Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 379 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 193 °C

@Thickness 6.35 mm
379 °F

@Thickness 0.250 in
Unannealed; ASTM D648
PolyOne Therma-Tech™ NJ-6000 TC Polyamide 12 (Nylon 12)
Therma-Tech™ Thermal Management Compounds have been engineered to combine the heat transfer and cooling capabilities of metals with the design freedom, weight reduction and cost advantages of therm..
Deflection Temperature at 0.46 MPa (66 psi) 193 °C
379 °F
DIN 53461
Qualchem Danamid FCF-20 Polyamide 6, 20% Carbon Fiber
Reinforced with carbon fiber, antistatic and conductive.Information provided by Qualchem Zrt.
Deflection Temperature at 0.46 MPa (66 psi) 193 °C
379 °F
ASTM D648
Polymer Resources TP-IM-G7.5 Polybutylene Terephthalate, 7.5% Glass Reinforced, Impact Modified
Polybutylene Terephthalate, 7.5% Glass Reinforced, Impact ModifiedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test sample..
Deflection Temperature at 0.46 MPa (66 psi) 193 °C

@Thickness 6.35 mm
379 °F

@Thickness 0.250 in
Unannealed; ASTM D648
PolyOne Therma-Tech™ NJC-6000 TC Nylon 12  (discontinued **)
Therma-Tech™ Thermal Management Compounds have been engineered to combine the heat transfer and cooling capabilities of metals with the design freedom, weight reduction and cost advantages of therm..
Deflection Temperature at 0.46 MPa (66 psi) 193 °C
379 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP LUBRICOMP QAP22S PA 6/10 (Asia Pacific)
LNP* Lubricomp* QAP22S is a compound based on Nylon 6/10 resin containing PTFE, Aramid Fiber, Silicone. Added features of this material include: Internally Lubricated, Heat Stabilized.
Deflection Temperature at 0.46 MPa (66 psi) 193 °C
379 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP LUBRICOMP QAP22S PA6.10
LNP* LUBRICOMP* QAP22S is a compound based on Nylon 6/10 resin containing 10% PTFE/Silicone, 10% Aramid Fiber. Added features of this material include: Wear Resistant, Heat Stabilized.
Deflection Temperature at 0.46 MPa (66 psi) 193 °C

@Thickness 6.40 mm
379 °F

@Thickness 0.252 in
unannealed; ASTM D 648
SABIC Innovative Plastics Ultem ATX153R PEI+PCE
30% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Americas region.
Deflection Temperature at 0.46 MPa (66 psi) 193 °C

@Thickness 6.40 mm
379 °F

@Thickness 0.252 in
unannealed; ASTM D 648
SABIC Innovative Plastics Ultem ATX153R PEI+PCE (Asia Pacific)
30% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Asia Pacific region.
Deflection Temperature at 0.46 MPa (66 psi) 193 °C

@Thickness 6.40 mm
379 °F

@Thickness 0.252 in
unannealed; ASTM D648
SABIC Innovative Plastics NORYL GTX GTX910 PPE+PS+PA
Unfilled grade for automotive on-line painted components. Dimensional stability. Excellent chemical resistance. Class A surface appearance.
Deflection Temperature at 0.46 MPa (66 psi) 193 °C

@Thickness 6.40 mm
379 °F

@Thickness 0.252 in
unannealed; ASTM D648
SABIC Innovative Plastics NORYL GTX GTX910 PPE+PS+PA (Asia Pacific)
Unfilled grade for automotive on-line painted components. Dimensional stability. Excellent chemical resistance. Class A surface appearance.
Deflection Temperature at 0.46 MPa (66 psi) 193 °C
379 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP LUBRICOMP YI001 Polyester Elastomer (Europe-Africa-Middle East)
LNP* LUBRICOMP* YI001 is a compound based on Polyester Elastomer containing Silicone. Added features include; Internally Lubricated.
Deflection Temperature at 0.46 MPa (66 psi) 193 °C

@Thickness 6.40 mm
379 °F

@Thickness 0.252 in
unannealed; ASTM D 648
SABIC Innovative Plastics Ultem ATX153R PEI+PCE (Europe-Africa-Middle East)
30% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Europe-Africa-Middle East regio..
Deflection Temperature at 0.46 MPa (66 psi) 193 °C
379 °F
ASTM D648
Unitika M2350 PA6, Dry
Nano composite nylonInformation provided by Unitika Ltd.
Deflection Temperature at 0.46 MPa (66 psi) 193 °C
379 °F
Flatw 80x10x4, sp=64 mm; ISO 75/Bf
Eurostar Starflam PK0069 PA6, Mineral Fiber Filled, Flame Retardant, Injection Molded
Starflam PK0069 is a Free Flame Retardant Mineral Filled Polyamide 6 Injection Molding Resin (also known as Starflam PA6 30E6 Z88)Information provided by Eurostar.
Deflection Temperature at 0.46 MPa (66 psi) 193 °C
379 °F
ASTM D648
Adell AS-10 Nylon 66, General Purpose
Data provided by Adell Plastics, Inc.
Deflection Temperature at 0.46 MPa (66 psi) 193 °C
379 °F
ASTM D648
Ashley Polymers Ashlene® 527 Nylon 66
A very high impact, slightly lubricated, nylon resin.Data provided by the manufacturer
Deflection Temperature at 0.46 MPa (66 psi) 193 °C
379 °F
ASTM D648
A. Schulman ComAlloy Hiloy® 419 Polyester - PBT, Mineral Reinforced
Data provided by the manufacturer, ComAlloy International Company.40% Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Deflection Temperature at 0.46 MPa (66 psi) 193 °C
379 °F
ASTM D648
Adell AS-30 Nylon 66, General Purpose
Data provided by Adell Plastics, Inc.
Deflection Temperature at 0.46 MPa (66 psi) 193 °C
379 °F
ISO 75
BASF Ultradur B 4406 G4 BKQ113 7110 20% Glass Filled PBT
Ultradur B 4406 G4 BKQ113 7110 is an UL V0 injection molding, pigmented black, PBT grade with 20% glass fiber reinforcement.
Deflection Temperature at 0.46 MPa (66 psi) 193 °C
379 °F
ASTM D648
A. Schulman ComAlloy Hiloy® 663 Nylon 6, Glass Bead Reinforced
Data provided by the manufacturer, ComAlloy International Company.30% Glass Bead Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Deflection Temperature at 0.46 MPa (66 psi) 193 °C

@Thickness 3.20 mm
379 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP THERMOCOMP PH0800A PA 6
LNP* THERMOCOMP* PH0800A is a compound based on Nylon 6 resin. Added feature of this material is: High Specific Gravity.
Deflection Temperature at 0.46 MPa (66 psi) 193 °C
379 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP Thermocomp PK0069 PA 6 (Europe-Africa-Middle East)
LNP* THERMOCOMP* PK0069 is a compound based on PA 6 resin containing Glass Bead, Flame Retardant. Added features include Flame Retardant.This data was supplied by SABIC-IP for the Europe-Africa-Midd..