Polymer Property : Flexural Modulus = 885 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	6.10 GPa	885 ksi	Tangent; ASTM D790
RheTech Products F49-01 35% Glass Fiber/Mineral Co-Reinforced Polypropylene, Chemically Coupled, Black Applications: Fan shroudsSupport ductsHousingsInjection molding conditions reported in table.Information provided by RheTech Products.
Flexural Modulus	6.10 GPa	885 ksi	ISO 178
Radici Radilon® A RCV3015 RKC Nylon 66-GF30 Automotive cooling liquid resistant PA66-GF30 grade designed to be processed by GIT technology.Information provided by Radici group.
Flexural Modulus	6.10 GPa @Temperature 23.0 °C	885 ksi @Temperature 73.4 °F	DAM; ISO 178
DuPont Performance Polymers Zytel® HTN 52GM50EF WT001 Polyphthalamide (PPA) (Unverified Data**) Zytel® HTN52GM50EF WT001 is a glass and mineral reinforced high performance polyamide resin developed for LED reflector applications. It is also a PPA resin.Information provided by DuPont Performan..
Flexural Modulus	6.10 GPa	885 ksi	ASTM D790
LATI LASTIROL R G/30 30% Glass Fiber Reinforced Polystyrene (PS) (discontinued **) Description: Lastirol thermoplastics are polystyrene (PS) products. The Lastirols feature excellent dimensional stability, good flowability, and can be molded without any particular problem. Glass f..
Flexural Modulus	6.10 GPa	885 ksi	2mm/min; ASTM D790
Kingfa PA66-G15 15% Glass Fiber Reinforced PA66 Features:Good size stabilityLow tendency to wrapHigh mechanical propertiesGood low temperature resistanceGood surfaceExcellent balance propertiesApplications:Injection moldingAutomobile partsPower t..
Flexural Modulus	6.10 GPa	885 ksi	cond., 2 mm/min; ISO 178-A
Lanxess DurethanÂ® AM 40 X H2.0 901510 Nylon 66, Glass Fiber/Mineral Reinforced PA 66, 40% glass fibers/mineral, injection molding, heat-aging stabilized, low tendency to warpInformation provided by LANXESS.
Flexural Modulus	6.10 GPa	885 ksi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP IFL34 PA 6/12 LNP* LUBRICOMP* IFL34 is a compound based on Nylon 6/12 resin containing 20% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant.
Flexural Modulus	6.10 GPa	885 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics ValoxÂ® DR48 PBT (Europe-Africa-Middle East) VALOX DR48 is a 17% glass reinforced, flame retardant injection moulding PBT resin. Applications: lamp sockets, connectors, switches, electrical housings and bases, bobbins, trimmers and electromoto..
Flexural Modulus	6.10 GPa	885 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP DF004XXC PC (Europe-Africa-Middle East) Polycarbonate compound, countaining Glass Fiber
Flexural Modulus	6.10 GPa	885 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP STAT-KON KEL22A Acetal Homopolymer (Europe-Africa-Middle East) LNP* LUBRICOMP* KEL22A is a compound based on Acetal Homopolymer resin containing Carbon Fiber, PTFE. Added features include: Electrically Conductive, Internally Lubricated.
Flexural Modulus	6.10 GPa	885 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics Noryl CRX2201 PPE+HIPS Noryl* CRX2201 resin is a 25% mineral reinforced, injection moldable modified polyphenylene ether resin designed for improved chemical resistance when compared with standard Noryl resins. Noryl CRX..
Flexural Modulus	6.10 GPa	885 ksi	ASTM D790
Chase Plastics CP Pryme® NN133GLUV (COND, 50% RH) Nylon 66, 33% Glass Fiber Reinforced, Internally Lubricated, UV Stabilized Information provided by Chase Plastics.
Flexural Modulus	6.10 GPa	885 ksi	ASTM D790
Chase Plastics CP Pryme® NN230GL (COND, 50% RH) Nylon 66, 33% Glass Fiber Reinforced, Internally Lubricated Information provided by Chase Plastics.
Flexural Modulus	6.10 GPa	885 ksi	ASTM D790
Plenco 7202 Phenolic, Granular, Injection Molded PLENCO 07202 is an organic fiber reinforced phenolic molding compound, formulated to offer improved mechanical strength properties with an industrial finish. UL recognized under component file E4065..
Flexural Modulus	6.10 GPa	885 ksi	ISO 178
Polyplastics Duranex® HN7315 Polybutylene Terephthalate (PBT), Low warpage, 15% GF filled DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers ..
Flexural Modulus	6.10 GPa @Temperature 160 °C	885 ksi @Temperature 320 °F	ISO 178
DSM Stanyl® OCD2300 BLK PA46-GF50 50% Glass Reinforced, Heat Stabilized
Flexural Modulus	6.10 GPa	885 ksi	DIN 52457
CP-Polymer-Technik Wellamid® 6000 MF 30 HWCP 30% Milled Glass Fiber Nylon 6, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG
Flexural Modulus	6.10 GPa	885 ksi	DIN 52457
CP-Polymer-Technik Wellamid® 6600 GV 20 HWCP 20% Glass Fiber Nylon 66, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG
Flexural Modulus	6.10 GPa	885 ksi	ISO Data
BASF Ultradur B 4300 G4 BK5110 20% Glass Filled PBT Ultradur B 4300 G4 BK5110 is an easy flowing, pigmented black, injection molding PBT with 20% glass fiber reinforcement for rigid, tough, and dimensionally stable parts.
Flexural Modulus	6.10 GPa	885 ksi	ISO 178
Ascend Performance Materials Vydyne® R220 Nylon 66, 40% mineral reinforced, DAM Vydyne® R220 is a 40% mineral-reinforced PA66 resin formulated for improved impact strength. Available in natural, it is an injection-molding grade formulated to retain the inherent processing adva..
Flexural Modulus	6.10 GPa	885 ksi	ISO 178
Ascend Performance Materials Vydyne® R220/R228 Nylon 66, 40% Mineral Reinforced, Dry as Molded Vydyne® R220 is a 40% mineral reinforced Nylon 66 resin formulated for improved impact strength. Also available in black as R228. It is an injection molding grade formulated to retain the inherent ..
Flexural Modulus	6.10 GPa	885 ksi	ISO 178
Ascend Performance Materials Vydyne® R228 Nylon 66, 40% Mineral Reinforced, DAM Vydyne® R228 is a 40% mineral-reinforced PA66 resin formulated for improved impact strength. Available in black, it is an injection-molding grade formulated to retain the inherent processing advant..
Flexural Modulus	6.10 GPa	885 ksi	2 [mm/min]; ISO 178
Akro-Plastic Akromid® B3 GF 20 (2470) PA 6 Dry, 20% Glass Filled AKROMID® B (Polyamide 6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperatur..
Flexural Modulus	6.10 GPa	885 ksi	ASTM D790
Ashley Polymers Ashlene® 520-25GU Nylon 66, 25% Glass Reinforced Nylon 66, 25% glass reinforced resin, utility grade.Data provided by the manufacturer
Flexural Modulus	6.10 GPa	885 ksi	ISO 527
BASF Ultramid® B35G3 BK 00564 15% Glass Filled PA6 (Dry) Description: 15% glass fiber reinforced injection molding grade e.g. for internal gas pressure applications such as flashing direction switch gears, automobile mirror housings and wheels of mountain..
Flexural Modulus	6.10 GPa	885 ksi	2 mm/min; ISO 178
Covestro Makroblend® UT4045 G PC/PBT Blend, 20% Glass Filled Main characteristics:• High toughness even at low temperatures• Good chemical resistance• Good paintability• Good flowability• Low moisture intakeGrade characteristics:• Excellent chemic..
Flexural Modulus	6.10 GPa	885 ksi	ISO 178-93
Wellman Wellamid® MRB40K004-WT1 40% Mineral Reinforced Nylon 66 Description: Mineral Reinforced Nylon 66Information provided by Wellman.
Flexural Modulus	6.10 GPa	885 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics Noryl CRX2201 PPE+HIPS (Europe-Africa-Middle East) Noryl* CRX2201 resin is a 25% mineral reinforced, injection moldable modified polyphenylene ether resin designed for improved chemical resistance when compared with standard Noryl resins. Noryl CRX..