- Polymer Property : CTE, linear = 8.78 µin/in-°F
Polymer Property : CTE, linear = 8.78 µin/in-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 15.8 µm/m-°C @Temperature 0.000 - 700 °C |
8.78 µin/in-°F @Temperature 32.0 - 1290 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, 1.6 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 0.000 - 700 °C |
8.78 µin/in-°F @Temperature 32.0 - 1290 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, 15.9 mm thick bar Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 0.000 - 700 °C |
8.78 µin/in-°F @Temperature 32.0 - 1290 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 7.9 mm thick plate, aged 3 hours at 816°C Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 25.0 - 700 °C |
8.78 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 25.0 - 700 °C |
8.78 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 25.0 - 700 °C |
8.78 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 188 alloy, plate at RT after 0 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 25.0 - 700 °C |
8.78 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 188 alloy, plate at RT after 16000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 25.0 - 700 °C |
8.78 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 214® alloy, 10% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 25.0 - 700 °C |
8.78 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 214® alloy, 40% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 25.0 - 700 °C |
8.78 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 214® alloy, sheet, 1000 hours exposure at 980°C (1800°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 25.0 - 700 °C |
8.78 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 214® alloy, sheet, 32 hours exposure at 980°C (1800°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 25.0 - 400 °C |
8.78 µin/in-°F @Temperature 77.0 - 752 °F |
|
| Haynes HR-120® alloy, solution heat-treated aged at 1400°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 0.000 - 1000 °C |
8.78 µin/in-°F @Temperature 32.0 - 1830 °F |
|
| Kennametal Stellite Stellite® 12 Satisfactory finishing results can be obtained using carbide tipped tools. Applications include cutting plastics, rubber, paper, carpet, and wood; saw teeth, trimmer knives, carpet knives, ledger bl.. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 25.0 - 800 °C |
8.78 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 25 alloy, cold rolled and 1205°C (2200°F) solution annealed sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 25.0 - 800 °C |
8.78 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 25 alloy, cold worked sheet, 15 % cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 25.0 - 800 °C |
8.78 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 25 alloy, room temperature after 25% cold reduction, 1175°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 25.0 - 800 °C |
8.78 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 25 alloy, room temperature sheet after 100 hours of 760°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 25.0 - 800 °C |
8.78 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 25 alloy, room temperature sheet after 500 hours of 650°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 25.0 - 800 °C |
8.78 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 25 alloy, sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 24.0 - 871 °C |
8.78 µin/in-°F @Temperature 75.2 - 1600 °F |
|
| Haynes Hastelloy® C-22® alloy, 40% cold worked sheet, aged 100 hours at 500°C HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 24.0 - 871 °C |
8.78 µin/in-°F @Temperature 75.2 - 1600 °F |
|
| Haynes Hastelloy® C-22® alloy, 50% cold worked sheet HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 24.0 - 871 °C |
8.78 µin/in-°F @Temperature 75.2 - 1600 °F |
|
| Haynes Hastelloy® C-22® alloy, all-weld metal, GMAW short arc HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 20.0 - 315 °C |
8.78 µin/in-°F @Temperature 68.0 - 599 °F |
|
| ATI Allegheny Ludlum AL 400™ Nickel-Base Alloy, Heavily Cold Rolled Sheet and Strip, UNS N04400 Moderately to faintly magnetic at room temperature. Allegheny Ludlum AL 400 alloy is a ductile nickel-copper alloy with resistance to a variety of corrosive conditions. The alloy is most frequentl.. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 24.0 - 871 °C |
8.78 µin/in-°F @Temperature 75.2 - 1600 °F |
|
| Haynes Hastelloy® C-22® alloy, transverse, GTAW short arc weldment, plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 24.0 - 871 °C |
8.78 µin/in-°F @Temperature 75.2 - 1600 °F |
|
| Haynes Hastelloy® C-22® alloy, transverse, SMAW weldment, 19.1 mm thick plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 21.0 - 982 °C |
8.78 µin/in-°F @Temperature 69.8 - 1800 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 593°C (1100°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 24.0 - 871 °C |
8.78 µin/in-°F @Temperature 75.2 - 1600 °F |
|
| Haynes Hastelloy® C-22® alloy, 0% cold worked sheet, aged 100 hours at 500°C HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 24.0 - 871 °C |
8.78 µin/in-°F @Temperature 75.2 - 1600 °F |
|
| Haynes Hastelloy® C-22® alloy, all-weld metal, GTAW HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 21.0 - 982 °C |
8.78 µin/in-°F @Temperature 69.8 - 1800 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 649°C (1200°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
| CTE, linear | 15.8 µm/m-°C @Temperature 0.000 - 700 °C |
8.78 µin/in-°F @Temperature 32.0 - 1290 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 11.1 mm thick plate, aged 3 hours at 816°C Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||