPa @Thickness 4.00 mm |
899 ksi @Thickness 0.157 in |
2mm/min, injection molded, unannealed; ISO 178 |
Styron EMERGEâ„¢ 5302 Acrylonitrile Butadiene Styrene (ABS) EMERGEâ„¢ ABS 5302 is a black, 20% glass-filled ABS which is suitable for use in a wide variety of internal structural component applications in the information technology market. Applications: .. |
|||
Flexural Modulus | 6.20 GPa | 899 ksi | ASTM D 790 |
SABIC Innovative Plastics LNP Thermocomp OF002A PPS LNP* Thermocomp* OF002A is a compound based on Polyphenylene Sulfide resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Modulus | 6.20 GPa | 899 ksi | ASTM D 790 |
SABIC Innovative Plastics LNP Thermocomp OF002A PPS (Asia Pacific) LNP* Thermocomp* OF002A is a compound based on Polyphenylene Sulfide resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Flexural Modulus | 6.20 GPa | 899 ksi | 2mm/min; ISO 178 |
Borealis GB311U Polypropylene Compound, Glass Fiber Reinforced GB311U is a 30% chemically coupled glass fiber reinforced polypropylene compound intended for injection molding. This material shows excellent mechanical properties also at elevated temperatures. .. |
|||
Flexural Modulus | 6.20 GPa @Temperature -40.0 °C |
899 ksi @Temperature -40.0 °F |
ASTM D790 |
Toyobo NB-5620S Nylon/Olefin Alloy, 15% Mineral Reinforced (DAM) Features: 15% Mineral Reinforced, Light WeightInformation provided by Toyobo. |
|||
Flexural Modulus | 6.20 GPa | 899 ksi | cond; ISO 178 |
DSM Novamid® 1010GN8-30 NAT PA6-GF30 FR 30% Glass Reinforced, Flame Retardant, Halogen free |
|||
Flexural Modulus | 6.20 GPa | 899 ksi | DIN 52457 |
CP-Polymer-Technik Wellamid® 6600 MF30 HWCP 30% Milled Glass Fiber Nylon 66, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
Flexural Modulus | 6.20 GPa | 899 ksi | ASTM D790 |
Adell AH-38 Nylon 66, 40% Mineral Filled Data provided by Adell Plastics, Inc. |
|||
Flexural Modulus | 6.20 GPa | 899 ksi | ASTM D790 |
A. Schulman ComAlloy Voloy® 631 Nylon 6/6, Glass Reinforced, Flow Enhanced, Flame Retardant, UL Data provided by the manufacturer, ComAlloy International Company.13% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Flexural Modulus | 6.20 GPa | 899 ksi | dry; ISO 178 |
Azoty Tarnow™ Tarnamid® T-27 GF20 GB10 Polyamide 6 - Glass Beads Reinforced 20% Glass fiber and 10% glass beads reinforced, medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has the following .. |
|||
Flexural Modulus | 6.20 GPa | 899 ksi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP DCP32 PC (Asia Pacific) LNP* Lubricomp* DCP32 is a compound based on Polycarbonate resin containing PTFE, Carbon Fiber, Silicone. Added features of this material include: Electrically Conductive, Internally Lubricated. |
|||
Flexural Modulus | 6.20 GPa | 899 ksi | ASTM D790 |
Adell AH-18 Nylon 66, 40% Mineral Filled Data provided by Adell Plastics, Inc. |
|||
Flexural Modulus | 6.20 GPa | 899 ksi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP DFP34 PC LNP* Lubricomp* DFP34 is a compound based on Polycarbonate resin containing 20% Glass Fiber, 15% PTFE/Silicone. Added features of this material include: Internally Lubricated. |
|||
Flexural Modulus | 6.20 GPa | 899 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP GF004 PSU (Asia Pacific) LNP* Thermocomp* GF004 is a compound based on Polysulfone resin containing Glass Fiber. |