Thermal Properties | Metric | English | Comments |
---|---|---|---|
Melting Point | 200 - 220 °C | 392 - 428 °F | DSC; STN EN ISO 3146 |
Plastcom SLOVASTER® B GF 30 FRK 3 Polybutylene Terephthalate, 30% Chemically Coupled Glass Fiber, Red Phosphorus Flame Retardant FeaturesPBT with the content of 30% chemically coupled glass fiber and flame retardant based on red phosphorus. Anisotropy of shrinkage enables injection moulding of round, cylindrical or other hol.. |
|||
Melting Point | 200 - 220 °C | 392 - 428 °F | |
Plastcom SLOVASTER® B1 GF 10 FRX 5 PBT reinforced with 10% glass fibre, with flame retardant Features: PBT with the content of 10 % chemically bound glass fibre and with the halogen freeflame retardant. Anisotropy of shrinkage enables the injection moulding of round, cylindrical or other ho.. |
|||
Melting Point | 200 - 220 °C | 392 - 428 °F | |
Plastcom SLOVASTER® B1 GF 15 FRX 5 PBT reinforced with 15% glass fibre, with flame retardant Features: PBT with the content of 15 % chemically bound glass fibre and with the halogen freeflame retardant. Anisotropy of shrinkage enables the injection moulding of round, cylindrical or other ho.. |
|||
Melting Point | 200 - 220 °C | 392 - 428 °F | |
Plastcom SLOVASTER® B1 GF 20 000/2 PBT, 20% glass fibre FeaturesPBT for injection moulding, pure without lubricant, chemically reinforced with 20% glass fibre, excellent flow. Characterised by excellent properties also at minus temperatures like eg. modu.. |
|||
Melting Point | 200 - 220 °C | 392 - 428 °F | |
Plastcom SLOVASTER® B1 GF 20 PBT, 20% glass fibre FeaturesPBT for injection moulding, chemically reinforced with 20% glass fibre. Characterised by excellent properties also at minus temperatures like eg. modulus of elasticity in tension and bending.. |
|||
Melting Point | 200 - 250 °C | 392 - 482 °F | Average value: 224 °C Grade Count:18 |
Overview of materials for Polybutylene Terephthalate (PBT), 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 50% Glass Fiber Filled". Specific grades with glass content between 45.. |
|||
Melting Point | 200 - 220 °C | 392 - 428 °F | |
Plastcom SLOVASTER® B1 GF 6 PBT, 6% glass fibre FeaturesPBT for injection moulding, chemically reinforced with 6 % glass fibre. Characterised by excellent properties also at minus temperatures like eg. modulus of elasticity in tension and bending.. |
|||
Melting Point | 200 - 220 °C | 392 - 428 °F | |
Plastcom SLOVASTER® B1 HML GF 10 PBT, 10% glass fibre FeaturesPBT for injection moulding, chemically reinforced with 10% glass fibre. Characterised by excellent properties also at minus temperatures like eg. modulus of elasticity in tension and bending.. |
|||
Melting Point | 200 - 260 °C | 392 - 500 °F | Average value: 234 °C Grade Count:3 |
Overview of materials for Nylon 66/6, 10% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, 10% Glass Fiber Reinforced". Specific grades with glass content between 5% and 14% are incl.. |
|||
Melting Point | 200 °C | 392 °F | ASTM D3418 |
Honeywell Aegis™ HCA73MP Nylon 6/6,6 Extrusion Grade Copolymer
(discontinued **) Description: Aegis HCA73MP is a lubricated and nucleated low viscosity, nylon 6/6,6 extrusion grade copolymer for cast or blown film. It conforms to Food and Drug Administration requirements of 21 C.. |
|||
Melting Point | 200 °C | 392 °F | ASTM D3418 |
Honeywell Aegis™ HCA95MP Nylon 6/6,6 Extrusion Grade Copolymer
(discontinued **) Description: Aegis HCA95MP is a low viscosity nylon 6/6,6 copolymer extrusion grade. It conforms to Food and Drug Administration requirements of 21 CFR177.1500. Aegis HCA73ZP possesses the combinati.. |
|||
Melting Point | 200 °C | 392 °F | ASTM D3418 |
Honeywell Aegis™ HCA115QP Nylon 6/6,6 Extrusion Grade Copolymer
(discontinued **) Description: Aegis HCA115QP is a lubricated high viscosity, nylon 6/6,6 extrusion grade copolymer for cast or blown film. It conforms to Food and Drug Administration requirements of 21 CFR 177.1500... |
|||
Melting Point | 200 °C | 392 °F | ASTM D3418 |
Honeywell Aegis™ HCA155MP Nylon 6/6,6 Extrusion Grade Copolymer
(discontinued **) Description: Aegis HCA115MP is a lubricated and nucleated high viscosity, nylon 6/6,6 extrusion grade copolymer for cast or blown film. It conforms to Food and Drug Administration requirements of 21.. |
|||
Melting Point | 200 °C | 392 °F | Peak |
LG Chemical KEYFLEX BT 2140D Ester Type TPE Description: Injection Molding, TPC-ET, Specialty, Low ModulusApplication: Films & SheetsCAS: 37282-12-5Information provided by LG Chemical |
|||
Melting Point | 200 °C | 392 °F | Peak |
LG Chemical KEYFLEX BT HB9242D Ester Type TPE Description: TPC-ET, Blow Moldable, Low Modulus, Black ColorApplication: Cable & Wire Jackets, Hose & Tubing, SheetCAS: 37282-12-5 and 1333-86-4Information provided by LG Chemical |
|||
Melting Point | 200 °C | 392 °F | |
Global EPP PA 6C IMPACT Cast Polyamide 6 + Plasticizer Cast nylons are generally accepted as the primary engineering polymer, suitable for virtually any plain bearing application. By varying the conditions of polymerisation the mechanical properties of .. |
|||
Melting Point | 200 - 300 °C | 392 - 572 °F | Sheath Melt Point; LCL-PR29 |
Intercontinental Polymers 1128 Bicomponent PBT/PET Fiber Type - 1.8 Denier X 3 Inches 50/50 PBT Sheath/PET Core. Luster: Semi-Dull. Finish: Hydrophilic.Applications of bicomponent polyester fiber: Absorbent products, hygiene products, non-wovens, filtration, sliver knit, microdenie.. |
|||
Melting Point | 200 - 220 °C | 392 - 428 °F | ISO R 1218 |
Schwartz Technical Plastics LAMIGAMID® 309 Cast Polyamide 6, Oil Filled, Dry Application: slippers, inserts for coupling boxes, wear linersInformation provided by Schwartz Technical Plastics GmbH |
|||
Melting Point | 200 °C | 392 °F | ASTM D2117 |
Samyang Triel® 5400 Thermoplastic Polyether Ester Elastomer TRIEL® resins offer superior mechanical properties, elasticities, heat and chemical resistance, which allow it to be widely used for electric/electronic equipments, automotive parts and outdoor r.. |
|||
Melting Point | 200 °C | 392 °F | ASTM D2117 |
Samyang Triel® 5401BM Thermoplastics Polyetherester Elastomer, Blow Molding Excellent mechanical characteristics, elasticity, thermal resistance and chemical resistance.5401BM is for blow molding applications.Applications: Automotive - CVJB and BellowsInformation provided .. |
|||
Melting Point | 200 °C | 392 °F | DSC |
Lubrizol Estane® ETE 70DT3 Thermoplastic Polyurethane, Easy-to-Extrude Type: Estane® ETE 70DT3 is an aromatic polyether-based thermoplastic polyurethane (TPU).Features: Hard TPU with wide extrusion processing window and melt stability, low temperature flexibility, hig.. |
|||
Melting Point | 200 °C | 392 °F | 10°C/min; ISO 11357-1/-3 |
EMS-Grivory Grivory® 1S XE 4224 nat PA1010 Product Description: Grilamid XE 4224 natural is a heat and UV stabilized high viscosity polyamide 1010 (PA1010), designed for extrusion. In addition the product can be used for thicker injection mo.. |
|||
Melting Point | 200 °C | 392 °F | 10°C/min; ISO 11357-1/-3 |
EMS-Grivory Grivory® 1SBVX-50H LDS black PA1010-GF50 Product Description: Grilamid 1SBVX-50H LDS black is a 50% glass fiber reinforced Polyamide 1010 injection molding grade. This grade is specifically optimized for the laser Direct Structuring techno.. |
|||
Melting Point | 200 °C | 392 °F | 10°C/min; ISO 11357-1/-3 |
EMS-Grivory Grivory® 1SVX-65H black 9288 PA1010-GF65 Product Description: Grilamid 1SVX-65H black is a 65% glass fiber reinforced Polyamide 1010 injection molding grade with the following product profile: Raw materials based on renewable resources Exc.. |
|||
Melting Point | 200 °C | 392 °F | 10°C/min; ISO 11357-1/-3 |
EMS-Grivory Grivory® CR 9 PA* Product description: Grilon CR 9 is a copolyamide with low melting temperature. Grilon CR 9 shows the following features: High flexibility and toughnessGood thermoforming and orientation propertiesH.. |
|||
Melting Point | 200 °C | 392 °F | 10°C/min; ISO 11357-1/-3 |
DuPont Performance Polymers Hytrel® 52FR Polyester Elastomer TPC-ET
(Unverified Data**) Concentrate in 55 Shore D Polyester Elastomer Carrier Developed for Improving Flame RetardancyInformation provided by DuPont Performance Polymers |
|||
Melting Point | 200 °C | 392 °F | 10°C/min; ISO 11357-1/-3 |
Barlog Plastics KEBAFLEX P D55.1 Polyester-Elastomer, Shore D55 TPC-ETInformation provided by BARLOG plastics GmbH. |
|||
Melting Point | 200 - 220 °C | 392 - 428 °F | |
Plastcom SLOVASTER® B2 BT PBT, basic type FeaturesPBT basic type for injection molding. Melt is characterised by outstanding fluidity, which enables injection molding of complicated and divided products also on multiple molds. Anisotropy of.. |
|||
Melting Point | 200 - 220 °C | 392 - 428 °F | |
Plastcom SLOVASTER® B1 GF 30 PBT, 30% glass fibre FeaturesPBT for injection moulding, chemically reinforced with 30% glass fibre. Characterised by excellent properties also at minus temperatures like eg. modulus of elasticity in tension and bending.. |