Thermal Properties | Metric | English | Comments |
---|---|---|---|
Glass Transition Temp, Tg | 275 °C | 527 °F | ASTM D3418 |
Quadrant EPP Duratron® PAI T4203 Extruded Polyamide-imide (ASTM Product Data Sheet) |
|||
Glass Transition Temp, Tg | 275 °C | 527 °F | ASTM D3418 |
Quadrant EPP Semitron® ESd 520HR (ASTM Product Data Sheet) |
|||
Glass Transition Temp, Tg | 275 °C | 527 °F | ASTM D3418 |
Quadrant EPP Semitron® MPR-1000 (ASTM Product Data Sheet) |
|||
Glass Transition Temp, Tg | 275 °C @Temperature 227 °C, Time 21600 sec |
527 °F @Temperature 440 °F, Time 6.00 hour |
Storage Modulus, Dry, Vary post cure conditions, initial cure at 375°F, 3 hrs |
Renegade Materials Corporation RM-3002 Bismaleimide (BMI) Resin IM7 12K Carbon Uni-tape Developed using state-of-the-art formulating technologies, RM-3002 BMI prepreg products deliver superior hot/wet performance in airframe, missile and propulsion applications at service temperatures .. |
|||
Glass Transition Temp, Tg | 275 °C | 527 °F | ASTM D3418 |
Quadrant EPP Duratron® PAI T4501 Polyamide-imide, compression molded bearing grade (ASTM Product Data Sheet) |
|||
Glass Transition Temp, Tg | 275 °C | 527 °F | ASTM D3418 |
Quadrant EPP Duratron® PAI T4503 Compression Molded, Polyamide-imide, Eelectrical Grade (ASTM Product Data Sheet) |
|||
Glass Transition Temp, Tg | 275 °C | 527 °F | ASTM D3418 |
Quadrant EPP Duratron® PAI T4540 Polyamide-imide, compression molded (ASTM Product Data Sheet) |
|||
Glass Transition Temp, Tg | 275 °C | 527 °F | ASTM D3418 |
Quadrant EPP Duratron® PAI T5030 Polyamide-imide, glass reinforced, extruded (ASTM Product Data Sheet) |
|||
Glass Transition Temp, Tg | 275 °C | 527 °F | ASTM D3418 |
Quadrant EPP Duratron® PAI T5530 Compression Molded Glass Reinforced Polyamide-imide (ASTM Product Data Sheet) |
|||
Glass Transition Temp, Tg | 275 °C | 527 °F | ASTM D3418 |
Quadrant EPP Duratron® T7130 PAI Polyamide-imide, carbon fiber reinforced, extruded (ASTM Product Data Sheet) |
|||
Glass Transition Temp, Tg | 275 °C | 527 °F | Amorphous; ASTM D3418 |
Quadrant EPP Semitron® CMP XL20 (ASTM Product Data Sheet) |
|||
Glass Transition Temp, Tg | 275 - 280 °C | 527 - 536 °F | Average value: 277 °C Grade Count:6 |
Overview of materials for Polyamide-Imide, Molded This property data is a summary of similar materials in the MatWeb database for the category "Polyamide-Imide, Molded". Each property range of values reported is minimum and maximum values of approp.. |
|||
Glass Transition Temp, Tg | 275 - 280 °C | 527 - 536 °F | Average value: 277 °C Grade Count:3 |
Overview of materials for Polyamide-Imide, Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyamide-Imide, Glass Filled". Each property range of values reported is minimum and maximum values of .. |
|||
Glass Transition Temp, Tg | 275 °C | 527 °F | |
Vyncolit Neopreg Kinel® SK4503 S5 Aramid Reinforced Molding Compound Long aramid fiber reinforced BMI molding compound suited for very demanding tribologic applications under medium to poor lubricated conditions, high temperatures & PV levelsInformation provided by S.. |
|||
Glass Transition Temp, Tg | 275 °C | 527 °F | dynamic; DIN 53 736 |
Hippe PAI Polyamide-imide Particularly used where high strength in a wide range of temperature (-190°C…+260°C), high notched strength and very good dielectric properties are required. Features good chemical stability, fl.. |
|||
Glass Transition Temp, Tg | 275 °C | 527 °F | |
Vyncolit Neopreg Kinel® SK4502 S8 Carbon Reinforced Molding Compound KINEL SK4502 S8 is a long carbon fiber reinforced BMI molding compound suited for very demanding tribological applications, high speeds and temperatures even under dry running conditions. Thermal ex.. |
|||
Glass Transition Temp, Tg | 275 °C | 527 °F | ASTM D3418 |
Quadrant EPP Duratron® PAI T4301 Polyamide-imide, extruded bearing grade (ASTM Product Data Sheet) |
|||
Glass Transition Temp, Tg | 275 °C | 527 °F | ASTM D3418 |
Quadrant EPP Duratron® PAI T7530, Compression Molded Carbon Fiber Reinforced Polyamide-Imide |
|||
Glass Transition Temp, Tg | 275 °C | 527 °F | Postcured, Dry |
Hexcel® HexTOOL™ M61 Quasi-isotropic High Temperature Prepreg Tooling Compound HexTOOL™ Tooling Compound is randomly layered strips of uni-directional prepreg which is consolidated into rolled goods. It can be utilized as multi-ply quasi-isotropic hand lay-up, and subsequentl.. |
|||
Glass Transition Temp, Tg | 275 °C | 527 °F | |
Vyncolit Neopreg Kinel® SK4525 S5 Glass Fiber Reinforced Molding Compound BMI molding compound long glass fiber reinforced with excellent mechanical and thermal properties. Especially suited to be used for injection molding.Information provided by Sumitomo Bak North Ameri.. |
|||
Glass Transition Temp, Tg | 275 °C | 527 °F | ASTM D3418 |
Quadrant EPP Duratron® PAI T7530, Compression Molded Carbon Fiber Reinforced Polyamide-Imide |