Polymer Property : CTE, linear = 17.1 µm/m-°C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
CTE, linear 17.1 µm/m-°C

@Temperature 25.0 - 800 °C
9.50 µin/in-°F

@Temperature 77.0 - 1470 °F
Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes
Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr..
CTE, linear 17.1 µm/m-°C

@Temperature 25.0 - 800 °C
9.50 µin/in-°F

@Temperature 77.0 - 1470 °F
Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes
Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr..
CTE, linear 17.1 µm/m-°C

@Temperature 25.0 - 800 °C
9.50 µin/in-°F

@Temperature 77.0 - 1470 °F
Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet
Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr..
CTE, linear 17.1 µm/m-°C

@Temperature 25.0 - 800 °C
9.50 µin/in-°F

@Temperature 77.0 - 1470 °F
Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes
Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr..
CTE, linear 17.1 µm/m-°C

@Temperature 25.0 - 800 °C
9.50 µin/in-°F

@Temperature 77.0 - 1470 °F
Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes
Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr..
CTE, linear 17.1 µm/m-°C

@Temperature 25.0 - 800 °C
9.50 µin/in-°F

@Temperature 77.0 - 1470 °F
Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes
Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr..
CTE, linear 17.1 µm/m-°C

@Temperature 25.0 - 800 °C
9.50 µin/in-°F

@Temperature 77.0 - 1470 °F
Haynes 188 alloy, hot rolled and 1175°C solution annealed plate
Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr..
CTE, linear 17.1 µm/m-°C

@Temperature 25.0 - 800 °C
9.50 µin/in-°F

@Temperature 77.0 - 1470 °F
Haynes 188 alloy, plate at RT after 1000 hours at 870°C (1600°F)
Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr..
CTE, linear 17.1 µm/m-°C

@Temperature 25.0 - 800 °C
9.50 µin/in-°F

@Temperature 77.0 - 1470 °F
Haynes 188 alloy, plate at RT after 8000 hours at 870°C (1600°F)
Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr..
CTE, linear 17.1 µm/m-°C

@Temperature 25.0 - 900 °C
9.50 µin/in-°F

@Temperature 77.0 - 1650 °F
Haynes HR-160® alloy plate, aged 1000 hours at 649°C (1200°F)
Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
CTE, linear 17.1 µm/m-°C

@Temperature 25.0 - 900 °C
9.50 µin/in-°F

@Temperature 77.0 - 1650 °F
Haynes HR-160® alloy plate, aged 4000 hours at 649°C (1200°F)
Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
CTE, linear 17.1 µm/m-°C

@Temperature 25.0 - 900 °C
9.50 µin/in-°F

@Temperature 77.0 - 1650 °F
Haynes HR-160® alloy, annealed plate
Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
CTE, linear 17.1 µm/m-°C

@Temperature 25.0 - 900 °C
9.50 µin/in-°F

@Temperature 77.0 - 1650 °F
Haynes HR-160® alloy, plate, aged 1000 hours at 760°C (1400°F)
Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
CTE, linear 17.1 µm/m-°C

@Temperature 25.0 - 900 °C
9.50 µin/in-°F

@Temperature 77.0 - 1650 °F
Haynes HR-160® alloy, plate, aged 1000 hours at 871°C (1600°F)
Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
CTE, linear 17.1 µm/m-°C

@Temperature 25.0 - 900 °C
9.50 µin/in-°F

@Temperature 77.0 - 1650 °F
Haynes HR-160® alloy, plate, aged 4000 hours at 760°C (1400°F)
Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
CTE, linear 17.1 µm/m-°C

@Temperature 25.0 - 900 °C
9.50 µin/in-°F

@Temperature 77.0 - 1650 °F
Haynes HR-160® alloy, plate, aged 4000 hours at 871°C (1600°F)
Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
CTE, linear 17.1 µm/m-°C

@Temperature 25.0 - 800 °C
9.50 µin/in-°F

@Temperature 77.0 - 1470 °F
Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes
Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr..
CTE, linear 17.1 µm/m-°C

@Temperature 25.0 - 1000 °C
9.50 µin/in-°F

@Temperature 77.0 - 1830 °F
Haynes 556® alloy, 30% cold reduction, 1010°C anneal for 5 minutes
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
CTE, linear 17.1 µm/m-°C

@Temperature 25.0 - 1000 °C
9.50 µin/in-°F

@Temperature 77.0 - 1830 °F
Haynes 556® alloy, 50% cold reduction, 1010°C anneal for 5 minutes
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
CTE, linear 17.1 µm/m-°C

@Temperature 25.0 - 1000 °C
9.50 µin/in-°F

@Temperature 77.0 - 1830 °F
Haynes 556® alloy, all-weld metal GTAW
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
CTE, linear 17.1 µm/m-°C

@Temperature 25.0 - 1000 °C
9.50 µin/in-°F

@Temperature 77.0 - 1830 °F
Haynes 556® alloy, bar, after 1000 hours at 760°C (1400°F)
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
CTE, linear 17.1 µm/m-°C

@Temperature 25.0 - 1000 °C
9.50 µin/in-°F

@Temperature 77.0 - 1830 °F
Haynes 556® alloy, sheet after 1000 hours at 760°C (1400°F)
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
CTE, linear 17.1 µm/m-°C

@Temperature 0.000 - 316 °C
9.50 µin/in-°F

@Temperature 32.0 - 600 °F
Crucible Steel 348 Chromium-Nickel Steel
Crucible 348 is a non-hardenable austenitic chromium-nickel steel which are particularly adaptable for use at temperatures between 800 and 1650°F. This grade is non-magnetic in the annealed conditi..
CTE, linear 17.1 µm/m-°C

@Temperature 25.0 - 250 °C
9.48 µin/in-°F

@Temperature 77.0 - 482 °F
Carpenter Gall-Tough PLUS™ Stainless, Annealed
Data provided by Carpenter Technology Corporation.6.4 mm diameter tensile specimens from center of 25.4 mm diameter bar annealed 1066°C 1 hour, water quenched, and ground.Threshold Galling Stress 4..
CTE, linear 17.1 µm/m-°C

@Temperature 25.0 - 250 °C
9.48 µin/in-°F

@Temperature 77.0 - 482 °F
Carpenter Gall-Tough PLUS™ Stainless, Annealed, 15% Cold Work
Data provided by Carpenter Technology Corporation.Annealed 1150°C, water quenched, and cold drawn.Threshold Galling Stress 48 MPa. The avg. total volume loss on the wear test is 10.6 mm³ at 100 r..
CTE, linear 17.1 µm/m-°C

@Temperature 20.0 - 500 °C
9.50 µin/in-°F

@Temperature 68.0 - 932 °F
ATI Allegheny Ludlum 310H Austenitic Stainless Steel
Characteristics: comparable corrosion resistance, superior resistance to oxidation, and the retention of a larger fraction of room temperature strength than common austenitic alloys. Good creep defo..
CTE, linear 17.1 µm/m-°C

@Temperature 20.0 - 500 °C
9.50 µin/in-°F

@Temperature 68.0 - 932 °F
ATI Allegheny Ludlum 310Si Austenitic Stainless Steel
Characteristics: comparable corrosion resistance, superior resistance to oxidation, and the retention of a larger fraction of room temperature strength than common austenitic alloys. Good creep defo..
CTE, linear 17.1 µm/m-°C

@Temperature 25.0 - 250 °C
9.48 µin/in-°F

@Temperature 77.0 - 482 °F
Carpenter Gall-Tough PLUS™ Stainless, Annealed, 20% Cold Work
Data provided by Carpenter Technology Corporation.Annealed 1150°C, water quenched, and cold drawn.Threshold Galling Stress 48 MPa. The avg. total volume loss on the wear test is 10.6 mm³ at 100 r..
CTE, linear 17.1 µm/m-°C

@Temperature 25.0 - 250 °C
9.48 µin/in-°F

@Temperature 77.0 - 482 °F
Carpenter Gall-Tough PLUS™ Stainless, Annealed, 25% Cold Work
Data provided by Carpenter Technology Corporation.Annealed 1150°C, water quenched, and cold drawn.Threshold Galling Stress 48 MPa. The avg. total volume loss on the wear test is 10.6 mm³ at 100 r..
CTE, linear 17.1 µm/m-°C

@Temperature 25.0 - 1000 °C
9.50 µin/in-°F

@Temperature 77.0 - 1830 °F
Haynes 556® alloy, 40% cold reduction
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..