- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 255 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 255 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C @Thickness 3.20 mm |
255 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Cycoloy® CE8510 PC+ABS (Asia Pacific) Extrusion grade PC/ABS. Low viscosity, high impact and ductility.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PP CPQ10015 FF Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | ASTM D648 |
| Polymer Resources PC-IM2-UV Polycarbonate, Impact Modified, Medium Flow, UV-stabilized Polycarbonate, Impact Modified, Medium Flow, UV-stabilizedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Inform.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | ASTM D648 |
| Polymer Resources PC-IM3 Polycarbonate, Impact Modified, High Flow Polycarbonate, Impact Modified, High FlowProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | ASTM D648 |
| Polymer Resources PC-IM4 Polycarbonate, Impact Modified, Easy Flow Polycarbonate, Impact Modified, Easy FlowProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C @Thickness 3.20 mm |
255 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® HFD1930 PC Copolymer 55 MFR LEXAN High Flow Ductile Copolymer, Natural color only |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | ASTM D648 |
| RheTech Products M25P100-01 25% Mica Reinforced Polypropylene, Black Applications: Underhood applicationsInternal I/P ComponentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C @Thickness 3.20 mm |
255 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Lexan® EXRL0683 PC Copolymer 11 MFR LEXAN High Flow Ductile CopolymerThis data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 - 138 °C | 255 - 280 °F | Average value: 130 °C Grade Count:5 |
| Overview of materials for Polycarbonate/Styrenic Alloy This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate/Styrenic Alloy". Each property range of values reported is minimum and maximum values of a.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C @Thickness 6.40 mm |
255 °F @Thickness 0.252 in |
ASTM D648 |
| Kingfa MAC-601 DY Modified 60/40 PC/ABS Alloy Features:Excellent balance propertiesHigh impact strengthGood electro-plating propertiesGood processing propertiesApplications:Injection moldingAutomobile instrument panelPower toolComputer and acce.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | ASTM D648 |
| Global TPP-130 30% Talc Filled Polypropylene Information provided by Global Polymers Corporation. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics XYLEX X7503 PC+POLYESTER PC-Siloxane copolymer + Polyester alloy, High Impact, Transparent |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics XYLEX X7503 PC+POLYESTER (Europe-Africa-Middle East) PC-Siloxane copolymer + Polyester alloy, High Impact, Transparent |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | Unannealed; ASTM D648 |
| Styron PULSEâ„¢ 2300 PT PC/ABS Engineering Resin Information provided by Styron |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C @Thickness 3.20 mm |
255 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL BN9003G PPE+HIPS PPE+PS blend. Unfilled. Blow molding. Excellent balance of impact and surface aesthetics. Suitable for automotive exterior components including spoilers. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1200X High Flow, Calcium Carbonate Fortified Homopolymer Polypropylene DescriptionPolyfort® FPP 1200X is a high flow 40% calcium carbonate fortified homopolymer polypropylene.Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1285H Glass Reinforced Copolymer Polypropylene DescriptionPolyfort® FPP 1285H is a 20% glass reinforced copolymer polypropylene compound. It has good impact and heat resistance. Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1285H Glass Reinforced Copolymer Polypropylene DescriptionPolyfort® FPP 1285H is a 20% glass reinforced copolymer polypropylene compound. It has good impact and heat resistance. Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | ISO 75-1,-2 |
| Covestro Bayblend® T65 AT PC/ABS Blend Main characteristics:• High toughness even at low temperatures• High dimensional accuracy and stability• Good paintability• Good flowabilityGrade characteristics:• Injection molding• Imp.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | ASTM D648 |
| Aclo Accutech Polypropylene HP0335T40V Homopolymer Talc Reinforced Approved to ESF-M4D355B White B12391 |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | ASTM D648 |
| Adell RQ-14 Copolymer Polypropylene, 20% Mica Reinforced Data provided by Adell Plastics, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | ASTM Test |
| BASF Ultramid® 8254 HS BK-102 PA6 (Dry) Ultramid 8254 HS is a highly flexible, heat stabilized, impact modified nylon 6 extrusion grade for tubing applications. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | ASTM D648 |
| Aaron Industries AAROPRENE® TFPP 2020 Talc Filled Polypropylene AAROPRENE® TFPP 2000 Series Talc Reinforced CompoundsMelt flow index may be specified. Color may be specified. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | ASTM D648 |
| Asahi Kasei Thermofil P6-30MI-0533 30% Mica Reinforced, Flame Retardant, Heat Stabilized Information provided by Asahi Thermofil |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | ASTM D648 |
| Ashley Polymers Ashlene® 1105 Polycarbonate, 5-7% Glass Reinforced A general purpose foamable injection molding grade resin with 5-7% glass reinforcement.Data provided by the manufacturer |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | ISO 75 |
| Teijin Multilon T-2711 Standard, Automobile Part Series PC/ABS Polymer Alloy PC/ABS polymer alloy general grade developed for automobile parts use. It has high heat resistance, impact strength, light resistance and fluidity, particularly, the high impact strength in a wide r.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | Unannealed; ASTM D648 |
| Multibase Multi-Flam™ 0102 Natural PP Polypropylene Features:Flame Retardant Forms:PelletsProcessing Methods:Injection MoldingInformation provided by Multibase |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1200H High Flow, Calcium Carbonate Fortified Homopolymer Polypropylene DescriptionPolyfort® FPP 1200H is a high flow 40% calcium carbonate fortified homopolymer polypropylene.Information provided by A. Schulman. |
|||