Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Shear Strength | 31.0 MPa @Temperature 177 °C |
4500 psi @Temperature 350 °F |
Short-Beam, Dry, Autoclave; ASTM D2344 |
Park Electrochemical Nelcote® E-746 Epoxy Prepreg, 3k 5HS Carbon Reinforced Nelcote® E-746 is a modified epoxy resin system designed to retain excellent mechanical properties after extended exposure to high temperature. E-746 has a proven history in many demanding aerospac.. |
|||
Shear Strength | 31.0 MPa @Temperature 177 °C |
4500 psi @Temperature 350 °F |
Short-Beam, Dry, Autoclave with Post-Cure; ASTM D2344 |
Park Electrochemical Nelcote® E-746 Epoxy Prepreg, 581 Quartz Reinforced Nelcote® E-746 is a modified epoxy resin system designed to retain excellent mechanical properties after extended exposure to high temperature. E-746 has a proven history in many demanding aerospac.. |
|||
Shear Strength | 31.0 MPa @Temperature -55.0 °C |
4500 psi @Temperature -67.0 °F |
Lap Shear, Cured at 250°C for 60 min at 30 psi MMM-A-132 and MIL-A-25463. |
Hexcel® Redux® 382H (0.06 psf) Film Adhesive Redux 382H is a 250°F curing modified epoxy film adhesive available in both supported and unsupported versions. Redux 382H is a versatile adhesive system suitable for bonding a wide variety of subs.. |
|||
Shear Strength | 31.0 MPa @Temperature 21.1 °C |
4500 psi @Temperature 70.0 °F |
Lap Shear |
Hexcel® Redux® 609 (0.04 psf) Adhesive film for bonding metallic and composite components Redux 609 is a 250°F curing modified epoxy film adhesive containing a cottom scrim for easy handling and glue-line thickness control. It is available at standard areal weights of 0.06 psf and 0.04 .. |
|||
Shear Strength | 31.0 MPa @Temperature 48.9 °C |
4500 psi @Temperature 120 °F |
Lap Shear |
Hexcel® Redux® 609 (0.04 psf) Adhesive film for bonding metallic and composite components Redux 609 is a 250°F curing modified epoxy film adhesive containing a cottom scrim for easy handling and glue-line thickness control. It is available at standard areal weights of 0.06 psf and 0.04 .. |
|||
Shear Strength | 31.0 MPa @Temperature 48.9 °C |
4500 psi @Temperature 120 °F |
Lap Shear |
Hexcel® Redux® 609 (0.06 psf) Adhesive film for bonding metallic and composite components Redux 609 is a 250°F curing modified epoxy film adhesive containing a cottom scrim for easy handling and glue-line thickness control. It is available at standard areal weights of 0.06 psf and 0.04 .. |
|||
Shear Strength | 31.0 MPa @Temperature 21.1 °C |
4500 psi @Temperature 70.0 °F |
Tensile Shear, Redux 775 Liquid & Powder (P:L Ration = 1.3:1) |
Hexcel® Redux® 775 Vinyl phenolic structural adhesive Redux 775 was adopted as the world's first metal-to-metal bonding process to be officially approved for use in the manufacture of aircraft primary structures in 1943. It is available either as a fil.. |
|||
Shear Strength | 31.0 MPa @Temperature 24.0 °C |
4500 psi @Temperature 75.2 °F |
Aluminum Overlap |
3M Scotch-Weld™ 2214 Hi-Dense Epoxy Adhesive 3M™ Scotch-Weld™ Adhesive 2214 Hi-Dense is a deareted version of Scotch-Weld adhesive 2214 regular for use where a very dense, void free bondline is required. One part 250°F (121°C) curing 100% .. |
|||
Shear Strength | 31.0 MPa @Temperature 82.0 °C |
4500 psi @Temperature 180 °F |
Aluminum Overlap |
3M Scotch-Weld™ 2214 Hi-Dense Epoxy Adhesive 3M™ Scotch-Weld™ Adhesive 2214 Hi-Dense is a deareted version of Scotch-Weld adhesive 2214 regular for use where a very dense, void free bondline is required. One part 250°F (121°C) curing 100% .. |
|||
Shear Strength | 31.0 MPa @Temperature 82.0 °C |
4500 psi @Temperature 180 °F |
Aluminum Overlap |
3M Scotch-Weld™ 2214 Non-Metallic Filled Epoxy Adhesive 3M™ Scotch-Weld™ Non-Metallic Filled is a non-metal filled version of Scotch-Weld adhesive 2214 regular. One part 250°F (121°C) curing 100% solids, 3M™ Scotch-Weld™ Epoxy Adhesive 2214 is a pa.. |
|||
Shear Strength | 31.0 MPa @Temperature 82.0 °C |
4500 psi @Temperature 180 °F |
Overlap |
3M Scotch-Weld™ 1386 One-Part Epoxy Adhesives and Metal Primer High Temperature strength and Impact resistanceInformation provided by 3M |
|||
Shear Strength | 31.0 MPa @Temperature 24.0 °C |
4500 psi @Temperature 75.2 °F |
Aluminum Overlap |
3M Scotch-Weld™ 2214 Regular Epoxy Adhesive 3M™ Scotch-Weld™ Adhesive 2214 Regular is an aluminum filled general purpose product for use in applications where high strength bonds are needed in a temperature range of -53-121°C.One part 250°.. |
|||
Shear Strength | 31.0 MPa @Temperature 82.0 °C |
4500 psi @Temperature 180 °F |
Aluminum Overlap |
3M Scotch-Weld™ 2214 Regular Epoxy Adhesive 3M™ Scotch-Weld™ Adhesive 2214 Regular is an aluminum filled general purpose product for use in applications where high strength bonds are needed in a temperature range of -53-121°C.One part 250°.. |