Polymer Property : Shear Strength = 20.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Shear Strength	20.0 - 32.0 MPa @Temperature 22.0 °C, Time 86400 sec	2900 - 4640 psi @Temperature 71.6 °F, Time 24.0 hour	ISO 10123; Compressive, Steel pins and collars
Palm Labs Adhesives TURBO-LOCK SERIES 17-OR Anaerobic Thread Locking Compound BEARING AND SHAFT - SERIES 17-OR is a fast curing, GREEN, high strength, oil resistant, close fit, anaerobic retaining compound for bonding, sealing and retaining of cylindrical parts. It is highly ..
Shear Strength	20.0 MPa @Temperature 26.7 Â°C	2900 psi @Temperature 80.0 Â°F	ASTM D732
Greene Tweed AvalonÂ® 16 PTFE, Glass, Molybdenum Filled Products made from AvalonÂ® thermoplastics are constructed from proprietary high-performance reinforced PTFE material. Greene, Tweeds Avalon thermoplastics, available in grades ranging from virgin..
Shear Strength	20.0 MPa @Temperature 23.9 °C	2900 psi @Temperature 75.0 °F	Cure cycle: 7 days @ RT (+7 days gasoline soak) , with Aced Etched 6061-T6 Aluminum
Zyvex Performance Materials Epovex™ Nano-Engineered Composite Epoxy Adhesive Liquid Epovex® Adhesive is a carbon nanotube enhanced ambient or elevated temperature cure two-part epoxy adhesive. Used for bonding, laminating, filling or potting, Epovex is ideal for many metals, woods..
Shear Strength	20.0 MPa @Temperature 121 °C	2900 psi @Temperature 250 °F	Lap Shear
Hexcel® Redux® 308 Modified epoxy film adhesive Redux 308 is a high-strength film adhesive curing at 350°F. It is suitable for a wide range of structural bonding applications including metal to metal bonding and sandwich constructions, where ope..
Shear Strength	20.0 MPa @Temperature 121 °C	2900 psi @Temperature 250 °F	Lap Shear
Hexcel® Redux® 308A-NA Modified epoxy film adhesive Redux 308A-NA is a high-strength, flow-controlled film adhesive with flexible cure schedules at 300°F or 350°F. Redux 308A-NA contains glass beads that give good flow control. It is suitable for m..
Shear Strength	20.0 MPa @Temperature 177 °C	2900 psi @Temperature 350 °F	Lap Shear
Hexcel® Redux® 322 Modified epoxy film adhesive (0.078 psf) Redux 322 is a high performance modified epoxy film adhesive curing at 350°F. It is suitable for bonding metal to metal and for sandwich structures, where operating temperatures are experienced up ..