Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 16.5 µm/m-°C @Thickness 0.0508 mm, Temperature 0.000 - 150 °C |
9.17 µin/in-°F @Thickness 0.00200 in, Temperature 32.0 - 302 °F |
X-Direction; IPC-TM-650 2.1.41 |
Rogers Corporation Syron™ 7100 Thermoplastic Circuit Material SYRON™ 7100 thermoplastic circuit materials provide an excellent solution for printed circuit board applications used in demanding environmental conditions. SYRON 7100 is thermally stable, with a .. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 200 °C |
9.17 µin/in-°F @Temperature 392 °F |
|
Outokumpu 4306 Cr-Ni Austenitic Stainless Steel General purpose steel with good corrosion resistance.Applications: Wide variety of applications in construction, chemical, petroleum, automobile, and domestic appliance markets.Available in hot roll.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 0.000 - 300 °C |
9.17 µin/in-°F @Temperature 32.0 - 572 °F |
|
Industeel URANUS® 65 310 L Modified Grade - Low C and Si for Nitric Acid Service Description: URANUS® 65 is a 25 Cr 20 Ni austenitic stainless steel with sharp control of the residual elements in order to provide high corrosion resistance properties in boiling 50-65% Nitric a.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 20.0 - 300 °C |
9.17 µin/in-°F @Temperature 68.0 - 572 °F |
|
Industeel URANUS® B28 High Nickel Super-Austenitic Stainless Steel Description: URANUS® B28 (UR B28) is a super-austenitic stainless steel with very high nickel (31%) and chromium (27%) contents. The molybdenum content is about 3.5%. The alloy is designed for sp.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 800 °C |
9.17 µin/in-°F @Temperature 77.0 - 1470 °F |
|
Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 800 °C |
9.17 µin/in-°F @Temperature 77.0 - 1470 °F |
|
Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 800 °C |
9.17 µin/in-°F @Temperature 77.0 - 1470 °F |
|
Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 800 °C |
9.17 µin/in-°F @Temperature 77.0 - 1470 °F |
|
Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 800 °C |
9.17 µin/in-°F @Temperature 77.0 - 1470 °F |
|
Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 800 °C |
9.17 µin/in-°F @Temperature 77.0 - 1470 °F |
|
Haynes 188 alloy, hot rolled and 1175°C solution annealed plate Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 800 °C |
9.17 µin/in-°F @Temperature 77.0 - 1470 °F |
|
Haynes 188 alloy, plate at RT after 0 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 800 °C |
9.17 µin/in-°F @Temperature 77.0 - 1470 °F |
|
Haynes 188 alloy, plate at RT after 16000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 800 °C |
9.17 µin/in-°F @Temperature 77.0 - 1470 °F |
|
Haynes 188 alloy, plate at RT after 8000 hours at 650°C (1200°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 800 °C |
9.17 µin/in-°F @Temperature 77.0 - 1470 °F |
|
Haynes 188 alloy, plate at RT after 8000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 900 °C |
9.17 µin/in-°F @Temperature 77.0 - 1650 °F |
|
Haynes 25 alloy, hot rolled and 1230°C solution annealed sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 900 °C |
9.17 µin/in-°F @Temperature 77.0 - 1650 °F |
|
Haynes 25 alloy, cold worked sheet, 15 % cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 900 °C |
9.17 µin/in-°F @Temperature 77.0 - 1650 °F |
|
Haynes 25 alloy, room temperature sheet after 1000 hours of 870°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 900 °C |
9.17 µin/in-°F @Temperature 77.0 - 1650 °F |
|
Haynes 25 alloy, room temperature sheet after 2500 hours of 650°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 900 °C |
9.17 µin/in-°F @Temperature 77.0 - 1650 °F |
|
Haynes 25 alloy, sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 20.0 - 100 °C |
9.17 µin/in-°F @Temperature 68.0 - 212 °F |
|
ATI Allegheny Ludlum Type 316L Stainless Steel, UNS S31603 This is a molybdenum-bearing austenitic stainless steels which is more resistant to general corrosion and pitting/crevice corrosion than the conventional chromium-nickel austenitic stainless steels .. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 900 °C |
9.17 µin/in-°F @Temperature 77.0 - 1650 °F |
|
Haynes 25 alloy, room temperature after 15% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 900 °C |
9.17 µin/in-°F @Temperature 77.0 - 1650 °F |
|
Haynes 25 alloy, room temperature after 20% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 21.1 - 816 °C |
9.17 µin/in-°F @Temperature 70.0 - 1500 °F |
|
Kennametal Stellite Stellite® 31 PM after P/M processing, aged 8 hours at 802°C air cooled Typical applications include vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing blanks, diesel engine exhaust, fluid valve seats, saw cutter inserts, miscellaneous we.. |
|||
CTE, linear | 16.5 µm/m-°C @Temperature 25.0 - 900 °C |
9.17 µin/in-°F @Temperature 77.0 - 1650 °F |
|
Haynes 25 alloy, room temperature after 10% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |