Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Shear Strength 17.2 MPa

@Temperature 25.0 °C
2500 psi

@Temperature 77.0 °F
Tensile lap
Resin Technology Group TIGA 110-EXDP Low Viscosity, Optically Clear Glass Bonder
Mix ratio 100/50 by volume.TIGA 110EX-DP is a transparent, low viscosity epoxy resin formulation recommended for industrial adhesive, small potting and laminating applications where sparkling clarit..
Shear Strength 17.2 MPa

@Temperature 93.3 °C
2500 psi

@Temperature 200 °F
ASTM D732
Greene Tweed Avalon® 89 PTFE
Products made from Avalon® thermoplastics are constructed from proprietary high-performance reinforced PTFE material. Greene, Tweeds Avalon thermoplastics, available in grades ranging from virgin..
Shear Strength 17.2 MPa

@Temperature 98.9 °C
2500 psi

@Temperature 210 °F
Lap Shear
Hexcel® Redux® 312L Modified epoxy film adhesive
Redux® 312 is a high-strength 250°F curing film adhesive, suitable for metal to metal bonding and sandwich constructions, where operating temperatures of up to 210°F may be experienced. A support..
Shear Strength 17.2 MPa

@Temperature 93.3 °C
2500 psi

@Temperature 200 °F
Lap Shear
Hexcel® Redux® 335U Adhesive film for bonding metallic and composite components (0.03 psf)
Redux 335 is a film adhesive curing at 250F. It is available in a range of standard areal weights from 0.015 to 0.06 psf. It is available either unsupported or with knitted and/or matt carrier for a..
Shear Strength 17.2 MPa

@Temperature -55.0 °C
2500 psi

@Temperature -67.0 °F
Tensile Lap Shear; Aluminum No Primer; ASTM D1002
Hexcel® Redux® HP655 Toughened BMI film Adhesive
Redux® HP655 is a toughened BMI structural adhesive designed for metal to metal, composite to composite, and honeycomb sandwich bonding for both co-cured and precured composite skins. Redux® HP655..
Shear Strength 17.2 MPa

@Temperature 24.0 °C
2500 psi

@Temperature 75.2 °F
Overlap
3M Scotch-Weld™ 1838L B/A Two-Part Structural Adhesive
Multi-purpose and Rigid bondsInformation provided by 3M
Shear Strength 17.2 MPa

@Temperature 121 °C
2500 psi

@Temperature 250 °F
Aluminum Overlap
3M Scotch-Weld™ 2214 Hi-Temp Epoxy Adhesive
3M™ Scotch-Weld™ Adhesive 2214 Hi-Temp is an aluminum filled, deaerated products fro use where higher strengths are required between 82-177°C. One part 250°F (121°C) curing 100% solids, 3M™ Sc..
Shear Strength 17.2 MPa

@Temperature 149 °C
2500 psi

@Temperature 300 °F
Aluminum Overlap
3M Scotch-Weld™ 2214 Hi-Temp Epoxy Adhesive
3M™ Scotch-Weld™ Adhesive 2214 Hi-Temp is an aluminum filled, deaerated products fro use where higher strengths are required between 82-177°C. One part 250°F (121°C) curing 100% solids, 3M™ Sc..
Shear Strength 17.2 MPa

@Temperature 121 °C
2500 psi

@Temperature 250 °F
Aluminum Overlap
3M Scotch-Weld™ 2214 Hi-Temp New Formula Epoxy Adhesive
3M™ Scotch-Weld™ Adhesive 2214 Hi-Temp Formula is an aluminum filled, deaerated products fro use where higher strengths are required between 82-177°C. One part 250°F (121°C) curing 100% solids,..
Shear Strength 17.2 MPa

@Temperature 25.0 °C,
Time 86400 sec
2500 psi

@Temperature 77.0 °F,
Time 24.0 hour
Lap, Alum to Alum
Atom Adhesives AA-BOND F112 Epoxy Adhesive
AA-BOND F112 is an impact resistant, fiber-optic adhesive. AA-BOND F112 is two-part, low viscosity epoxy has the distinct advantage of remaining below 3000 cps for a minimum of 40 minutes. AA-BOND F..
Shear Strength 17.2 MPa

@Temperature 121 °C
2500 psi

@Temperature 250 °F
Overlap
3M Scotch-Weld™ 1386 One-Part Epoxy Adhesives and Metal Primer
High Temperature strength and Impact resistanceInformation provided by 3M
Shear Strength 17.2 MPa

@Temperature -40.0 °C
2500 psi

@Temperature -40.0 °F
Overlap, Etched Aluminum
3M Scotch-Weld™ 3532 B/A Two-Part Structural Adhesive
3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie..
Shear Strength 17.2 MPa

@Temperature -55.0 °C
2500 psi

@Temperature -67.0 °F
Overlap
3M Scotch-Weld™ 3532 B/A Two-Part Structural Adhesive
3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie..
Shear Strength 17.2 MPa

@Temperature -40.0 °C
2500 psi

@Temperature -40.0 °F
Overlap, Etched Aluminum
3M Scotch-Weld™ 3535 B/A Two-Part Structural Adhesive
3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie..
Shear Strength 17.2 MPa

@Temperature -55.0 °C
2500 psi

@Temperature -67.0 °F
Overlap
3M Scotch-Weld™ 3535 B/A Two-Part Structural Adhesive
3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie..
Shear Strength 17.2 MPa

@Temperature -40.0 °C
2500 psi

@Temperature -40.0 °F
Overlap, Etched Aluminum
3M Scotch-Weld™ 3549 B/A Two-Part Structural Adhesive
3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie..
Shear Strength 17.2 MPa

@Temperature -55.0 °C
2500 psi

@Temperature -67.0 °F
Overlap
3M Scotch-Weld™ 3549 B/A Two-Part Structural Adhesive
3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie..
Shear Strength 17.2 MPa

@Temperature 24.0 °C
2500 psi

@Temperature 75.2 °F
Overlap
3M Scotch-Weld™ DP270 Black Structural Adhesive
Rigid potting compound, Non-corrosiveInformation provided by 3M
Shear Strength 17.2 MPa

@Temperature 24.0 °C
2500 psi

@Temperature 75.2 °F
Overlap
3M Scotch-Weld™ DP270 Clear Structural Adhesive
Rigid potting compound, Non-corrosiveInformation provided by 3M