- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 390 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 390 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 199 °C @Thickness 3.18 mm |
390 °F @Thickness 0.125 in |
Annealed; ASTM D648 |
| PolyOne LubriOne™ NY-10GF/10T BLACK Polyamide 6 (Nylon 6) Information provided by PolyOne |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 199 °C | 390 °F | ASTM D648 |
| Polymer Resources PC/TP-GP3-G30 PC/Polyester Alloy, 30% Glass Reinforced Superior Chemical Resistance, 30% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information pr.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 199 °C | 390 °F | ASTM D648 |
| Polymer Resources TP-FRG7.5 Polybutylene Terephthalate, 7 1/2 % Glass Reinforced, Flame Retardant Polybutylene Terephthalate, 7 1/2 % Glass Reinforced, Flame RetardantProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test sam.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 199 °C | 390 °F | ASTM D648 |
| Polymer Resources TP-IGFR-G30 Polybutylene Terephthalate, 30% Glass Reinforced, Flame Retardant, Reduced Warpage Polybutylene Terephthalate, 30% Glass Reinforced, Flame Retardant, Reduced WarpageProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmen.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 199 °C | 390 °F | ASTM D648 |
| Polymer Resources TP-IM-G15 Polybutylene Terephthalate, 15% Glass Reinforced, Impact Modified Polybutylene Terephthalate, 15% Glass Reinforced, Impact ModifiedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 199 °C | 390 °F | ASTM D648 |
| Shell Carilon® DA6P2L10 Polyketone, High Performance Lubricated Injection Molding Grade
(discontinued **) Shell announced in Feb. 2000 that the Carilon product line is being discontinued. CARILON Polymer DA6P2L10 is a high-performance lubricated injection molding grade with mechanical properties which .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 199 °C | 390 °F | ASTM D648 |
| PolyOne Lubri-Tech™ NL-10GF/15TF Nylon 6/12 - 10% Glass Fiber - 15% PTFE Flock
(discontinued **) Data provided by PolyOne. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 199 °C @Thickness 3.20 mm |
390 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Ultem ATX202R PEI+PCE (Asia Pacific) 20% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 199 °C @Thickness 3.20 mm |
390 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Ultem ATX202R PEI+PCE (Europe-Africa-Middle East) 20% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Europe-Africa-Middle East regio.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 199 °C | 390 °F | Unannealed; ASTM D648 |
| Techmer ES Electrablend® PA6/6 C BK Availability: North AmericaForms: PelletsFiller/Reinforcement: Unspecified Filler/Reinfor.Features: ConductiveAppearance: BlackInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 199 °C | 390 °F | Unannealed; ASTM D648 |
| Techmer ES Electrablend® PA6/6 IM C BK Availability: North AmericaForms: PelletsFiller/Reinforcement: Unspecified Filler/Reinfor.Additive: Impact ModifierFeatures: Conductive and Impact ModifiedAppearance: BlackInformation provided by TP.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 199 °C @Thickness 3.20 mm |
390 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Ultem HFATX200 PEI+PCE High flow Polyetherimide blend with internal mold release. ECO Conforming.This data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 199 °C | 390 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® PS 06001 Availability: North AmericaForms: PelletsFiller/Reinforcement: Mineral Filler/Unspecified FillerReinfor.Information provided by TP Composites, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 199 °C @Thickness 3.20 mm |
390 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Thermocomp PH0600A PA 6 LNP THERMOCOMP* PH0600A is a compound based on Nylon 6 resin. Added features of this material include: High Specific Gravity.This data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 199 °C | 390 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics Noryl GTX GTX977 PPE+PA66 Noryl GTX GTX977 resin is a mineral reinforced conductive Noryl GTX with a improved CTE (7) with a balanced performance of Impact and stiffness. (developmental grade : EXNX0074)This data was supplie.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 199 °C | 390 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics Noryl GTX GTX977 PPE+PA66 (Asia Pacific) Noryl GTX GTX977 resin is a mineral reinforced conductive Noryl GTX with a improved CTE (7) with a balanced performance of Impact and stiffness. (developmental grade : EXNX0074)This data was supplie.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 199 °C | 390 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics Noryl GTX GTX977 PPE+PA66 (Europe-Africa-Middle East) Noryl GTX GTX977 resin is a mineral reinforced conductive Noryl GTX with a improved CTE (7) with a balanced performance of Impact and stiffness. (developmental grade : EXNX0074)This data was supplie.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 199 °C | 390 °F | ASTM D648 |
| Chase Plastics CP Pryme® N100L (COND, 50% RH) Nylon 6, Internally Lubricated Information provided by Chase Plastics. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 199 °C | 390 °F | method Bf; ISO 75-2 |
| Lubrizol ESTALOC® T514 Ester-Type, Reinforced Engineering Thermoplastic (European Grade) Description: Estaloc® RETP (Reinforced Engineering Thermoplastic) is a tough, dimensionally stable, abrasion-resistant thermoplastic that withstands demanding environments. Developed as an extensio.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 199 °C | 390 °F | ASTM D648 |
| Clariant Renol 6004G23 Nylon 6, 23% Glass Fiber Reinforced Data provided by Clariant Masterbatches |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 199 °C | 390 °F | ASTM D648 |
| Adell BT-13 Nylon 6, 15% Glass Reinforced; Impact Modified Data provided by Adell Plastics, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 199 °C | 390 °F | ASTM D648 |
| Adell BT-33 Nylon 6, 15% Glass Reinforced; Impact Modified Data provided by Adell Plastics, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 199 °C | 390 °F | ASTM Test |
| BASF Ultramid® A27 E 01 PA66 (Dry) Ultramid A27 E 01 is a low-viscosity, general-purpose PA66 grade for compounding. It conforms to FDA requirements including, 21 CFR 177.1500,EU Directive 2002/72/EC, the German BfR recommendation ".. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 199 °C | 390 °F | ASTM Test |
| BASF Ultramid® A34 01 PA66 (Dry) Ultramid A34 01 is an intermediate visosity, PA66 grade. It conforms to FDA requirements including, 21 CFR 177.1500,EU Directive 2002/72/EC, the German BfR recommendation "X Polyamide", 1.6.1998 or .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 199 °C | 390 °F | ASTM D648 |
| A. Schulman ComAlloy Lubrilon® 602 Nylon 6/6, Molybdenum Disulfide Filled, Flow Enhanced Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulma.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 199 °C | 390 °F | ASTM D648 |
| Aaron Industries AAROPRENE® AEN 6600-3 Nylon 6/6 Engineered Resin |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 199 °C @Thickness 3.20 mm |
390 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Valox® VC108 PBT (Asia Pacific) This data was supplied by SABIC-IP for the Asia Pacific region. |
|||