Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 394 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 201 °C

@Thickness 3.20 mm
394 °F

@Thickness 0.126 in
ASTM D648
Ovation Polymers RIGITRON 20433 GF PBT, 33% Glass Reinforced
PBT - Glass reinforced (33 %), high tensile strength, stiffness and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepared acco..
Deflection Temperature at 0.46 MPa (66 psi) 201 °C
394 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP COLORCOMP W10009I PBT (Europe-Africa-Middle East)
LNP* THERMOCOMP* W10009I is a compound based on Polybutylene Terephalate resin containing Flame Retardant.
Deflection Temperature at 0.46 MPa (66 psi) 201 °C
394 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP LUBRICOMP EL002 PEI
LNP* Lubricomp* EL002 is a compound based on Polyetherimide resin containing 10% PTFE. Added features of this material include: Internally Lubricated.
Deflection Temperature at 0.46 MPa (66 psi) 201 °C
394 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP LUBRICOMP RL004 PA 66
LNP* LUBRICOMP* RL004 is a copmpound based on Nylon 66 resin containing 20% PTFE. Added feature of this grade includes: Wear Resistant.
Deflection Temperature at 0.46 MPa (66 psi) 201 °C

@Thickness 3.20 mm
394 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP LUBRICOMP RP003 PA 66
LNP* LUBRICOMP* RP003 is a compound based on Nylon 66 resin containing 15% PTFE/Silicone. Added feature of this material is: Wear Resistant.
Deflection Temperature at 0.46 MPa (66 psi) 201 °C

@Thickness 3.20 mm
394 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP LUBRICOMP RP003 PA 66 (Asia Pacific)
LNP* Lubricomp* RP003 is a compound based on Nylon 66 resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated.
Deflection Temperature at 0.46 MPa (66 psi) 201 °C

@Thickness 3.20 mm
394 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics ULTEM LTX300A PEI Copolymer
High flow Polyetherimide blend with low toxicity, smoke and flame evolution. ECO Compliant, UL94 V0 listing in recognized colors.
Deflection Temperature at 0.46 MPa (66 psi) 201 °C

@Thickness 3.20 mm
394 °F

@Thickness 0.126 in
unannealed; ASTM D 648
SABIC Innovative Plastics Ultem LTX300A PEI Copolymer (Europe-Africa-Middle East)
High flow Polyetherimide blend with low toxicity, smoke and flame evolution. ECO Compliant, UL94 V0 listing in recognized colors.This data was supplied by SABIC-IP for the Europe-Africa-Middle East..
Deflection Temperature at 0.46 MPa (66 psi) 201 °C

@Thickness 3.20 mm
394 °F

@Thickness 0.126 in
unannealed; ASTM D 648
SABIC Innovative Plastics Valox® 507 PBT+PC (Asia Pacific)
This data was supplied by SABIC-IP for the Asia Pacific region.
Deflection Temperature at 0.46 MPa (66 psi) 201 °C

@Thickness 3.20 mm
394 °F

@Thickness 0.126 in
unannealed; ASTM D 648
SABIC Innovative Plastics Valox® DR48M PBT (Asia Pacific)
This data was supplied by SABIC-IP for the Asia Pacific region.
Deflection Temperature at 0.46 MPa (66 psi) 201 °C

@Thickness 3.20 mm
394 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics ULTEM LTX300A PEI Copolymer (Asia Pacific)
High flow Polyetherimide blend with low toxicity, smoke and flame evolution. ECO Compliant, UL94 V0 listing in recognized colors.
Deflection Temperature at 0.46 MPa (66 psi) 201 °C
394 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP STAT-KON REF42 PA 66
LNP* STAT-KON* REF42 is a compound based on Nylon 66 resin containing 20% Glass Fiber, 10% Carbon Fiber. Added features of this material include: Electrically Conductive.
Deflection Temperature at 0.46 MPa (66 psi) 201 °C
394 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP STAT-LOY PF306 PA 6
LNP* STAT-LOY* PF306 is a compound based on Nylon 6 resin containing 30% Glass Fiber. Added feature of this grade includes: Antistat.
Deflection Temperature at 0.46 MPa (66 psi) 201 °C
394 °F
Unannealed; ISO 75-2/B
Ascend Performance Materials Vydyne® 21SPF BLK Nylon 66, Conditioned
Vydyne® 21SPF BLK is a, general-purpose PA66 resin used for extrusion-compounding. Available in black, it is designed principally for injection-molding fabrication. This grade offers a well-balance..
Deflection Temperature at 0.46 MPa (66 psi) 201 °C
394 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP STAT-KON REF42 PA 66 (Asia Pacific)
LNP* Stat-kon* REF42 is a compound based on Nylon 66 resin containing Glass Fiber, Carbon Fiber.