- Polymer Property : CTE, linear = 9.11 µin/in-°F
Polymer Property : CTE, linear = 9.11 µin/in-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 16.4 µm/m-°C @Temperature 21.0 - 100 °C |
9.11 µin/in-°F @Temperature 69.8 - 212 °F |
Mean |
| Pyramid Stainless Steel AISI 304/316L, STAINLESS STEEL SHEET NO.4 FINISH Information provided by Pyramid Stainless Steel Ind Co Ltd |
|||
| CTE, linear | 16.4 - 17.4 µm/m-°C @Temperature 20.0 - 100 °C |
9.11 - 9.67 µin/in-°F @Temperature 68.0 - 212 °F |
|
| PEAK Werkstoff DISPAL S250 Aluminum Alloy, AlSi20Fe5Ni2, Condition F Excellent properties:abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allow the manufacturing of pistons for highest operational.. |
|||
| CTE, linear | 16.4 µm/m-°C @Temperature 25.0 - 600 °C |
9.11 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes HR-120® alloy, solution heat-treated Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
| CTE, linear | 16.4 µm/m-°C @Temperature 25.0 - 600 °C |
9.11 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes HR-120® alloy, solution heat-treated aged at 1200°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
| CTE, linear | 16.4 µm/m-°C @Temperature 26.0 - 871 °C |
9.11 µin/in-°F @Temperature 78.8 - 1600 °F |
|
| Haynes Ultimet® alloy, 12.7 mm (1/2 in.) thick plate, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 16.4 µm/m-°C @Temperature 26.0 - 871 °C |
9.11 µin/in-°F @Temperature 78.8 - 1600 °F |
|
| Haynes Ultimet® alloy, 19.1 mm thick plate, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 16.4 µm/m-°C @Temperature 26.0 - 871 °C |
9.11 µin/in-°F @Temperature 78.8 - 1600 °F |
|
| Haynes Ultimet® alloy, aged 1000 hours at 204°C (400°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 16.4 µm/m-°C @Temperature 26.0 - 871 °C |
9.11 µin/in-°F @Temperature 78.8 - 1600 °F |
|
| Haynes Ultimet® alloy, aged 1000 hours at 427°C (800°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 16.4 µm/m-°C @Temperature 26.0 - 871 °C |
9.11 µin/in-°F @Temperature 78.8 - 1600 °F |
|
| Haynes Ultimet® alloy, mill annealed Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 16.4 µm/m-°C @Temperature 26.0 - 871 °C |
9.11 µin/in-°F @Temperature 78.8 - 1600 °F |
|
| Haynes Ultimet® alloy, plate, GMAW weld (short) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 16.4 µm/m-°C @Temperature 25.0 - 700 °C |
9.11 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 556® alloy, 0% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.4 µm/m-°C @Temperature 25.0 - 700 °C |
9.11 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 556® alloy, 10% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.4 µm/m-°C @Temperature 25.0 - 700 °C |
9.11 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 556® alloy, 10% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.4 µm/m-°C @Temperature 25.0 - 700 °C |
9.11 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 556® alloy, 10% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.4 µm/m-°C @Temperature 25.0 - 700 °C |
9.11 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 556® alloy, 40% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.4 µm/m-°C @Temperature 25.0 - 700 °C |
9.11 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 556® alloy, bar, after 1000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.4 µm/m-°C @Temperature 25.0 - 700 °C |
9.11 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 556® alloy, bar, after 8000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.4 µm/m-°C @Temperature 25.0 - 700 °C |
9.11 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 556® alloy, bar, after 8000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.4 µm/m-°C @Temperature 25.0 - 700 °C |
9.11 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 556® alloy, sheet after 1000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.4 µm/m-°C @Temperature 25.0 - 600 °C |
9.11 µin/in-°F @Temperature 77.0 - 1110 °F |
|
| Haynes HR-120® alloy, solution heat-treated plate Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
| CTE, linear | 16.4 µm/m-°C @Temperature 0.000 - 250 °C |
9.11 µin/in-°F @Temperature 32.0 - 482 °F |
|
| CLAL-MSX CUPROROR® TL2 1/2 hard, Copper Alloy Alloy especially suited to applications in electronics and electro technology. This doped copper, displays high electrical and thermal conductivity, good mechanical properties and excellent temperat.. |
|||
| CTE, linear | 16.4 µm/m-°C @Temperature 20.0 - 538 °C |
9.11 µin/in-°F @Temperature 68.0 - 1000 °F |
|
| ATI Allegheny Ludlum AL 400™ Nickel-Base Alloy, Heavily Cold Rolled Sheet and Strip, UNS N04400 Moderately to faintly magnetic at room temperature. Allegheny Ludlum AL 400 alloy is a ductile nickel-copper alloy with resistance to a variety of corrosive conditions. The alloy is most frequentl.. |
|||
| CTE, linear | 16.4 µm/m-°C @Temperature 20.0 - 600 °C |
9.11 µin/in-°F @Temperature 68.0 - 1110 °F |
|
| ATI Allegheny Ludlum Stainless Steel AL-6XN® Alloy (UNS N08367), 20% Cold Work The AL-6XN® alloy is a superaustenitic stainless steel which was developed by Allegheny Ludlum Corporation. It exhibits far greater resistance to chloride pitting, crevice corrosion and stress-co.. |
|||
| CTE, linear | 16.4 µm/m-°C @Temperature 20.0 - 600 °C |
9.11 µin/in-°F @Temperature 68.0 - 1110 °F |
|
| ATI Allegheny Ludlum Stainless Steel AL-6XN® Alloy (UNS N08367), 50% Cold Work The AL-6XN® alloy is a superaustenitic stainless steel which was developed by Allegheny Ludlum Corporation. It exhibits far greater resistance to chloride pitting, crevice corrosion and stress-co.. |
|||
| CTE, linear | 16.4 µm/m-°C @Temperature 20.0 - 600 °C |
9.11 µin/in-°F @Temperature 68.0 - 1110 °F |
|
| ATI Allegheny Ludlum Stainless Steel AL-6XN® Alloy (UNS N08367), 75% Cold Work The AL-6XN® alloy is a superaustenitic stainless steel which was developed by Allegheny Ludlum Corporation. It exhibits far greater resistance to chloride pitting, crevice corrosion and stress-co.. |
|||
| CTE, linear | 16.4 µm/m-°C @Temperature 25.0 - 700 °C |
9.11 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 556® alloy, 20% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.4 µm/m-°C @Temperature 25.0 - 700 °C |
9.11 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 556® alloy, 40% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.4 µm/m-°C @Temperature 25.0 - 700 °C |
9.11 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 556® alloy, 50% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.4 µm/m-°C @Temperature 25.0 - 700 °C |
9.11 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 556® alloy, bar after 16000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.4 µm/m-°C @Temperature 25.0 - 700 °C |
9.11 µin/in-°F @Temperature 77.0 - 1290 °F |
|
| Haynes 556® alloy, bar, after 4000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||