- Polymer Property : CTE, linear = 14.9 µm/m-°C
Polymer Property : CTE, linear = 14.9 µm/m-°C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 14.9 µm/m-°C @Temperature 30.0 - 427 °C |
8.28 µin/in-°F @Temperature 86.0 - 801 °F |
|
| Haynes Hastelloy® G-30® alloy, mill annealed HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 20.0 - 871 °C |
8.28 µin/in-°F @Temperature 68.0 - 1600 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 20.0 - 871 °C |
8.28 µin/in-°F @Temperature 68.0 - 1600 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 20.0 - 871 °C |
8.28 µin/in-°F @Temperature 68.0 - 1600 °F |
|
| Haynes Hastelloy® S alloy, weld metal, aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 25.0 - 540 °C |
8.28 µin/in-°F @Temperature 77.0 - 1000 °F |
|
| Haynes HR-160® alloy, plate, aged 4000 hours at 871°C (1600°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 25.0 - 540 °C |
8.28 µin/in-°F @Temperature 77.0 - 1000 °F |
|
| Haynes HR-160® alloy, plate, aged 8000 hours at 760°C (1400°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 25.0 - 540 °C |
8.28 µin/in-°F @Temperature 77.0 - 1000 °F |
|
| Haynes HR-160® alloy, solution annealed sheet Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 25.0 - 200 °C |
8.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 556® alloy, 0% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 25.0 - 200 °C |
8.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 556® alloy, 10% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 25.0 - 200 °C |
8.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 556® alloy, 30% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 25.0 - 200 °C |
8.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 556® alloy, 50% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 25.0 - 200 °C |
8.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 556® alloy, 50% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 25.0 - 200 °C |
8.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 556® alloy, bar, after 1000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 25.0 - 200 °C |
8.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 556® alloy, bar, after 4000 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 24.0 - 871 °C |
8.28 µin/in-°F @Temperature 75.2 - 1600 °F |
|
| Haynes Hastelloy® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, aged 1000 hours at 649°C (1200°F) Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) rang.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 30.0 - 427 °C |
8.28 µin/in-°F @Temperature 86.0 - 801 °F |
|
| Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate, GTAW weld 3.2 mm diameter filler wire HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 30.0 - 427 °C |
8.28 µin/in-°F @Temperature 86.0 - 801 °F |
|
| Haynes Hastelloy® G-30® alloy, 50% cold rolled and 5000 hours at 500°C, air cooled HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 30.0 - 427 °C |
8.28 µin/in-°F @Temperature 86.0 - 801 °F |
|
| Haynes Hastelloy® G-30® alloy, plate and bar HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 25.0 - 540 °C |
8.28 µin/in-°F @Temperature 77.0 - 1000 °F |
|
| Haynes HR-160® alloy plate, aged 8000 hours at 649°C (1200°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 21.0 - 700 °C |
8.28 µin/in-°F @Temperature 69.8 - 1290 °F |
Mean |
| Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed 2150°F (1180°C) Tensile strength (ultimate and yield), elongation, and hardness values are for samples annealed 2150°F (1180°C)/5 minutes/AC. This produces ASTM grain size 5.5. Other property values are ty.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 21.0 - 700 °C |
8.28 µin/in-°F @Temperature 69.8 - 1290 °F |
Mean |
| Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed 2150°F (1180°C) + Aged 1400°F (760°C) Tensile strength (ultimate and yield), elongation, and hardness values are for samples annealed 2150°F (1180°C)/5 minutes/AC + Aged 1400°F (760°C)/100h/AC. This produces ASTM grain siz.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 25.0 - 200 °C |
8.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 556® alloy, 20% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 25.0 - 200 °C |
8.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 556® alloy, 20% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 25.0 - 200 °C |
8.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 556® alloy, 30% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 25.0 - 200 °C |
8.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 556® alloy, bar after 16000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 25.0 - 200 °C |
8.28 µin/in-°F @Temperature 77.0 - 392 °F |
|
| Haynes 556® alloy, sheet after 1000 hours at 871°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 24.0 - 871 °C |
8.28 µin/in-°F @Temperature 75.2 - 1600 °F |
|
| Haynes Hastelloy® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, GTAW Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T.. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 20.0 - 871 °C |
8.28 µin/in-°F @Temperature 68.0 - 1600 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
| CTE, linear | 14.9 µm/m-°C @Temperature 21.0 - 700 °C |
8.28 µin/in-°F @Temperature 69.8 - 1290 °F |
Mean |
| Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed 1950°F (1070°C) + Aged 1200°F (650°C) Tensile strength (ultimate and yield), elongation, and hardness values are for samples annealed 1950°F (1070°C)/5 minutes/AC + Aged 1200°F (650°C)/100h/AC. This produces ASTM grain size 9.5. .. |
|||