Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 124 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 51.0 - 199 °C
124 - 390 °F
Average value: 146 °C Grade Count:9
Overview of materials for Thermoplastic Polyurethane, Elastomer, Glass Filled
This property data is a summary of similar materials in the MatWeb database for the category "Thermoplastic Polyurethane, Elastomer, Glass Filled". Each property range of values reported is minimum ..
Deflection Temperature at 0.46 MPa (66 psi) 51.0 °C
124 °F
ISO 75/Method Bf
Premix Thermoplastics PRE-ELEC® PE 1313  (discontinued **)
PRE-ELEC PE 1313 is a conductive thermoplastic compound based on PE-LLD. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC PE 13..
Deflection Temperature at 0.46 MPa (66 psi) 51.2 °C
124 °F
ASTM D648-98c
DSM Somos® WaterClear® 10110 Epoxy Resin for Stereolithography  (discontinued **)
DescriptionDSM Somos® 10110 is a high-speed liquid photopolymer that produces strong, rigid, and durable parts with optical clarity using stereolithography machines. This material is especially us..
Deflection Temperature at 0.46 MPa (66 psi) 51.0 °C

@Thickness 3.20 mm
124 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP LUBRICOMP TX97446 PU
LNP* LUBRICOMP* TX97446 is a compound based on Polyurethane containing Proprietary Fillers. Added feature of this material is: Wear Resistant.
Deflection Temperature at 0.46 MPa (66 psi) 51.0 °C
124 °F
ASTM D648
A. Schulman POLYFORT™ PP 3702 Clarified Copolymer Polypropylene
DescriptionPolyfort® PP 3702 is a clarified copolymer polypropylene.Information provided by A. Schulman.
Deflection Temperature at 0.46 MPa (66 psi) 51.0 °C
124 °F
ASTM D648
A. Schulman POLYFORT™ PP 3702 Clarified Copolymer Polypropylene
DescriptionPolyfort® PP 3702 is a clarified copolymer polypropylene.Information provided by A. Schulman.
Deflection Temperature at 0.46 MPa (66 psi) 51.0 °C
124 °F
ASTM D648
A. Schulman POLYFORT™ PP 3702 Clarified Copolymer Polypropylene
DescriptionPolyfort® PP 3702 is a clarified copolymer polypropylene.Information provided by A. Schulman.
Deflection Temperature at 0.46 MPa (66 psi) 51.0 °C
124 °F
ASTM D648
A. Schulman POLYFORT™ PP 3702 Clarified Copolymer Polypropylene
DescriptionPolyfort® PP 3702 is a clarified copolymer polypropylene.Information provided by A. Schulman.
Deflection Temperature at 0.46 MPa (66 psi) 51.0 °C
124 °F
ASTM D648
Lubrizol ESTALOC® 59010 Polyester-Type, Reinforced Engineering Thermoplastic Polyurethane
Features: Fast Cycling, Dimensional Stability, Durability, Aesthetics, Low Temperature ImpactUses: Injection MoldingAvailability: Americas and AsiaInformation provided by Lubrizol
Deflection Temperature at 0.46 MPa (66 psi) 51.0 °C
124 °F
ASTM D648
Lubrizol Estaloc® 59020 Reinforced Thermoplastic Polyurethane
Type: Estaloc® 59020 RETPU is a polyester-type reinforced engineered thermoplastic polyurethane (RETPU).Features: Fast cycling, dimensional stability, durability, aesthetics, low temperature impact..
Deflection Temperature at 0.46 MPa (66 psi) 51.0 °C
124 °F
ASTM D648
Chevron Phillips Marlex® 7104 LLDPE Sheet Extrusion
Resin Type: Hexene CopolymerCharacteristics: Outstanding ESCRGood melt strengthExcellent flexibilityGood processabilityGood glossHigh COFApplications: Landfill coversFlat and round-die productsCoext..
Deflection Temperature at 0.46 MPa (66 psi) 51.0 °C
124 °F
Method A; ASTM D648
Chevron Phillips Marlex® K203 LLDPE Sheet Extrusion
Resin Type: Hexene CopolymerCharacteristics: Outstanding ESCRBroad fusion rangeExcellent melt strengthGood processabilityExcellent flexibilityImproved output and texturingApplications: Coextruded ca..
Deflection Temperature at 0.46 MPa (66 psi) 51.1 °C
124 °F
Molded and tested in accordance with ASTM D4976; ASTM D648
Dow DNDA-1081 NT 7 Linear Low Density Polyethylene Resin
DOW DNDA-1081 NT 7 is produced using UNIPOL™ PE process technology. It is intended for high-speed injection molding of thin walled parts such as downguaged lids. Information provided by Dow
Deflection Temperature at 0.46 MPa (66 psi) 51.1 °C
124 °F
ASTM D648
Aclo Accutech Polypropylene Copolymer CP0436C10L1 Calcium Reinforced
Deflection Temperature at 0.46 MPa (66 psi) 51.0 °C
124 °F
ASTM-D648
Braskem Symbios 3102 Polypropylene Terpolymer
Braskem Symbios 3102 is a medium melt flow rate terpolymer with a heat seal temperature below 110ºC on its non-treated face. It is designed for use as a heat sealing layer for cast film coextrusion..
Deflection Temperature at 0.46 MPa (66 psi) 51.0 - 54.0 °C
124 - 129 °F
ASTM D648
3D Systems Accura® 40 Plastic for SLA® Systems
40 Accura "Nd" type material - for use with Viper SLA, and SLA 3500, 5000 and 7000 systems.ApplicationsHigh temperature testing:Automotive "under-the-hood" partsIntake manifoldsLighting components a..
Deflection Temperature at 0.46 MPa (66 psi) 51.0 °C
124 °F
ASTM D648
Ashley Polymers Ashlene® 847 Nylon 6, Film Grade
A very high impact, low flexural modulus Nylon 6 resin for molding or extrusion. Outstanding low temperature properties.Data provided by the manufacturer
Deflection Temperature at 0.46 MPa (66 psi) 51.0 - 170 °C
124 - 338 °F
Average value: 119 °C Grade Count:13
Overview of materials for Thermoplastic Polyurethane (TPUR), Polyester Grade
This property data is a summary of similar materials in the MatWeb database for the category "Thermoplastic Polyurethane (TPUR), Polyester Grade". Each property range of values reported is minimum a..
Deflection Temperature at 0.46 MPa (66 psi) 51.1 - 135 °C
124 - 275 °F
Average value: 91.2 °C Grade Count:32
Overview of materials for Polypropylene with 10% Calcium Carbonate (CaCO3) Filler
This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 10% Calcium Carbonate (CaCO3) Filler". Specific grades with primary filler content be..