Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 16.0 µm/m-°C @Temperature 100 °C |
8.89 µin/in-°F @Temperature 212 °F |
|
Outokumpu 4436 Cr-Ni-Mo Austenitic Stainless Steel General purpose steel with excellent corrosion resistance, particularly in the presence of halides.Applications: FiltersBraiding for hydraulic hosesShaftsFastenersMarine componentsAvailable in hot r.. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 100 °C |
8.89 µin/in-°F @Temperature 212 °F |
|
Outokumpu 4439 Austenitic Stainless Steel Applications: Wet corrosion resistance and general service.Available in hot rolled plate (Quarto), hot rolled strip/sheet (CPP), and cold rolled strip/sheet forms. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature -50.0 - 50.0 °C |
8.89 µin/in-°F @Temperature -58.0 - 122 °F |
Axial; ASTM E831 |
Solvay Specialty Polymers Ryton® R-4-220BL Polyphenylene Sulfide Compound
(Unverified Data**) Black Polyphenylene Sulfide CompoundRyton® R-4-220BL is an advanced 40% fiberglass reinforced polyphenylene sulfide compound formulated for enhanced hydrolytic stability in applications requiring .. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 30.0 - 649 °C |
8.89 µin/in-°F @Temperature 86.0 - 1200 °F |
|
Haynes Hastelloy® G-30® alloy, all-weld metal, GTAW weld 3.2 mm diameter filler wire HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 23.0 - 500 °C |
8.89 µin/in-°F @Temperature 73.4 - 932 °F |
|
Haynes Multimet® alloy, 1.32 mm thick sheet, 1177°C heat treatment, rapid air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 23.0 - 500 °C |
8.89 µin/in-°F @Temperature 73.4 - 932 °F |
|
Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 15% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 23.0 - 500 °C |
8.89 µin/in-°F @Temperature 73.4 - 932 °F |
|
Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 30% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 25.0 - 800 °C |
8.89 µin/in-°F @Temperature 77.0 - 1470 °F |
|
Haynes 625 alloy, 30% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 25.0 - 800 °C |
8.89 µin/in-°F @Temperature 77.0 - 1470 °F |
|
Haynes 625 alloy, 30% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 25.0 - 800 °C |
8.89 µin/in-°F @Temperature 77.0 - 1470 °F |
|
Haynes 625 alloy, 50% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 25.0 - 800 °C |
8.89 µin/in-°F @Temperature 77.0 - 1470 °F |
|
Haynes 625 alloy, plate after 16000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 25.0 - 800 °C |
8.89 µin/in-°F @Temperature 77.0 - 1470 °F |
|
Haynes 625 alloy, plate after 4000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 30.0 - 649 °C |
8.89 µin/in-°F @Temperature 86.0 - 1200 °F |
|
Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate, GMAW spray weld 1.1 mm diameter filler wire HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 30.0 - 649 °C |
8.89 µin/in-°F @Temperature 86.0 - 1200 °F |
|
Haynes Hastelloy® G-30® alloy, 25.4 mm thick bar HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 30.0 - 649 °C |
8.89 µin/in-°F @Temperature 86.0 - 1200 °F |
|
Haynes Hastelloy® G-30® alloy, 30% cold rolled HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 30.0 - 649 °C |
8.89 µin/in-°F @Temperature 86.0 - 1200 °F |
|
Haynes Hastelloy® G-30® alloy, 6.4 mm thick plate HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 30.0 - 760 °C |
8.89 µin/in-°F @Temperature 86.0 - 1400 °F |
|
Haynes Hastelloy® G-30® alloy, plate and bar HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 23.0 - 500 °C |
8.89 µin/in-°F @Temperature 73.4 - 932 °F |
|
Haynes Multimet® alloy, SMAW, 3.2 mm sheet Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 20.0 - 300 °C |
8.89 µin/in-°F @Temperature 68.0 - 572 °F |
|
Schott P-PK53 Glass Suitable for precision moldingInformation Provided by SCHOTT North America, Inc. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 20.0 - 50.0 °C |
8.89 µin/in-°F @Temperature 68.0 - 122 °F |
TD |
DuPont Teijin Films Melinex® 377 Polyester Film, 75 Gauge Melinex® 377 is a translucent matte film having a medium surface gloss which is suitable for creating woodgrain and muted metallic effects.Typical Applications: Melinex® is suitable for use in sta.. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 0.000 - 300 °C |
8.89 µin/in-°F @Temperature 32.0 - 572 °F |
|
CLAL-MSX ARCAP Anticorrosion AP1C 0 Annealed, Drawn Copper Alloy Description: The AP1C grade (used in rods for parts that are to be deformed by torsion, bending, riveting, swaging... and for welding) and the AP1 grade (sheet, strip, wire, tubes) is machineable un.. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 0.000 - 300 °C |
8.89 µin/in-°F @Temperature 32.0 - 572 °F |
|
CLAL-MSX ARCAP Anticorrosion AP1C H12 1/2 hard, Rolled Copper Alloy Description: The AP1C grade (used in rods for parts that are to be deformed by torsion, bending, riveting, swaging... and for welding) and the AP1 grade (sheet, strip, wire, tubes) is machineable un.. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 0.000 - 300 °C |
8.89 µin/in-°F @Temperature 32.0 - 572 °F |
|
CLAL-MSX ARCAP Anticorrosion AP1C 0 Annealed, Rolled Copper Alloy Description: The AP1C grade (used in rods for parts that are to be deformed by torsion, bending, riveting, swaging... and for welding) and the AP1 grade (sheet, strip, wire, tubes) is machineable un.. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 0.000 - 300 °C |
8.89 µin/in-°F @Temperature 32.0 - 572 °F |
|
CLAL-MSX ARCAP Anticorrosion AP4 H12 1/2 hard, Drawn Copper Alloy Description: The AP4 grade is less easy to turn than the other grades of ARCAP. It can however be machined without more difficulty than the nickel chromium molybdenum steels.High Corrosion Resistanc.. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 20.0 - 250 °C |
8.89 µin/in-°F @Temperature 68.0 - 482 °F |
|
ATI Allegheny Ludlum Type 332 Stainless Steel, UNS N08800 Type 332 is a nickel and chromium austenitic stainless steel designed to resist oxidation and carburization at elevated temperatures. The nickel content, 32%, makes the alloy highly resistant both .. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 23.0 - 500 °C |
8.89 µin/in-°F @Temperature 73.4 - 932 °F |
|
Haynes Multimet® alloy, 12.7-50.8 mm hot-rolled bar, 1185°C heat treatment, water quenched Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 23.0 - 500 °C |
8.89 µin/in-°F @Temperature 73.4 - 932 °F |
|
Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 10% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |