- HOME
- POLYMER SEARCH
- Polymer Property : CTE, linear = 7.11 µin/in-°F
Polymer Property : CTE, linear = 7.11 µin/in-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 12.8 µm/m-°C @Temperature 20.0 - 300 °C |
7.11 µin/in-°F @Temperature 68.0 - 572 °F |
|
| Kennametal Stellite Deloro® 40G Nickel base. Good combination of wear resistance, corrosion resistance, machinability, and repairability. Machined with tungsten carbide tools, using slow speeds and light feeds. Finish grinding ach.. |
|||
| CTE, linear | 12.8 µm/m-°C @Temperature 20.0 - 100 °C |
7.11 µin/in-°F @Temperature 68.0 - 212 °F |
|
| Kennametal Stellite Stellite® 19 Can be machined with carbide tipped tools, but when hardness exceeds Rc55 it is best to grind. Applications include cutting tools, bearing races, guide rolls, and nozzle discs. Excellent resistance .. |
|||
| CTE, linear | 12.8 µm/m-°C @Temperature 20.0 - 200 °C |
7.11 µin/in-°F @Temperature 68.0 - 392 °F |
|
| Industeel CREUSABRO® 4000 High Wear Resistant Steel Description: CREUSABRO® 4000 is a high wear resistant steel, offering a 30 % extra in service life compared to a conventional 400 HB water quenched. Improved properties of CREUSABRO® 4000 resu.. |
|||
| CTE, linear | 12.8 µm/m-°C @Temperature 20.0 - 316 °C |
7.11 µin/in-°F @Temperature 68.0 - 601 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 12.8 µm/m-°C @Temperature 20.0 - 316 °C |
7.11 µin/in-°F @Temperature 68.0 - 601 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| CTE, linear | 12.8 µm/m-°C @Temperature 25.0 - 100 °C |
7.11 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 12.8 µm/m-°C @Temperature 25.0 - 100 °C |
7.11 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 12.8 µm/m-°C @Temperature 25.0 - 100 °C |
7.11 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 625 alloy, plate after 16000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 12.8 µm/m-°C @Temperature 25.0 - 100 °C |
7.11 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 625 alloy, plate after 4000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 12.8 µm/m-°C @Temperature 25.0 - 100 °C |
7.11 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 625 alloy, plate, as annealed at 1025°C, rapid cooled Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 12.8 µm/m-°C @Temperature 23.9 - 316 °C |
7.11 µin/in-°F @Temperature 75.0 - 600 °F |
|
| HP Alloys Alloy C-276, 10% Cold Worked 10% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, Inco Alloys International, and Haynes Internati.. |
|||
| CTE, linear | 12.8 µm/m-°C @Temperature 23.9 - 316 °C |
7.11 µin/in-°F @Temperature 75.0 - 600 °F |
|
| HP Alloys Alloy C-276, 20% Cold Worked 20% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, Inco Alloys International, and Haynes Internati.. |
|||
| CTE, linear | 12.8 µm/m-°C @Temperature 23.9 - 316 °C |
7.11 µin/in-°F @Temperature 75.0 - 600 °F |
|
| HP Alloys Alloy C-276, 40% Cold Worked 40% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, Inco Alloys International, and Haynes Internati.. |
|||
| CTE, linear | 12.8 µm/m-°C @Temperature 21.0 - 100 °C |
7.11 µin/in-°F @Temperature 69.8 - 212 °F |
Mean |
| Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 15% Cold Work Tensile strength (ultimate and yield), elongation, and reduction of area values are for annealed then cold worked samples. This produces ASTM grain size 9.0. Other property values are typical of t.. |
|||
| CTE, linear | 12.8 µm/m-°C @Temperature 21.0 - 100 °C |
7.11 µin/in-°F @Temperature 69.8 - 212 °F |
Mean |
| Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed 1950°F (1070°C) Tensile strength (ultimate and yield), elongation, and hardness values are for samples annealed 1950°F (1070°C)/5 minutes/AC. This produces ASTM grain size 9.5. Other property values are ty.. |
|||
| CTE, linear | 12.8 µm/m-°C @Temperature 21.0 - 100 °C |
7.11 µin/in-°F @Temperature 69.8 - 212 °F |
Mean |
| Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed 2150°F (1180°C) + Aged 1400°F (760°C) Tensile strength (ultimate and yield), elongation, and hardness values are for samples annealed 2150°F (1180°C)/5 minutes/AC + Aged 1400°F (760°C)/100h/AC. This produces ASTM grain siz.. |
|||
| CTE, linear | 12.8 µm/m-°C @Temperature 100 °C |
7.11 µin/in-°F @Temperature 212 °F |
|
| Bohler-Uddeholm BÖHLER M268 VMR® Plastic Mold Steel Description: HBÖHLER M268 VMR is a hardened and tempered plastic mould steel with excellent cleanliness for best polishability. The hardness is constant over the entire cross-section of the steel b.. |
|||
| CTE, linear | 12.8 µm/m-°C @Temperature <=871 °C |
7.11 µin/in-°F @Temperature <=1600 °F |
|
| AK Steel 400 Ferritic Stainless steel AK Steel 400 is one of the most economical chromium ferritic stainless steels. It has corrosion and oxidation resistance comparable to Type 410 stainless steel with good fabricating characteristics.. |
|||
| CTE, linear | 12.8 µm/m-°C @Temperature 21.0 - 93.0 °C |
7.11 µin/in-°F @Temperature 69.8 - 199 °F |
|
| Carpenter MP35N* Ni-Co-Cr-Mo Alloy, 53% Cold Reduction + Aged 538°C (1000°F)/4hr/AC Data provided by Carpenter Technology Corporation.Carpenter MP35N alloy is a nonmagnetic, nickel-cobalt-chromium-molybdenum alloy possessing a unique combination of ultrahigh tensile strength, good .. |
|||
| CTE, linear | 12.8 µm/m-°C @Temperature 21.0 - 93.0 °C |
7.11 µin/in-°F @Temperature 69.8 - 199 °F |
|
| Carpenter MP35N* Ni-Co-Cr-Mo Alloy, 55% Cold Reduction Data provided by Carpenter Technology Corporation.Carpenter MP35N alloy is a nonmagnetic, nickel-cobalt-chromium-molybdenum alloy possessing a unique combination of ultrahigh tensile strength, good .. |
|||
| CTE, linear | 12.8 µm/m-°C @Temperature 21.0 - 93.0 °C |
7.11 µin/in-°F @Temperature 69.8 - 199 °F |
|
| Carpenter MP35N* Ni-Co-Cr-Mo Alloy, Cold Drawn 33%, Aged 565°C/4hr/AC Data provided by Carpenter Technology Corporation.Carpenter MP35N alloy is a nonmagnetic, nickel-cobalt-chromium-molybdenum alloy possessing a unique combination of ultrahigh tensile strength, good .. |
|||
| CTE, linear | 12.8 µm/m-°C @Temperature 20.0 - 600 °C |
7.11 µin/in-°F @Temperature 68.0 - 1110 °F |
|
| ATI Allegheny Ludlum 425 Mod Martensitic Stainless Steel Characteristics: superior wear resistance, hardenable, excellent corrosion resistance. Applications:cutlery, dental and surgical instruments, nozzles, valve parts, hardened steel ball and seats for.. |
|||
| CTE, linear | 12.8 µm/m-°C @Temperature 20.0 - 600 °C |
7.11 µin/in-°F @Temperature 68.0 - 1110 °F |
|
| ATI Allegheny Ludlum Martensitic Stainless Steel Type 425 Mod, Hardened + 204°C Temper Allegheny Ludlum Type 425 Mod is a hardenable straight-chromium stainless steel which combines superior wear resistance of high carbon alloys with the excellent corrosion resistance of chromium stai.. |
|||
| CTE, linear | 12.8 µm/m-°C @Temperature 20.0 - 600 °C |
7.11 µin/in-°F @Temperature 68.0 - 1110 °F |
|
| ATI Allegheny Ludlum Martensitic Stainless Steel Type 425 Mod, Hardened + 482°C Temper Allegheny Ludlum Type 425 Mod is a hardenable straight-chromium stainless steel which combines superior wear resistance of high carbon alloys with the excellent corrosion resistance of chromium stai.. |
|||
| CTE, linear | 12.8 µm/m-°C @Temperature 25.0 - 100 °C |
7.11 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| CTE, linear | 12.8 µm/m-°C @Temperature 20.0 - 316 °C |
7.11 µin/in-°F @Temperature 68.0 - 601 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
| CTE, linear | 12.8 µm/m-°C @Temperature 0.000 - 100 °C |
7.11 µin/in-°F @Temperature 32.0 - 212 °F |
|
| Carpenter BioDur™ CCM Plus™ Medical Implant Alloy, Hot Worked Data provided by Carpenter Technology Corporation.Medical Implant Alloy. Non-magnetic Co-Cr-Mo alloy exhibiting high strength, corrosion resistance, and wear resistance. BioDur CCM Plus alloy is a.. |
|||
| CTE, linear | 12.8 µm/m-°C @Temperature 20.0 - 500 °C |
7.11 µin/in-°F @Temperature 68.0 - 932 °F |
|
| ATI Allegheny Ludlum ALFA-I™ Stainless Steel Type 406 Characteristics:superior oxidation resistance for the temperature range 1600°F-over 2200°F, high electrical resistivity, high resistance to sulfidation, high resistance to carburization. Applicat.. |
|||
| CTE, linear | 12.8 µm/m-°C @Temperature 25.0 - 100 °C |
7.11 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| CTE, linear | 12.8 µm/m-°C @Temperature 21.0 - 100 °C |
7.11 µin/in-°F @Temperature 69.8 - 212 °F |
Mean |
| Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed 1950°F (1070°C) + Aged 1200°F (650°C) Tensile strength (ultimate and yield), elongation, and hardness values are for samples annealed 1950°F (1070°C)/5 minutes/AC + Aged 1200°F (650°C)/100h/AC. This produces ASTM grain size 9.5. .. |
|||
Copyright © lookpolymers.com All Rights Reserved