Polymer Property : Specific Heat Capacity = 0.270 BTU/lb-°F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Specific Heat Capacity	1.13 J/g-°C	0.270 BTU/lb-°F	ASTM C351
SABIC Innovative Plastics Lexan® 3413R PC 30% GR, provides improved mechanical properties and UL94V-1 rated at 0.058"". Internal mold release added.
Specific Heat Capacity	1.13 J/g-°C	0.270 BTU/lb-°F	ASTM C351
SABIC Innovative Plastics Lexan® 3413R PC (Asia Pacific) Lexan* resin 3413R is a flame retardant polycarbonate grade with 30% glass fiber reinforcement to meet UL 94 V1 listing at 1.5mm. This grade can be considered for applications requiring higher stiff..
Specific Heat Capacity	1.13 J/g-°C	0.270 BTU/lb-°F	ASTM E1461
Park Electrochemical Nelco® N4000-12 SI® High Speed/Low Loss, CAF Resistant Laminate and Prepreg The Nelco® N4000-12 series is an enhanced epoxy resin system designed for use in high speed, low loss applications requiring thermal stability, excellent signal speed and CAF resistance.Key Feature..
Specific Heat Capacity	1.13 - 1.55 J/g-°C	0.270 - 0.370 BTU/lb-°F	Average value: 1.43 J/g-°C Grade Count:4
Overview of materials for Polycarbonate, 20% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, 20% Glass Filled". Specific grades with glass content between 15% and 24% are included. E..
Specific Heat Capacity	1.13 - 1.90 J/g-°C	0.270 - 0.454 BTU/lb-°F	Average value: 1.57 J/g-°C Grade Count:8
Overview of materials for PVC, Foam Grade This property data is a summary of similar materials in the MatWeb database for the category "PVC, Foam Grade". Each property range of values reported is minimum and maximum values of appropriate Ma..
Specific Heat Capacity	1.13 J/g-°C	0.270 BTU/lb-°F	Differential Scanning Calorimeter
UBE UPILEX 75S (75 micron) Polyimide Film Description: UPILEX, the ultra-high heat-resistant polyimide film, is the product of the polycondensation reaction between biphenyltetracarboxylic dianhydride (BPDA), of which process Ube Industries..
Specific Heat Capacity	1.13 J/g-°C	0.270 BTU/lb-°F
Zircar Ceramics DAHP Dense Alumina Hearth Plate ZIRCAR Dense Alumina Hearth Plates are used for supporting loads in high temperature furnaces and other thermal process systems. These dense plates are made of fully sintered fine grain high purity ..
Specific Heat Capacity	1.13 J/g-°C	0.270 BTU/lb-°F	Differential Scanning Calorimeter
UBE UPILEX 25S (25 micron) Polyimide Film Description: UPILEX, the ultra-high heat-resistant polyimide film, is the product of the polycondensation reaction between biphenyltetracarboxylic dianhydride (BPDA), of which process Ube Industries..
Specific Heat Capacity	1.13 J/g-°C @Temperature 1093 °C	0.270 BTU/lb-°F @Temperature 1999 °F
Unifrax Fiberfrax® Durablanket® 2600 Ceramic Fiber Insulator Fiberfrax Durablanket 2600 insulation extends the high-temperature performance of the Durablanket product line. The product is made from high-purity alumina, zirconia, and silica spun ceramic fiber..
Specific Heat Capacity	1.13 J/g-°C @Temperature 1093 °C	0.270 BTU/lb-°F @Temperature 1999 °F
Unifrax Fiberfrax® Durablanket® S Ceramic Fiber Insulator Fiberfrax Durablanket S insulation is a strong, lightweight, flexible needled blanket that is made from spun ceramic fibers. Available in a wide variety of thicknesses, widths and densities, Durabl..
Specific Heat Capacity	1.13 J/g-°C	0.270 BTU/lb-°F	ASTM D2766
Covestro Makrolon® 8325 Polycarbonate High viscosity injection molding and extrusion grade with 20% standard glass fibers and easy mold release, high strength and stiffness.Information provided by Bayer.As of 1 September 2015, Bayer Mat..
Specific Heat Capacity	1.13 J/g-°C	0.270 BTU/lb-°F	ASTM D2766
Covestro Makrolon® 9415(Z) Polycarbonate Medium viscosity, flame retardant extrusion and injection molding grade with 10% standard glass fibers and easy mold release agent.Information provided by Bayer.As of 1 September 2015, Bayer Materia..
Specific Heat Capacity	1.13 J/g-°C	0.270 BTU/lb-°F
Ensinger TECASINT 1021 Polyimide, 15% Graphite Filled (PI) TECASINT is a range of non-melting high temperature polyimides characterized by high strength over a wide range of temperatures, good long term thermal stability, minimal thermal expansion and excel..
Specific Heat Capacity	1.13 J/g-°C	0.270 BTU/lb-°F
Ensinger RADEL® R-5500 Polyphenylsulfone (PPSU) RADEL® R is a Polyphenysulfone produced by Solvay Advanced Polymers. RADEL® R is in the same performance category as products like Polysulfone and ULTEM® (PEI). RADEL® R has increased performa..
Specific Heat Capacity	1.13 J/g-°C	0.270 BTU/lb-°F
Asahi Glass ASAHIKLIN AK-225AES Hydrochlorofluorocarbon Solvent AK-225 AES was developed as a defluxing agent. It is an azeotrope-like mixture of AK-225, ethanol and stabilizer and is suitable for use in a vapor degreaser. It effectively removes flux residues as..
Specific Heat Capacity	1.13 J/g-°C @Temperature 500 °C	0.270 BTU/lb-°F @Temperature 932 °F
3M Nextel™ 440 Industrial Ceramic Fiber Chemical composition above is wt%. Crystal phases are gamma alumina + mullite + amorphous SiO2. Filament diameter is 10-12 µm.3M Nextel fibers 312, 440, and 550 are designed for non-structural ap..
Specific Heat Capacity	1.13 J/g-°C @Temperature 500 °C	0.270 BTU/lb-°F @Temperature 932 °F
3M Nextel™ BF-30 Woven Fabric 440 Information provided by 3M
Specific Heat Capacity	1.13 J/g-°C @Temperature 500 °C	0.270 BTU/lb-°F @Temperature 932 °F
3M Nextel™ BF-20 Woven Fabric 440 Information provided by 3M
Specific Heat Capacity	1.13 J/g-°C @Temperature 500 °C	0.270 BTU/lb-°F @Temperature 932 °F
3M Nextel™ BF-40 Woven Fabric 440 Information provided by 3M
Specific Heat Capacity	1.13 J/g-°C	0.270 BTU/lb-°F
3M Novec™ 774 Engineered Fluid 3M™ Novec™ 774 Engineered Fluid is a clear, colorless and low odor fluid, and is one in a line of 3M products designed as replacements for ozone depleting substances (ODSs) and compounds with high..
Specific Heat Capacity	1.13 J/g-°C @Temperature 1093 °C	0.270 BTU/lb-°F @Temperature 1999 °F
Unifrax Fiberfrax® Moist Pak-D® Ceramic Fiber Insulator Fiberfrax Moist Pak-D insulation is made from high-strength ceramic fiber blankets impregnated with inorganic bonding agents. This processing results in a flexible insulation that air dries to form..