Polymer Property : CTE, linear = 12.6 µm/m-°C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 12.6 µm/m-°C @Temperature 0.000 - 500 °C |
7.00 µin/in-°F @Temperature 32.0 - 932 °F |
|
| Kennametal Stellite Stellite® STAR with P/M Processing Applications: Vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing blanks, diesel engine exhaust, fluid valve seats, saw cutter inserts, wear pads, pins, balls, hardfa.. |
|||
| CTE, linear | 12.6 µm/m-°C @Temperature 20.0 - 200 °C |
7.00 µin/in-°F @Temperature 68.0 - 392 °F |
|
| International Mold Steel NAK80 Precipitation Hardened Mold Steel Description: NAK80 is a precipitation or age-hardened mold steel with a uniform through hardness of approximately 40 HRc. It is super clean, Vacuum-Arc Remelted steel with uniform grain structure, u.. |
|||
| CTE, linear | 12.6 µm/m-°C @Temperature 25.0 - 200 °C |
7.00 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 12.6 µm/m-°C @Temperature 25.0 - 200 °C |
7.00 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 188 alloy, plate at RT after 0 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 12.6 µm/m-°C @Temperature 21.0 - 200 °C |
7.00 µin/in-°F @Temperature 69.8 - 392 °F |
|
| Haynes Hastelloy® G-35® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process†phosphoric acid, which is widely used in the production of fertilizers. Tests indicat.. |
|||
| CTE, linear | 12.6 µm/m-°C @Temperature 25.0 - 200 °C |
7.00 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 188 alloy, cold rolled and 1175°C solution annealed sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 12.6 µm/m-°C @Temperature 25.0 - 200 °C |
7.00 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 188 alloy, plate at RT after 8000 hours at 760°C (1400°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 12.6 µm/m-°C @Temperature 24.0 - 316 °C |
7.00 µin/in-°F @Temperature 75.2 - 601 °F |
|
| Haynes Hastelloy® C-22® alloy, 12.7-50.8 mm thick bar, solution heat treated HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| CTE, linear | 12.6 µm/m-°C @Temperature 24.0 - 316 °C |
7.00 µin/in-°F @Temperature 75.2 - 601 °F |
|
| Haynes Hastelloy® C-22® alloy, 40% cold worked sheet, aged 100 hours at 500°C HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| CTE, linear | 12.6 µm/m-°C @Temperature 24.0 - 316 °C |
7.00 µin/in-°F @Temperature 75.2 - 601 °F |
|
| Haynes Hastelloy® C-22® alloy, SMAW weld, C-22 base metal, C-22 weld metal HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| CTE, linear | 12.6 µm/m-°C @Temperature 21.1 - 399 °C |
7.00 µin/in-°F @Temperature 70.0 - 750 °F |
|
| Schmolz + Bickenbach Thermodur® 2367 Superclean Hot Work Die Steel Description: Thermodur® 2367 Superclean is an electro slag remelted (ESR) hot work die steel developed for applications where high temperature properties (tensile strength & thermal conductivity).. |
|||
| CTE, linear | 12.6 µm/m-°C @Temperature 21.1 - 93.3 °C |
7.00 µin/in-°F @Temperature 70.0 - 200 °F |
|
| Schmolz + Bickenbach Thermodur® 2714 Extra Fine Structure - Hot Work Die Steel Description: Thermodur 2714 is an Extra Fine Structure (EFS) nickel based tool steel.Characteristics: Excellent high temperature strength; Good toughness; and Good resistance to thermal shockApplica.. |
|||
| CTE, linear | 12.6 µm/m-°C @Temperature 21.1 - 427 °C |
7.00 µin/in-°F @Temperature 70.0 - 800 °F |
|
| Crucible Steel CHRO-MOW® Tool Steel, AISI H12 Chro-Mow is a general purpose hot work tool steel, combining good high-temperature strength with moderate toughness and heat check resistance. It is suited for applications where drastic coolants ar.. |
|||
| CTE, linear | 12.6 µm/m-°C @Temperature 21.1 - 204 °C |
7.00 µin/in-°F @Temperature 70.0 - 400 °F |
|
| Crucible Steel Holder Block Steel, AISI 4150 Modified Crucible Holder Block is a prehardened (26/30 HRC) free machining medium alloy steel intended for holders or backers for plastic molds, die casting dies, and cold or hot forming tools. It may also b.. |
|||
| CTE, linear | 12.6 µm/m-°C @Temperature 25.0 - 100 °C |
7.00 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Carpenter Custom Age 625 PLUS® Nickel-Base Alloy, Double Aged 732°C (1350°F)/8hr/AC to 621°C (1150°F)/8hr/AC Data provided by Carpenter Technology Corporation.Custom Age 625 PLUS® alloy is a precipitation hardenable, nickel-base alloy which, in many environments, displays corrosion resistance similar to t.. |
|||
| CTE, linear | 12.6 µm/m-°C @Temperature 20.0 - 850 °C |
7.00 µin/in-°F @Temperature 68.0 - 1560 °F |
|
| Carpenter Speed Star® High Speed Steel (Red-Hard) (AISI M2) Speed Star high speed steel in a fine-grained "Moly"-Tungsten high-speed steel manufactured under close control. It has certain advantages over 18-4-1 high speed steels, some of which are lower cost.. |
|||
| CTE, linear | 12.6 µm/m-°C @Temperature 25.0 - 600 °C |
7.00 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Carpenter Chrome Core® 8-FM Alloy Data provided by Carpenter Technology Corporation.Chrome Core® alloys are a family of controlled chemistry, ferritic 8 and 12% chromium-iron alloys which are candidates for use in magnetic componen.. |
|||
| CTE, linear | 12.6 µm/m-°C @Temperature 25.0 - 100 °C |
7.00 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Carpenter Custom Age 625 PLUS® Nickel-Base Alloy, Cold Drawn 37.5% Plus Aging 649°C (1200°F)/4hr/FC to 579°C/4hr/AC Data provided by Carpenter Technology Corporation.Custom Age 625 PLUS® alloy is a precipitation hardenable, nickel-base alloy which, in many environments, displays corrosion resistance similar to t.. |
|||
| CTE, linear | 12.6 µm/m-°C @Temperature 20.0 - 400 °C |
7.00 µin/in-°F @Temperature 68.0 - 752 °F |
|
| Assab Steels 8407 SUPREME Hot Work Steel 8407 SUPREME is characterized by:High level of resistance to thermal shock and thermal fatigueGood high temperature strengthExcellent toughness and ductility in all directionsGood machinability and .. |
|||
| CTE, linear | 12.6 µm/m-°C @Temperature 25.0 - 800 °C |
7.00 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Aremco AREMCOLOX™ 502-800 Macor® Machinable Glass Ceramic, MGC Recommended for temperatures to 1472°F (800°C) and peaks up to 1832°F (1000°C). Demonstrates low thermal conductivity, high strength, high electrical insulation, zero porosity, non-wetting, and .. |
|||
| CTE, linear | 12.6 µm/m-°C @Temperature 20.0 - 205 °C |
7.00 µin/in-°F @Temperature 68.0 - 401 °F |
|
| Crucible Steel S7 XL (Premium AISI S7) Tool Steel Crucible S7XL is a double refined, high purity grade of S7. The remelt operation produces a cleaner steel with a more uniform microstructure, offering the following advantages over conventional S7:B.. |
|||
| CTE, linear | 12.6 µm/m-°C @Temperature 24.0 - 316 °C |
7.00 µin/in-°F @Temperature 75.2 - 601 °F |
|
| Haynes Hastelloy® C-22® alloy, all-weld metal, SMAW HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| CTE, linear | 12.6 µm/m-°C @Temperature 24.0 - 316 °C |
7.00 µin/in-°F @Temperature 75.2 - 601 °F |
|
| Haynes Hastelloy® C-22® alloy, GTAW weld, 904L base metal, C-22 weld metal HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| CTE, linear | 12.6 µm/m-°C @Temperature 20.0 - 316 °C |
7.00 µin/in-°F @Temperature 68.0 - 601 °F |
|
| Haynes Hastelloy® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, aged 10 hours at 649°C (1200°F) Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T.. |
|||
| CTE, linear | 12.6 µm/m-°C @Temperature 21.0 - 200 °C |
7.00 µin/in-°F @Temperature 69.8 - 392 °F |
|
| Haynes Hastelloy® G-35® Nickel Alloy Sheet, Annealed at 2075°F (1135°C) Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process” phosphoric acid, which is widely used in the production of fertilizers. Tests indicate that it is.. |
|||
| CTE, linear | 12.6 µm/m-°C @Temperature 25.0 - 100 °C |
7.00 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Carpenter Custom Age 625 PLUS® Nickel-Base Alloy, Double Aged 746°C (1375°F)/8hr/AC to 621°C (1150°F)/8hr/AC Data provided by Carpenter Technology Corporation.Custom Age 625 PLUS® alloy is a precipitation hardenable, nickel-base alloy which, in many environments, displays corrosion resistance similar to t.. |
|||
| CTE, linear | 12.6 µm/m-°C @Temperature 21.1 - 399 °C |
7.00 µin/in-°F @Temperature 70.0 - 750 °F |
|
| Schmolz + Bickenbach Cryodur® 2357(S-7) Cold Work Die Steel Description: Cryodur 2357 is a shock resistant tool steel with excellent toughness and high strength; Suitable for cold and hot work applications up to 1000 °F; and Supplied in the annealed conditi.. |
|||
| CTE, linear | 12.6 µm/m-°C @Temperature 24.0 - 316 °C |
7.00 µin/in-°F @Temperature 75.2 - 601 °F |
|
| Haynes Hastelloy® C-22® alloy, 0% cold worked sheet, aged 100 hours at 500°C HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| CTE, linear | 12.6 µm/m-°C @Temperature 24.0 - 316 °C |
7.00 µin/in-°F @Temperature 75.2 - 601 °F |
|
| Haynes Hastelloy® C-22® alloy, 6.4-19.1 mm thick plate, solution heat treated HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| CTE, linear | 12.6 µm/m-°C @Temperature 24.0 - 316 °C |
7.00 µin/in-°F @Temperature 75.2 - 601 °F |
|
| Haynes Hastelloy® C-22® alloy, GMAW, aged 4000 hours at 450°C (800°F), unnotched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||