Polymer Property : CTE, linear = 13.3 µm/m-°C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 13.3 µm/m-°C @Temperature 25.0 - 200 °C |
7.39 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 214® alloy, 50% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| CTE, linear | 13.3 µm/m-°C @Temperature 25.0 - 200 °C |
7.39 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 214® alloy, sheet, 1000 hours exposure at 980°C (1800°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| CTE, linear | 13.3 µm/m-°C @Temperature 25.0 - 300 °C |
7.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 230® alloy plate, 4000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 13.3 µm/m-°C @Temperature 25.0 - 300 °C |
7.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 230® alloy, 10% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 13.3 µm/m-°C @Temperature 25.0 - 300 °C |
7.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 230® alloy, 30% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 13.3 µm/m-°C @Temperature 25.0 - 300 °C |
7.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 230® alloy, 40% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 13.3 µm/m-°C @Temperature 20.0 - 538 °C |
7.39 µin/in-°F @Temperature 68.0 - 1000 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 13.3 µm/m-°C @Temperature 20.0 - 538 °C |
7.39 µin/in-°F @Temperature 68.0 - 1000 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 13.3 µm/m-°C @Temperature 20.0 - 538 °C |
7.39 µin/in-°F @Temperature 68.0 - 1000 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 13.3 µm/m-°C @Temperature 20.0 - 538 °C |
7.39 µin/in-°F @Temperature 68.0 - 1000 °F |
|
| Haynes Hastelloy® S alloy, weld metal, aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 13.3 µm/m-°C @Temperature 25.0 - 600 °C |
7.39 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes Hastelloy® C-2000® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |
|||
| CTE, linear | 13.3 µm/m-°C @Temperature 24.0 - 427 °C |
7.39 µin/in-°F @Temperature 75.2 - 801 °F |
|
| Haynes Hastelloy® C-22® alloy, 12.7-50.8 mm thick bar, solution heat treated HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| CTE, linear | 13.3 µm/m-°C @Temperature 24.0 - 427 °C |
7.39 µin/in-°F @Temperature 75.2 - 801 °F |
|
| Haynes Hastelloy® C-22® alloy, 20% cold worked sheet, aged 100 hours at 500°C HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| CTE, linear | 13.3 µm/m-°C @Temperature 25.0 - 600 °C |
7.39 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes Hastelloy® C-22HS™ Nickel Alloy Gas Tungsten Arc Welded (GTAW) Plate Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou.. |
|||
| CTE, linear | 13.3 µm/m-°C @Temperature 20.0 - 427 °C |
7.39 µin/in-°F @Temperature 68.0 - 801 °F |
|
| Haynes Hastelloy® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, aged 1000 hours at 649°C (1200°F) Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) rang.. |
|||
| CTE, linear | 13.3 µm/m-°C @Temperature 20.0 - 600.0 °C |
7.39 µin/in-°F @Temperature 68.0 - 1112 °F |
|
| Schmolz + Bickenbach Thermodur® 2999 Hot Work Die Steel Description: Maximum high-temperature strength, good high-temperature wear resistance, excellent thermal shock resistance and thermal conductivity across the entire range of service temperatures App.. |
|||
| CTE, linear | 13.3 µm/m-°C @Temperature 25.0 - 316 °C |
7.39 µin/in-°F @Temperature 77.0 - 601 °F |
|
| Carpenter Stentor® Alloy Tool Steel (Oil-Hard) (AISI 02) An oil-hardening alloy with excellent size change properties, Stentor tool steel is especially suited for general purpose work in the toolroom. It is safe to harden, and shows little size change or .. |
|||
| CTE, linear | 13.3 µm/m-°C @Temperature 20.0 - 400 °C |
7.39 µin/in-°F @Temperature 68.0 - 752 °F |
Hardened and tempered to 56 HRC |
| Assab Steels CARMO Cold Work Steel CARMO is a high-strength, flame-induction and through hardening steel delivered prehardened to 240-270 HB.The surface of the steel can be flame-hardened without water cooling to a hardness of 58±2.. |
|||
| CTE, linear | 13.3 µm/m-°C @Temperature 20.0 - 600 °C |
7.39 µin/in-°F @Temperature 68.0 - 1110 °F |
|
| Assab Steels DIEVAR Hot Work Steel DIEVAR is a high performance chromium-molybdenum-vanadium alloyed hot work tool steel which offers a very good resistance to heat checking, gross checking, hot wear and plastic deformation. DIEVAR i.. |
|||
| CTE, linear | 13.3 µm/m-°C @Temperature 25.0 - 300 °C |
7.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 230® alloy, hot rolled and 1232°C solution annealed plate Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| CTE, linear | 13.3 µm/m-°C @Temperature 24.0 - 427 °C |
7.39 µin/in-°F @Temperature 75.2 - 801 °F |
|
| Haynes Hastelloy® C-22® alloy, transverse, SMAW weldment, 19.1 mm thick plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| CTE, linear | 13.3 µm/m-°C @Temperature 25.0 - 600 °C |
7.39 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes Hastelloy® C-22HS™ Nickel Alloy Plate and Bar, Hot-rolled, Solution Annealed, Age-hardened Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately doubl.. |
|||
| CTE, linear | 13.3 µm/m-°C @Temperature 25.0 - 600 °C |
7.39 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes Hastelloy® C-22HS™ Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately doubl.. |
|||
| CTE, linear | 13.3 µm/m-°C @Temperature 20.0 - 538 °C |
7.39 µin/in-°F @Temperature 68.0 - 1000 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
| CTE, linear | 13.3 µm/m-°C @Temperature 20.0 - 538 °C |
7.39 µin/in-°F @Temperature 68.0 - 1000 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
| CTE, linear | 13.3 µm/m-°C @Temperature 20.0 - 538 °C |
7.39 µin/in-°F @Temperature 68.0 - 1000 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
| CTE, linear | 13.3 µm/m-°C @Temperature 21.1 - 302 °C |
7.40 µin/in-°F @Temperature 70.0 - 575 °F |
|
| Schmolz + Bickenbach Formadur® 2311 Plastic Mold Steel Description: Formadur® 2311 is a pre-hardened plastic mold steelCharacteristics: Good texturing compared to Formadur®2312 and Good polishability compared to Formadur® 231Applications: Injection m.. |
|||
| CTE, linear | 13.3 µm/m-°C @Temperature 24.0 - 427 °C |
7.39 µin/in-°F @Temperature 75.2 - 801 °F |
|
| Haynes Hastelloy® C-22® alloy, GMAW, aged 4000 hours at 450°C (800°F), notched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| CTE, linear | 13.3 µm/m-°C @Temperature 24.0 - 427 °C |
7.39 µin/in-°F @Temperature 75.2 - 801 °F |
|
| Haynes Hastelloy® C-22® alloy, SMAW weld, 904L base metal, C-22 weld metal HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| CTE, linear | 13.3 µm/m-°C @Temperature 21.0 - 300 °C |
7.39 µin/in-°F @Temperature 69.8 - 572 °F |
Mean |
| Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed 1950°F (1070°C) + Aged 1200°F (650°C) Tensile strength (ultimate and yield), elongation, and hardness values are for samples annealed 1950°F (1070°C)/5 minutes/AC + Aged 1200°F (650°C)/100h/AC. This produces ASTM grain size 9.5. .. |
|||