Polymer Property : Melting Point = 1415 °C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Melting Point 1330 - 1415 °C
2430 - 2579 °F
Haynes 556® alloy, 0% cold reduction
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Melting Point 1330 - 1415 °C
2430 - 2579 °F
Haynes 556® alloy, 0% cold reduction, 1065°C anneal for 5 minutes
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Melting Point 1330 - 1415 °C
2430 - 2579 °F
Haynes 556® alloy, 0% cold reduction, 1121°C anneal for 5 minutes
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Melting Point 1330 - 1415 °C
2430 - 2579 °F
Haynes 556® alloy, 10% cold reduction
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Melting Point 1330 - 1415 °C
2430 - 2579 °F
Haynes 556® alloy, 10% cold reduction, 1010°C anneal for 5 minutes
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Melting Point 1330 - 1415 °C
2430 - 2579 °F
Haynes 556® alloy, 10% cold reduction, 1065°C anneal for 5 minutes
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Melting Point 1330 - 1415 °C
2430 - 2579 °F
Haynes 556® alloy, 30% cold reduction, 1010°C anneal for 5 minutes
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Melting Point 1330 - 1415 °C
2430 - 2579 °F
Haynes 556® alloy, 30% cold reduction, 1065°C anneal for 5 minutes
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Melting Point 1330 - 1415 °C
2430 - 2579 °F
Haynes 556® alloy, 40% cold reduction, 1010°C anneal for 5 minutes
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Melting Point 1330 - 1415 °C
2430 - 2579 °F
Haynes 556® alloy, 40% cold reduction, 1121°C anneal for 5 minutes
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Melting Point 1330 - 1415 °C
2430 - 2579 °F
Haynes 556® alloy, 50% cold reduction
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Melting Point 1330 - 1415 °C
2430 - 2579 °F
Haynes 556® alloy, 50% cold reduction, 1010°C anneal for 5 minutes
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Melting Point 1330 - 1415 °C
2430 - 2579 °F
Haynes 556® alloy, 50% cold reduction, 1121°C anneal for 5 minutes
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Melting Point 1330 - 1415 °C
2430 - 2579 °F
Haynes 556® alloy, bar after 16000 hours at 537°C
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Melting Point 1330 - 1415 °C
2430 - 2579 °F
Haynes 556® alloy, bar, after 1000 hours at 760°C (1400°F)
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Melting Point 1330 - 1415 °C
2430 - 2579 °F
Haynes 556® alloy, bar, after 1000 hours at 870°C (1600°F)
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Melting Point 1330 - 1415 °C
2430 - 2579 °F
Haynes 556® alloy, bar, after 4000 hours at 650°C (1200°F)
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Melting Point 1330 - 1415 °C
2430 - 2579 °F
Haynes 556® alloy, bar, after 4000 hours at 760°C (1400°F)
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Melting Point 1330 - 1415 °C
2430 - 2579 °F
Haynes 556® alloy, bar, after 8000 hours at 760°C (1400°F)
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Melting Point 1330 - 1415 °C
2430 - 2579 °F
Haynes 556® alloy, bar, after 8000 hours at 870°C (1600°F)
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Melting Point 1330 - 1415 °C
2430 - 2579 °F
Haynes 556® alloy, sheet after 1000 hours at 648°C
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Melting Point 1330 - 1415 °C
2430 - 2579 °F
Haynes 556® alloy, sheet after 1000 hours at 760°C (1400°F)
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Melting Point 1330 - 1415 °C
2430 - 2579 °F
Haynes 556® alloy, 20% cold reduction, 1065°C anneal for 5 minutes
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Melting Point 1330 - 1415 °C
2430 - 2579 °F
Haynes 556® alloy, 20% cold reduction, 1121°C anneal for 5 minutes
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Melting Point 1330 - 1415 °C
2430 - 2579 °F
Haynes 556® alloy, 30% cold reduction, 1121°C anneal for 5 minutes
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Melting Point 1330 - 1415 °C
2430 - 2579 °F
Haynes 556® alloy, 50% cold reduction, 1065°C anneal for 5 minutes
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Melting Point 1330 - 1415 °C
2430 - 2579 °F
Haynes 556® alloy, bar after 16000 hours at 871°C (1600°F)
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Melting Point 1330 - 1415 °C
2430 - 2579 °F
Haynes 556® alloy, sheet after 1000 hours at 871°C (1600°F)
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Melting Point 1330 - 1415 °C
2430 - 2579 °F
Haynes 556® alloy, 40% cold reduction, 1065°C anneal for 5 minutes
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Melting Point 1330 - 1415 °C
2430 - 2579 °F
Haynes 556® alloy, bar, after 4000 hours at 870°C (1600°F)
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..