- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 156 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 156 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 156 °C | 312 °F | ASTM D648 |
| RheTech Products F37-01 40% Glass Fiber/Mineral Co-Reinforced Polypropylene, Chemically Coupled, Black Applications: ElectronicsBracketsBattery traysInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 156 °C | 312 °F | ASTM D648 |
| RheTech Products F40-01 40% Glass Fiber/Mineral Co-Reinforced Polypropylene, Chemically Coupled, Black Applications: Battery traysAir cleaner housingFunctional support decksInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 156 °C | 312 °F | ASTM D648 |
| RheTech Products FRG220-773UB 20% Glass Fiber Reinforced Polypropylene Copolymer, Chemically Coupled, Flame Retardant, UV Stabilized, Light Grey Applications: Electrical housingsStructural componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 156 °C @Thickness 3.18 mm |
313 °F @Thickness 0.125 in |
Annealed; ASTM D648 |
| PolyOne Maxxam™ PPC-40G Black Polypropylene Copolymer (PP Copolymer) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 156 °C | 313 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PPH BF4075 VT1 Polypropylene Homopolymer, Reinforced, Heat Resistant Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 156 °C | 313 °F | ISO 75-1/-2 |
| Lanxess Durethan® DP 1802 H3.0 000000 Nylon 6 PA 6 injection and extrusion molding grade, non-reinforced, impact-modified, UL 94V-2 off 0,75 mm, GWIT: 775°C off 0,75 mm, halogen-free |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 156 °C | 313 °F | ISO 75-1/-2 |
| Lanxess Pocan® KU 1-7625 901510 PBT + PC, 20% Glass Fiber PBT+PC, 20% glass fibers, injection molding, low tendency to warp, improved surface finish |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 156 °C @Thickness 3.20 mm |
313 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP LL003 PEEK LNP* LUBRICOMP* LL003 is a compond based on Polyetheretherketone resin containing 15% PTFE Lubricant. Added feature of this material is: Wear Resistant. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 156 °C | 313 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP LUBRICOMP RX01514 PA 66 LNP* LUBRICOMP* RX01514 is a compound based on Nylon 66 resin containing Proprietary Filler(s). Added feature of this material is: Wear Resistant. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 156 °C @Thickness 3.20 mm |
313 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP KZ001L Acetal Copoly LNP* THERMOCOMP* KZ001L is a compound based on Acetal Copolymer resin containing 5% Milled Glass. Added features of this material include: Low Extractible. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 156 °C | 313 °F | ASTM D648 |
| SK Chemicals SKYPEL G182D General Grade SKYPEL is a thermoplastic polyester elastomer (TPEE). It is a polymer resin having the property somewhere between plastics and rubber, which have various properties ranging from high hardness plasti.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 156 °C @Thickness 3.20 mm |
313 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Noryl GTX GTX9200 PPE+PS+PA66 High Flow GTX for Automotive applicationsThis data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 156 °C | 313 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics Noryl GTX GTX9200 PPE+PS+PA66 (Asia Pacific) High Flow GTX for Automotive applicationsThis data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 156 °C @Thickness 3.20 mm |
313 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Noryl GTX GTX9200 PPE+PS+PA66 (Asia Pacific) High Flow GTX for Automotive applicationsThis data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 156 °C | 313 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics Noryl GTX GTX9200 PPE+PS+PA66 (Europe-Africa-Middle East) High Flow GTX for Automotive applicationsThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 156 °C @Thickness 3.20 mm |
313 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Noryl GTX GTX9200 PPE+PS+PA66 (Europe-Africa-Middle East) High Flow GTX for Automotive applicationsThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 156 °C | 313 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics NORYL N300X PPE+PS PPE+PS blend. Unfilled. Non-brominated, non-chlorinated FR system. UL94 V0. High heat. Dielectric strength. Dimensional stability. Suitable for E/E applications. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 156 °C | 313 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics NORYL N300X PPE+PS (Asia Pacific) PPE+PS blend. Unfilled. Non-brominated, non-chlorinated FR system. UL94 V0. High heat. Dielectric strength. Dimensional stability. Suitable for E/E applications. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 156 °C @Thickness 3.20 mm |
313 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Lubricomp LL003E PEEK LNP* Lubricomp* LL003E is a compound based on Polyetheretherketone (PEEK) containing PTFE. Characteristics of this grade are: Easy Molding and Internally Lubricated.This data was supplied by SABIC.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 156 °C | 313 °F | |
| Arkema Group Rilsan® BECN W3 TL Nylon 11, Sheathing Grade (Conditioned) Designation ISO 1874-PA11,KFHL,12-010Rigid grade for sheathing wires and cables. Available color: natural. Light and heat stabilized. Flame retardant agent.Fire-resistant. High abrasion resistance. .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 156 °C | 313 °F | ASTM D648 |
| Aclo Accutech Polypropylene Homopolymer HP0339G30CL Glass Reinforced Coupled |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 156 °C | 313 °F | ISO 75 |
| BASF Ultraform H 2320 006 Q600 POM Ultraform H2320 006 is a high-molecular-weight grade of POM for injection molding. It conforms to FDA requirements of 21 CFR 177.2470. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 156 °C | 313 °F | ISO 75 -1 & -2 flat |
| Asahi Kasei Tenac®-C 3510 Copolymer Acetal Resin High-impact, high elongation grade, with increased molecular weightInformation provided by Asahi Kasei Corporation. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 156 °C | 313 °F | ASTM D648 |
| Aaron Industries AAROPRENE® GFIPP 2020 High Impact Glass Filled Polypropylene AAROPRENE® GFIPP 2000 Series Reinforced CompoundsMelt flow index may be specified. Color may be specified. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 156 °C | 313 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics NORYL FR9310 PPE (Europe-Africa-Middle East) Noryl*FR9310 is a polyphenylene ether resin concentrate with nonhalogenated Flame retardant with Vicat of 165 deg C. Intended for use as an additive or a building block in a variety of thermoplasti.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 156 °C | 313 °F | ASTM D648 |
| LyondellBasell Higlass PF062-2 Polypropylene Homopolymer, 20% Glass Fiber Key Features: high melt flow, medium high modulus, chemically coupled, glass fiber-reinforced polypropylene homopolymer, high rigidity, high strength, excellent processabilityApplications: appliance.. |
|||