- Polymer Property : CTE, linear = 15.7 µm/m-°C
Polymer Property : CTE, linear = 15.7 µm/m-°C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 15.7 µm/m-°C @Temperature 21.1 - 649 °C |
8.72 µin/in-°F @Temperature 70.0 - 1200 °F |
|
| Kennametal Stellite Stellite® 31 PM cast Typical applications include vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing blanks, diesel engine exhaust, fluid valve seats, saw cutter inserts, miscellaneous we.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 900 °C |
8.72 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 230® alloy plate Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 900 °C |
8.72 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 230® alloy plate, 4000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 900 °C |
8.72 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 230® alloy, 10% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 900 °C |
8.72 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 230® alloy, 20% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 700 °C |
8.72 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes HR-160® alloy plate, aged 4000 hours at 649°C (1200°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 700 °C |
8.72 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes HR-160® alloy, annealed plate Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 700 °C |
8.72 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes HR-160® alloy, plate, aged 4000 hours at 760°C (1400°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 700 °C |
8.72 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes HR-160® alloy, solution annealed sheet Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 21.0 - 538 °C |
8.72 µin/in-°F @Temperature 69.8 - 1000 °F |
|
| Latrobe MP35N® Alloy MP35N is a nickel-cobalt base alloy of the Multiphase alloy system that has a unique combination of properties - ultra high strength, toughness, ductility, and outstanding corrosion resistance. The .. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 500 °C |
8.72 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 556® alloy, 0% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 500 °C |
8.72 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 556® alloy, 10% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 500 °C |
8.72 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 556® alloy, 40% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 500 °C |
8.72 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 556® alloy, 50% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 500 °C |
8.72 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 556® alloy, bar, after 1000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 500 °C |
8.72 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 556® alloy, bar, after 8000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 0.000 - 100 °C |
8.72 µin/in-°F @Temperature 32.0 - 212 °F |
|
| AK Steel 201 Austenitic Stainless steel AK Steel 210 was developed originally to conserve nickel. It provides properties similar to Type 301 and can be used in most applications for Type 301. This alloy is non-magnetic in the annealed c.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 0.000 - 100 °C |
8.72 µin/in-°F @Temperature 32.0 - 212 °F |
|
| AK Steel 201LN Austenitic Stainless steel AK Steel 210 was developed originally to conserve nickel. It provides properties similar to Type 301 and can be used in most applications for Type 301. This alloy is non-magnetic in the annealed c.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 21.0 - 538 °C |
8.72 µin/in-°F @Temperature 69.8 - 1000 °F |
|
| Carpenter MP35N* Ni-Co-Cr-Mo Alloy, 0% Cold Reduction + Aged 538°C (1000°F)/4hr/AC Data provided by Carpenter Technology Corporation.Carpenter MP35N alloy is a nonmagnetic, nickel-cobalt-chromium-molybdenum alloy possessing a unique combination of ultrahigh tensile strength, good .. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 21.0 - 538 °C |
8.72 µin/in-°F @Temperature 69.8 - 1000 °F |
|
| Carpenter MP35N* Ni-Co-Cr-Mo Alloy, 35% Cold Reduction + Aged 538°C (1000°F)/4hr/AC Data provided by Carpenter Technology Corporation.Carpenter MP35N alloy is a nonmagnetic, nickel-cobalt-chromium-molybdenum alloy possessing a unique combination of ultrahigh tensile strength, good .. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 900 °C |
8.72 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 230® alloy, GMAW deposit weld metal Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 500 °C |
8.72 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 556® alloy, 20% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 500 °C |
8.72 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 556® alloy, 40% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 500 °C |
8.72 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 556® alloy, bar after 16000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 20.0 - 982 °C |
8.72 µin/in-°F @Temperature 68.0 - 1800 °F |
|
| Haynes Hastelloy® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, GTAW Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 21.1 - 649 °C |
8.72 µin/in-°F @Temperature 70.0 - 1200 °F |
|
| Kennametal Stellite Stellite® 31 PM cast aged 8 hours at 802°C air cooled Typical applications include vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing blanks, diesel engine exhaust, fluid valve seats, saw cutter inserts, miscellaneous we.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 20.0 - 427 °C |
8.72 µin/in-°F @Temperature 68.0 - 801 °F |
|
| ATI Allegheny Ludlum AL 825™ Nickel Alloy Allegheny Ludlum AL 825 alloy is an austenitic nickel-iron-chromium-molybdenum-copper alloy containing high levels of corrosion resistance to both moderately oxidizing and moderately reducing enviro.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 900 °C |
8.72 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 230® alloy plate, 16000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 900 °C |
8.72 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 230® alloy plate, 8000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| CTE, linear | 15.7 µm/m-°C @Temperature 25.0 - 900 °C |
8.72 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 230® alloy, plate, 4000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||