Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 109 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	43.0 °C	109 °F	ASTM D648
DuPont™ Surlyn® 9720 Ionomer Resin, Zinc Surlyn® 9720 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with zinc ions. The amount of MAA and neutr..
Deflection Temperature at 0.46 MPa (66 psi)	43.0 °C	109 °F	ASTM D648
DuPont™ Surlyn® 9721 Ionomer Resin, Zinc Surlyn® 9721 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with zinc ions. The amount of MAA and neutr..
Deflection Temperature at 0.46 MPa (66 psi)	42.8 °C	109 °F	Molded and tested in accordance with ASTM D4976; ASTM D648
Dow DNDA-7144 NT 7 Linear Low Density Polyethylene Resin DOW DNDA-7144 NT 7 is produced using UNIPOL™ PE process technology. It is intended for use in injection molding applications such as large industrial containers and trash cans. Information provide..
Deflection Temperature at 0.46 MPa (66 psi)	42.8 °C	109 °F	Molded and tested in accordance with ASTM D4976; ASTM D648
Dow DNDA-8320 NT 7 Linear Low Density Polyethylene Resin DOW DNDA-8320 NT 7 is produced using UNIPOL™ PE process technology. It is intended for use in general purpose injection molding applications. Information provided by Dow
Deflection Temperature at 0.46 MPa (66 psi)	42.8 °C	109 °F	Molded and tested in accordance with ASTM D4976; ASTM D648
Dow GRSN-9820 NT 7 Linear Low Density Polyethylene Granular Solid DOW GRSN-9820 NT 7 is produced using UNIPOL™ PE process technology and is supplied in granular form. This resin is specifically designed as a carrier resin for color concentrates and other master ..
Deflection Temperature at 0.46 MPa (66 psi)	42.8 °C	109 °F	ASTM D648
Aclo Accucomp Polyethylene LD0102L Low Density
Deflection Temperature at 0.46 MPa (66 psi)	43.0 °C	109 °F
Arkema Group Pebax® MX 1059 Polyether Block Amide (PEBA) (Conditioned) POLYETHER BLOCK AMIDE (PEBA) Hardness 35 shore D Good resistance to oils. Applications: Automotive, cable...ISO data provided by the manufacturer, Arkema.
Deflection Temperature at 0.46 MPa (66 psi)	43.0 °C	109 °F	ASTM D648
Buckeye Polymers BP RPP 3012 C Polypropylene, 30% Mineral Filled Applications:Outdoor FurnitureCalcium carbonate-filled PP grades have a high impact toughness, moderate increased stiffness, and excel in high gloss applications. This material can be customized thr..
Deflection Temperature at 0.46 MPa (66 psi)	43.0 °C	109 °F	ASTM D648-06
Proto3000 Objet VeroWhite FullCure830 Rapid Prototyping Polymer Objet’s FullCure® Materials family of proprietary acrylic-based photopolymer materials enables Objet users to create highly accurate, finely detailed 3D models and parts for a wide range of Rapid ..
Deflection Temperature at 0.46 MPa (66 psi)	43.0 - 159 °C	109 - 318 °F	Average value: 101 °C Grade Count:48
Overview of materials for Polypropylene with 30% Calcium Carbonate (CaCO3) Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 30% Calcium Carbonate (CaCO3) Filler". Each property range of values reported is mini..