Polymer Property : Specific Heat Capacity = 0.111 BTU/lb-°F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Specific Heat Capacity 0.465 J/g-°C

@Temperature 300 °C
0.111 BTU/lb-°F

@Temperature 572 °F
Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes
Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr..
Specific Heat Capacity 0.465 J/g-°C

@Temperature 300 °C
0.111 BTU/lb-°F

@Temperature 572 °F
Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes
Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr..
Specific Heat Capacity 0.465 J/g-°C

@Temperature 300 °C
0.111 BTU/lb-°F

@Temperature 572 °F
Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes
Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr..
Specific Heat Capacity 0.465 J/g-°C

@Temperature 300 °C
0.111 BTU/lb-°F

@Temperature 572 °F
Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet
Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr..
Specific Heat Capacity 0.465 J/g-°C

@Temperature 300 °C
0.111 BTU/lb-°F

@Temperature 572 °F
Haynes 188 alloy, plate at RT after 4000 hours at 870°C (1600°F)
Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr..
Specific Heat Capacity 0.465 J/g-°C

@Temperature 300 °C
0.111 BTU/lb-°F

@Temperature 572 °F
Haynes 188 alloy, plate at RT after 8000 hours at 870°C (1600°F)
Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr..
Specific Heat Capacity 0.465 J/g-°C

@Temperature 400 °C
0.111 BTU/lb-°F

@Temperature 752 °F
Haynes 230® alloy plate
Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic..
Specific Heat Capacity 0.465 J/g-°C

@Temperature 400 °C
0.111 BTU/lb-°F

@Temperature 752 °F
Haynes 230® alloy, 10% cold reduction, 1121°C anneal for 5 minutes
Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic..
Specific Heat Capacity 0.465 J/g-°C

@Temperature 400 °C
0.111 BTU/lb-°F

@Temperature 752 °F
Haynes 230® alloy, 40% cold reduction, 1121°C anneal for 5 minutes
Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic..
Specific Heat Capacity 0.465 J/g-°C

@Temperature 300 °C
0.111 BTU/lb-°F

@Temperature 572 °F
Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet
Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr..
Specific Heat Capacity 0.465 J/g-°C

@Temperature 400 °C
0.111 BTU/lb-°F

@Temperature 752 °F
Haynes 230® alloy, plate, 8000 hours exposure at 760°C (1400°F)
Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic..
Specific Heat Capacity 0.464 J/g-°C
0.111 BTU/lb-°F
RT
Haynes 556® alloy, 0% cold reduction
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Specific Heat Capacity 0.464 J/g-°C
0.111 BTU/lb-°F
RT
Haynes 556® alloy, 0% cold reduction, 1121°C anneal for 5 minutes
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Specific Heat Capacity 0.464 J/g-°C
0.111 BTU/lb-°F
RT
Haynes 556® alloy, 10% cold reduction, 1010°C anneal for 5 minutes
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Specific Heat Capacity 0.464 J/g-°C
0.111 BTU/lb-°F
RT
Haynes 556® alloy, 10% cold reduction, 1121°C anneal for 5 minutes
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Specific Heat Capacity 0.464 J/g-°C
0.111 BTU/lb-°F
RT
Haynes 556® alloy, 30% cold reduction
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Specific Heat Capacity 0.464 J/g-°C
0.111 BTU/lb-°F
RT
Haynes 556® alloy, 50% cold reduction
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Specific Heat Capacity 0.464 J/g-°C
0.111 BTU/lb-°F
RT
Haynes 556® alloy, 50% cold reduction, 1010°C anneal for 5 minutes
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Specific Heat Capacity 0.464 J/g-°C
0.111 BTU/lb-°F
RT
Haynes 556® alloy, all-weld metal GTAW
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Specific Heat Capacity 0.464 J/g-°C
0.111 BTU/lb-°F
RT
Haynes 556® alloy, bar after 16000 hours at 648°C
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Specific Heat Capacity 0.464 J/g-°C
0.111 BTU/lb-°F
RT
Haynes 556® alloy, bar, after 0 hours at 650°C (1200°F)
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Specific Heat Capacity 0.464 J/g-°C
0.111 BTU/lb-°F
RT
Haynes 556® alloy, bar, after 4000 hours at 650°C (1200°F)
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Specific Heat Capacity 0.464 J/g-°C
0.111 BTU/lb-°F
RT
Haynes 556® alloy, cold rolled, solution annealed sheet, 0.8-2.8 mm thick
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Specific Heat Capacity 0.465 J/g-°C

@Temperature 400 °C
0.111 BTU/lb-°F

@Temperature 752 °F
Haynes 230® alloy, plate, 1000 hours exposure at 760°C (1400°F)
Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat..
Specific Heat Capacity 0.465 J/g-°C

@Temperature 400 °C
0.111 BTU/lb-°F

@Temperature 752 °F
Haynes 230® alloy, plate, 16000 hours exposure at 760°C (1400°F)
Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat..
Specific Heat Capacity 0.464 J/g-°C
0.111 BTU/lb-°F
RT
Haynes 556® alloy, 20% cold reduction
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Specific Heat Capacity 0.465 J/g-°C

@Temperature 400 °C
0.111 BTU/lb-°F

@Temperature 752 °F
Haynes 230® alloy, 50% cold reduction, 1066°C anneal for 5 minutes
Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat..
Specific Heat Capacity 0.465 J/g-°C

@Temperature 400 °C
0.111 BTU/lb-°F

@Temperature 752 °F
Haynes 230® alloy, cold rolled and 1232°C solution annealed sheet
Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat..
Specific Heat Capacity 0.464 J/g-°C
0.111 BTU/lb-°F
RT
Haynes 556® alloy, 40% cold reduction, 1065°C anneal for 5 minutes
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Specific Heat Capacity 0.464 J/g-°C
0.111 BTU/lb-°F
RT
Haynes 556® alloy, bar, after 4000 hours at 870°C (1600°F)
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..