- Polymer Property : CTE, linear = 16.9 µm/m-°C
Polymer Property : CTE, linear = 16.9 µm/m-°C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 16.9 µm/m-°C @Temperature 400 °C |
9.39 µin/in-°F @Temperature 752 °F |
|
| Outokumpu 4529 Austenitic Stainless Steel Applications: Wet corrosion resistance and general service.Available in hot rolled plate (Quarto) form. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 0.000 - 900 °C |
9.39 µin/in-°F @Temperature 32.0 - 1650 °F |
|
| Kennametal Stellite Stellite® 6 PM with P/M Processing Adhesive wear test data: 0.49 P/M, 0.48 Cast; Typical applications include: (aerospace) vane plugs, fuel metering pins, spacer bushings, (bearings) ball blanks, race blanks, (valve seat inserts) die.. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 0.000 - 900 °C |
9.39 µin/in-°F @Temperature 32.0 - 1650 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, 12.7 mm (1/2 in.) thick plate Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 0.000 - 900 °C |
9.39 µin/in-°F @Temperature 32.0 - 1650 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, 15.9 mm thick bar Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 0.000 - 900 °C |
9.39 µin/in-°F @Temperature 32.0 - 1650 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 11.1 mm thick plate Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 0.000 - 900 °C |
9.39 µin/in-°F @Temperature 32.0 - 1650 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 15.9 mm thick plate Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 0.000 - 900 °C |
9.39 µin/in-°F @Temperature 32.0 - 1650 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 7.9 mm thick plate, aged 3 hours at 816°C Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 25.0 - 700 °C |
9.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes HR-120® alloy, solution heat-treated aged at 1200°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 25.0 - 700 °C |
9.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes HR-120® alloy, solution heat-treated aged at 1400°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 25.0 - 700 °C |
9.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes HR-120® alloy, solution heat-treated aged at 1600°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 25.0 - 700 °C |
9.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes HR-120® alloy, solution heat-treated aged at 1800°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 26.0 - 982 °C |
9.39 µin/in-°F @Temperature 78.8 - 1800 °F |
|
| Haynes Ultimet® alloy, 1.6 mm sheet Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 26.0 - 982 °C |
9.39 µin/in-°F @Temperature 78.8 - 1800 °F |
|
| Haynes Ultimet® alloy, 12.7 mm (1/2 in.) thick plate, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 26.0 - 982 °C |
9.39 µin/in-°F @Temperature 78.8 - 1800 °F |
|
| Haynes Ultimet® alloy, 12.7-50.8 mm bar Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 26.0 - 982 °C |
9.39 µin/in-°F @Temperature 78.8 - 1800 °F |
|
| Haynes Ultimet® alloy, 19.1 mm thick plate, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 26.0 - 982 °C |
9.39 µin/in-°F @Temperature 78.8 - 1800 °F |
|
| Haynes Ultimet® alloy, 6.3-38.1 mm plate Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 26.0 - 982 °C |
9.39 µin/in-°F @Temperature 78.8 - 1800 °F |
|
| Haynes Ultimet® alloy, aged 1000 hours at 649°C (1200°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 26.0 - 982 °C |
9.39 µin/in-°F @Temperature 78.8 - 1800 °F |
|
| Haynes Ultimet® alloy, aged 1000 hours at 871°C (1600°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 26.0 - 982 °C |
9.39 µin/in-°F @Temperature 78.8 - 1800 °F |
|
| Haynes Ultimet® alloy, aged 1000 hours at 982°C Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 26.0 - 982 °C |
9.39 µin/in-°F @Temperature 78.8 - 1800 °F |
|
| Haynes Ultimet® alloy, all-weld metal, GMAW weld (spray) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 26.0 - 982 °C |
9.39 µin/in-°F @Temperature 78.8 - 1800 °F |
|
| Haynes Ultimet® alloy, all-weld metal, GTAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 26.0 - 982 °C |
9.39 µin/in-°F @Temperature 78.8 - 1800 °F |
|
| Haynes Ultimet® alloy, all-weld metal, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 0.000 - 900 °C |
9.39 µin/in-°F @Temperature 32.0 - 1650 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 3.2 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 25.0 - 700 °C |
9.39 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes HR-120® alloy, solution heat-treated plate Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 27.0 - 300 °C |
9.39 µin/in-°F @Temperature 80.6 - 572 °F |
Mean |
| Special Metals INCOLOY® A-286 Iron-Nickel-Chromium Alloy Data provided by the manufacturer, Special Metals. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 0.000 - 100 °C |
9.39 µin/in-°F @Temperature 32.0 - 212 °F |
|
| AK Steel 301 Austenitic Stainless steel AK Steel 301 provides high strength and good ductility when cold worked. It is a modification of AK Steel 302 to increase the cold work-hardening range, to permit higher tensile strengths to be ach.. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 0.000 - 100 °C |
9.39 µin/in-°F @Temperature 32.0 - 212 °F |
|
| AK Steel 304 Austenitic Stainless steel AK Steel 304 is a variation of the basic 18-8 grade, Type 302. Lower carbon, in Type 304, minimizes chromium carbide precipitation due to welding and its susceptibility to intergranular corrosion. .. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature <=538 °C |
9.39 µin/in-°F @Temperature <=1000 °F |
|
| AK Steel PH 15-7 Mo® Precipitation Hardening Stainless Steel, Condition A AK Steel 15-7 Mo® provides high strength and hardness, good corrosion resistance and minimum distortion on heat treatment. It is easily formed in the annealed condition and develops effective bala.. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 400 °C |
9.39 µin/in-°F @Temperature 752 °F |
|
| Outokumpu 904L High Performance Austenitic Stainless Steel Applications: Process equipment in chemical industryBleaching equipment in the pulp and paper industryFlue-gas cleaningDesalinationSeawater handlingHeat exchangersAvailable in hot rolled plate (Quar.. |
|||
| CTE, linear | 16.9 µm/m-°C @Temperature 0.000 - 900 °C |
9.39 µin/in-°F @Temperature 32.0 - 1650 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 11.1 mm thick plate, aged 3 hours at 816°C Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||