- Polymer Property : CTE, linear = 14.7 µm/m-°C
Polymer Property : CTE, linear = 14.7 µm/m-°C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 14.7 µm/m-°C @Temperature 0.000 - 400 °C |
8.17 µin/in-°F @Temperature 32.0 - 752 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, 1.6 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| CTE, linear | 14.7 µm/m-°C @Temperature 20.0 - 500 °C |
8.17 µin/in-°F @Temperature 68.0 - 932 °F |
|
| Industeel CREUSABRO® 4800 Advanced Technology in Wear Steel Description: CREUSABRO® 4800(P) is a wear resistant steel offering up to 50% extra in service life compared with a 400 HB water quenched steel. CREUSABRO® 4800(P) combines several modern metal.. |
|||
| CTE, linear | 14.7 µm/m-°C @Temperature 21.0 - 760 °C |
8.17 µin/in-°F @Temperature 69.8 - 1400 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 538°C (1000°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
| CTE, linear | 14.7 µm/m-°C @Temperature 21.0 - 760 °C |
8.17 µin/in-°F @Temperature 69.8 - 1400 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 704°C (1300°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
| CTE, linear | 14.7 µm/m-°C @Temperature 25.0 - 100 °C |
8.17 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 556® alloy, 0% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 14.7 µm/m-°C @Temperature 25.0 - 100 °C |
8.17 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 556® alloy, 10% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 14.7 µm/m-°C @Temperature 25.0 - 100 °C |
8.17 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 556® alloy, 10% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 14.7 µm/m-°C @Temperature 25.0 - 100 °C |
8.17 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 556® alloy, 10% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 14.7 µm/m-°C @Temperature 25.0 - 100 °C |
8.17 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 556® alloy, 30% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 14.7 µm/m-°C @Temperature 25.0 - 100 °C |
8.17 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 556® alloy, 40% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 14.7 µm/m-°C @Temperature 25.0 - 100 °C |
8.17 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 556® alloy, 40% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 14.7 µm/m-°C @Temperature 25.0 - 100 °C |
8.17 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 556® alloy, bar after 16000 hours at 537°C Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 14.7 µm/m-°C @Temperature 25.0 - 100 °C |
8.17 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 556® alloy, bar, after 1000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 14.7 µm/m-°C @Temperature 25.0 - 100 °C |
8.17 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 556® alloy, bar, after 4000 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 14.7 µm/m-°C @Temperature 25.0 - 100 °C |
8.17 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 556® alloy, bar, after 8000 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 14.7 µm/m-°C @Temperature 25.0 - 100 °C |
8.17 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 556® alloy, hot rolled, solution annealed plate, 6.4-12.7 mm (1/2 in.) thick Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 14.7 µm/m-°C @Temperature 21.0 - 500 °C |
8.17 µin/in-°F @Temperature 69.8 - 932 °F |
Mean |
| Special Metals DURANICKEL® 301 (UNS N03301) Half-Hard and Aged Strip Tensile strength (ultimate), hardness, and elongation values reported here are typical for Half-Hard and Aged Strip specifically. Other property values are typical of aged DURANICKEL® alloy 301 o.. |
|||
| CTE, linear | 14.7 µm/m-°C @Temperature 21.0 - 500 °C |
8.17 µin/in-°F @Temperature 69.8 - 932 °F |
Mean; aged |
| Special Metals DURANICKEL® 301 (UNS N03301) Spring Strip Tensile strength (ultimate), hardness, and elongation values reported here are typical for Spring Strip specifically. Other property values are typical of annealed DURANICKEL® alloy 301 or the al.. |
|||
| CTE, linear | 14.7 µm/m-°C @Temperature 21.0 - 500 °C |
8.17 µin/in-°F @Temperature 69.8 - 932 °F |
Mean |
| Special Metals DURANICKEL® 301 (UNS N03301) Spring Wire, Aged Tensile strength (ultimate) and elongation values reported here are typical for Spring Wire, Aged specifically. Other property values are typical of aged DURANICKEL® alloy 301 or the alloy in gen.. |
|||
| CTE, linear | 14.7 µm/m-°C @Temperature 25.0 - 700 °C |
8.18 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Carpenter BioDur™ CCM Plus™ Medical Implant Alloy, Annealed 1093°C 1 hr Data provided by Carpenter Technology Corporation.Annealing followed by water quench and low stress grinding prior to tensile testing.Medical Implant Alloy. Non-magnetic Co-Cr-Mo alloy exhibiting h.. |
|||
| CTE, linear | 14.7 µm/m-°C @Temperature 20.0 - 700 °C |
8.17 µin/in-°F @Temperature 68.0 - 1290 °F |
|
| Carpenter Vega® Alloy Tool Steel (Air-Tough) (AISI A6) Vega die steel combines the deep hardening and minimum size change characteristics of air-hardening steels with the simplicity of low temperature heat treatment possible in many oil-hardening steels.. |
|||
| CTE, linear | 14.7 µm/m-°C @Temperature 20.0 - 100 °C |
8.17 µin/in-°F @Temperature 68.0 - 212 °F |
|
| ATI Allegheny Ludlum AL 20™ Sheet and Strip Specialty Steel The N08020 alloy has been available for many years and has found applications in many environments, such as in chlorides and in sulfuric and sulfurous acids.Although AL 20 alloy was developed for im.. |
|||
| CTE, linear | 14.7 µm/m-°C @Temperature 25.0 - 100 °C |
8.17 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 556® alloy, 20% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 14.7 µm/m-°C @Temperature 25.0 - 100 °C |
8.17 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 556® alloy, sheet after 1000 hours at 871°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 14.7 µm/m-°C @Temperature 21.0 - 760 °C |
8.17 µin/in-°F @Temperature 69.8 - 1400 °F |
|
| Haynes Hastelloy® N, 1.6 mm sheet, heat treated at 1175°C, rapid air cooled Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
| CTE, linear | 14.7 µm/m-°C @Temperature 25.0 - 100 °C |
8.17 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 556® alloy, 40% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 14.7 µm/m-°C @Temperature 21.0 - 760 °C |
8.17 µin/in-°F @Temperature 69.8 - 1400 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 649°C (1200°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
| CTE, linear | 14.7 µm/m-°C @Temperature 21.0 - 760 °C |
8.17 µin/in-°F @Temperature 69.8 - 1400 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, heat treated at 1149°C (2100°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
| CTE, linear | 14.7 µm/m-°C @Temperature 0.000 - 400 °C |
8.17 µin/in-°F @Temperature 32.0 - 752 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 11.1 mm thick plate, aged 3 hours at 816°C Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| CTE, linear | 14.7 µm/m-°C @Temperature 21.0 - 704 °C |
8.17 µin/in-°F @Temperature 69.8 - 1300 °F |
|
| Latrobe LSS™ A6 Tool Steel (ASTM A6) TLS A6 tool steel is a medium-alloy, air-hardening tool steel that is characterized by its ability to be through hardened while using the low austenitizing temperatures which are typically associate.. |
|||