Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 15.1 µm/m-°C @Temperature 21.0 - 538 °C |
8.39 µin/in-°F @Temperature 69.8 - 1000 °F |
|
Kennametal Stellite Stellite® 31 PM with P/M Processing; heat treated at 93°C (200°F) and water quenched Typical applications include, miscellaneous wear parts. Data provided by the manufacturer, Deloro Stellite Inc.Product of former Deloro Stellite Inc. |
|||
CTE, linear | 15.1 µm/m-°C @Temperature 26.0 - 649 °C |
8.39 µin/in-°F @Temperature 78.8 - 1200 °F |
|
Haynes Ultimet® alloy, 12.7-50.8 mm bar Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
CTE, linear | 15.1 µm/m-°C @Temperature 26.0 - 649 °C |
8.39 µin/in-°F @Temperature 78.8 - 1200 °F |
|
Haynes Ultimet® alloy, 19.1 mm thick plate, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
CTE, linear | 15.1 µm/m-°C @Temperature 26.0 - 649 °C |
8.39 µin/in-°F @Temperature 78.8 - 1200 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 204°C (400°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
CTE, linear | 15.1 µm/m-°C @Temperature 26.0 - 649 °C |
8.39 µin/in-°F @Temperature 78.8 - 1200 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 538°C (1000°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
CTE, linear | 15.1 µm/m-°C @Temperature 26.0 - 649 °C |
8.39 µin/in-°F @Temperature 78.8 - 1200 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 760°C (1400°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
CTE, linear | 15.1 µm/m-°C @Temperature 26.0 - 649 °C |
8.39 µin/in-°F @Temperature 78.8 - 1200 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 871°C (1600°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
CTE, linear | 15.1 µm/m-°C @Temperature 26.0 - 649 °C |
8.39 µin/in-°F @Temperature 78.8 - 1200 °F |
|
Haynes Ultimet® alloy, all-weld metal, GMAW weld (spray) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 700 °C |
8.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
Haynes 25 alloy, cold worked sheet, 10% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 700 °C |
8.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
Haynes 25 alloy, cold worked sheet, 15 % cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 700 °C |
8.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
Haynes 25 alloy, room temperature after 25% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 700 °C |
8.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
Haynes 25 alloy, room temperature sheet after 1000 hours of 650°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 556® alloy, 10% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 556® alloy, 40% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 556® alloy, 40% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 556® alloy, 50% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 556® alloy, bar, after 1000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 556® alloy, bar, after 8000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 556® alloy, cold rolled, solution annealed sheet, 0.8-2.8 mm thick Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
CTE, linear | 15.1 µm/m-°C @Temperature 26.0 - 538 °C |
8.39 µin/in-°F @Temperature 78.8 - 1000 °F |
|
ATI Allegheny Ludlum Altemp® HX Nickel-Based superalloy Characteristics: outstanding resistance to oxidation at high temperatures, exceptional strength at elevated temperatures, good fabricability, good machinability in annealed condition, work hardening.. |
|||
CTE, linear | 15.1 µm/m-°C @Temperature 20.0 - 800 °C |
8.39 µin/in-°F @Temperature 68.0 - 1470 °F |
|
ATI Allegheny Ludlum Allcorr® Nickel-Based, Corrosion Resistant Alloy Characteristics: non-age hardenable; outstanding resistance to general corrosion, pitting corrosion, crevice corrosion, intergranular corrosion, and stress corrosion cracking; high strength; high du.. |
|||
CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 700 °C |
8.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
Haynes 25 alloy, room temperature after 10% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 700 °C |
8.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
Haynes 25 alloy, room temperature after 15% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 700 °C |
8.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
Haynes 25 alloy, room temperature after 15% cold reduction, 1175°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 556® alloy, 20% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 556® alloy, bar after 16000 hours at 871°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
CTE, linear | 15.1 µm/m-°C @Temperature 21.0 - 538 °C |
8.39 µin/in-°F @Temperature 69.8 - 1000 °F |
|
Kennametal Stellite Stellite® 31 PM cast aged 8 hours at 802°C air cooled Typical applications include vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing blanks, diesel engine exhaust, fluid valve seats, saw cutter inserts, miscellaneous we.. |
|||
CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 700 °C |
8.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
Haynes 25 alloy, room temperature after 15% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
CTE, linear | 15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 556® alloy, 40% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
CTE, linear | 15.1 µm/m-°C @Temperature 20.0 - 760 °C |
8.39 µin/in-°F @Temperature 68.0 - 1400 °F |
|
Haynes 617 Nickel Alloy Plate Haynes 617 alloy is a nickel-chromium-cobalt-molybdenum alloy with a good combination of metallurgical stability, strength, and oxidation resistance at high temperatures. The alloy is readily formed.. |