- Polymer Property : CTE, linear = 7.94 µin/in-°F
Polymer Property : CTE, linear = 7.94 µin/in-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 14.3 µm/m-°C @Temperature 0.000 - 900 °C |
7.94 µin/in-°F @Temperature 32.0 - 1650 °F |
|
| Kennametal Stellite Stellite® STAR cast Applications: Vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing blanks, diesel engine exhaust, fluid valve seats, saw cutter inserts, wear pads, pins, balls, hardfa.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 0.000 - 900 °C |
7.94 µin/in-°F @Temperature 32.0 - 1650 °F |
|
| Kennametal Stellite Stellite® STAR with P/M Processing Applications: Vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing blanks, diesel engine exhaust, fluid valve seats, saw cutter inserts, wear pads, pins, balls, hardfa.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 500 °C |
7.94 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 25 alloy, cold worked sheet, 15% cold reduction, aged at 370°C (700°F) for 1 hour Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 100 °C |
7.94 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes HR-120® alloy, solution heat-treated aged at 1200°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 100 °C |
7.94 µin/in-°F @Temperature 77.0 - 212 °F |
|
| Haynes HR-120® alloy, solution heat-treated aged at 1800°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 500 °C |
7.94 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 25 alloy, cold worked sheet, 10% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 400 °C |
7.94 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 25 alloy, cold worked sheet, 10% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 500 °C |
7.94 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 25 alloy, cold worked sheet, 15 % cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 500 °C |
7.94 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 25 alloy, room temperature after 25% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 400 °C |
7.94 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 25 alloy, room temperature after 25% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 500 °C |
7.94 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 25 alloy, room temperature after 25% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 400 °C |
7.94 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 25 alloy, room temperature after 25% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 500 °C |
7.94 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 25 alloy, room temperature sheet after 100 hours of 760°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 500 °C |
7.94 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 25 alloy, room temperature sheet after 1000 hours of 650°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 500 °C |
7.94 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 25 alloy, room temperature sheet after 2500 hours of 650°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 400 °C |
7.94 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 25 alloy, room temperature sheet after 2500 hours of 650°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 500 °C |
7.94 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 25 alloy, room temperature sheet after 500 hours of 650°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 500 °C |
7.94 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 25 alloy, vacuum investment castings, solution treated Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 38.0 - 649 °C |
7.94 µin/in-°F @Temperature 100 - 1200 °F |
|
| Latrobe Lescalloy® 52100 VAC-ARC High Performance Bearing Steel LESCALLOY 52100 VAC-ARC is a deep hardening alloy steel used for aircraft bearings and other high stressed parts where good rolling contact fatigue strength is required at operating temperatures bel.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 500 °C |
7.94 µin/in-°F @Temperature 77.0 - 932 °F |
|
| HP Alloys Alloy 718, 15% Cold Worked, Aged 15% Cold Worked, Aged applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, Inco Alloys International, and Haynes Int.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 500 °C |
7.94 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 25 alloy, room temperature after 10% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 500 °C |
7.94 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 25 alloy, room temperature after 10% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 500 °C |
7.94 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 25 alloy, room temperature after 10% cold reduction, 1175°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 500 °C |
7.94 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 25 alloy, room temperature after 15% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 400 °C |
7.94 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 25 alloy, room temperature after 15% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 400 °C |
7.94 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 25 alloy, room temperature after 15% cold reduction, 1175°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 400 °C |
7.94 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 25 alloy, room temperature after 20% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 400 °C |
7.94 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes 25 alloy, room temperature after 10% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 500 °C |
7.94 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 25 alloy, room temperature after 15% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| CTE, linear | 14.3 µm/m-°C @Temperature 25.0 - 500 °C |
7.94 µin/in-°F @Temperature 77.0 - 932 °F |
|
| HP Alloys Alloy 718, 25% Cold Worked 25% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, Inco Alloys International, and Haynes Internati.. |
|||