 POLYMER SEARCH

Polymer Property : CTE, linear, Transverse to Flow = 3.89 µin/in-°F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
CTE, linear, Transverse to Flow 7.00 µm/m-°C

@Temperature -30.0 - 30.0 °C
3.89 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
SABIC Innovative Plastics LNP STAT-KON DD0009E PC
LNP* STAT-KON* DD0009E is a compound based on Polycarbonate resin containing Carbon Powder. Added features of this material include: Electrically Conductive, Flame Retardant, Easy Molding.
CTE, linear, Transverse to Flow 7.00 µm/m-°C

@Temperature -30.0 - 30.0 °C
3.89 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
SABIC Innovative Plastics LNP STAT-KON DE0069F PC
LNP* STAT-KON* DE0069F is a compound based on Polycarbonate resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant, Superior Molding.
CTE, linear, Transverse to Flow 7.00 µm/m-°C

@Temperature -30.0 - 30.0 °C
3.89 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
SABIC Innovative Plastics LNP STAT-KON DEL13EXC PC
LNP STAT-KON* DEL13EXC is a compound based on Polycarbonate resin containing 15% Carbon Fiber, 5% PTFE. Added features of this material include: Easy Molding, Electrically Conductive, Wear Resistan..
CTE, linear, Transverse to Flow 7.00 µm/m-°C

@Temperature -30.0 - 30.0 °C
3.89 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
SABIC Innovative Plastics LNP THERMOCOMP DF005 PC
LNP* Thermocomp* DF005 is a compound based on Polycarbonate containing 25% Glass Fiber.
CTE, linear, Transverse to Flow 7.00 µm/m-°C

@Temperature -30.0 - 30.0 °C
3.89 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D 696
SABIC Innovative Plastics LNP Thermocomp DFZ22E PC
LNP* Thermocomp* DFZ22E is a compound based on Polycarbonate with Glass and Milled Fiber. Characteristics of this products is Easy Molding.This data was supplied by SABIC-IP for the Americas region..
CTE, linear, Transverse to Flow 7.00 µm/m-°C

@Temperature -30.0 - 30.0 °C
3.89 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
SABIC Innovative Plastics LNP THERMOCOMP DX06411H PC
LNP* THERMOCOMP* DX06411H is a compound based on Polycarbonate resin containing 20% Glass Fiber. Added features of this material include: Easy Molding, Mold Release, Healthcare.
CTE, linear, Transverse to Flow 7.00 µm/m-°C

@Temperature -30.0 - 30.0 °C
3.89 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
SABIC Innovative Plastics LNP STAT-KON DFD03 PC
LNP* STAT-KON* DFD03 is a compound based on Polycarbonate containing 15% Glass Fiber. Added feature of this grade is: Impact Modified.
CTE, linear, Transverse to Flow 7.00 µm/m-°C

@Temperature 23.0 - 85.0 °C
3.89 µin/in-°F

@Temperature 73.4 - 185 °F
ISO 11359
Solvay TECHNYL® A 205F PA66, DRY
Description: TECHNYL ® A 205F is an unreinforced polyamide 66 for injection molding. It is available in natural color.Benefits: The product offers two main advantages: excellent filling qualities..
CTE, linear, Transverse to Flow 7.00 µm/m-°C

@Temperature 23.0 - 1500 °C
3.89 µin/in-°F

@Temperature 73.4 - 2730 °F
Secant Value
Carlisle 201HD Carbon-Carbon Composite
Carbon-Carbon Composite manufactured as sheets from 4mm to 125mm thick this material is essentially a fracture tough, fiber reinforced graphite often referred to as a “CFC”. Good for use in air t..
CTE, linear, Transverse to Flow 7.00 µm/m-°C

@Temperature 23.0 - 1500 °C
3.89 µin/in-°F

@Temperature 73.4 - 2730 °F
Secant Value
Carlisle 201HL Carbon-Carbon Composite
Carbon-Carbon Composite manufactured as sheets from 4mm to 125mm thick this material is essentially a fracture tough, fiber reinforced graphite often referred to as a “CFC”. Good for use in air t..
CTE, linear, Transverse to Flow 7.00 µm/m-°C
3.89 µin/in-°F
ISO 11359-1/-2
Lanxess Durethan® DP AKV 35 LT H2.0 904040 Nylon 66, 35% Glass Fiber
PA 66, injection molding grade, 35% glass fibers, black colored for laser transmission- welding (laser-transparent), good heat-ageing resistance