- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 477 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 477 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 247 °C | 477 °F | ASTM D648 |
| Gromax CCP PET 9130-104 30% Glass Filled Product Description: PET glass/mineral 30% reinforced injection molding grade. Characteristics:Excellent electrical property Excellent mechanic and chemical property Excellent weatherability Excell.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 247 °C @Thickness 3.20 mm |
477 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP RX85514 PA 66 LNP LUBRICOMP* RX85514 is a compound based on Nylon 66 resin containing Proprietary Filler(s). Added features of this material include: Internally Lubricated. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 247 °C @Thickness 3.20 mm |
477 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP RX88514 PA 66 LNP LUBRICOMP* RX85514 is a compound based on Nylon 66 resin containing Proprietary Filler(s). AddedLNP LUBRICOMP* RX85514 is a compound based on Nylon 66 resin containing Proprietary Filler(s). A.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 247 °C @Thickness 3.20 mm |
477 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Thermocomp 9X06477 SPS LNP* Thermocomp* 9X06477 is a compound based on Syndiotactic Polystyrene resin containing Glass Fiber. Characteristics of this grade is Heat Stabilized.This data was supplied by SABIC-IP for the Am.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 247 °C @Thickness 3.20 mm |
477 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP RF003ES PA 66 LNP* THERMOCOMP* RF003ES is a Nylon 66 base resin containing 15% Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 247 °C | 477 °F | DAM; ISO 75-1/-2 |
| DuPont Performance Polymers Zytel® 84G33 BKB031 Nylon 66 + Nylon 6
(Unverified Data**) 33% Glass Reinforced Toughened Polyamide 66 + Polyamide 6 Zytel 84G33 BKB031 is a 33% glass reinforced toughened polyamide 66 and polyamide 6 co-melt black cube blended resin. This resin was develop.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 247 °C | 477 °F | ASTM D648 |
| Cheng Yu Plastic E2345 Flame Retardant PET, 45% Glass Fiber |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 247 °C | 477 °F | ASTM D648 |
| A. Schulman ComAlloy Comtuf® 621 Nylon 6/6, Glass Reinforced, Impact Modified, Flow Enhanced Data provided by the manufacturer, ComAlloy International Company.13% Glass Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been int.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 247 °C | 477 °F | ASTM D648 |
| Adell WR-37 33% Glass Reinforced PET |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 247 °C | 477 °F | ASTM D648 |
| LATI LATILUB 80-40GRT Polyphenylene sulfide Base (PPS), 40% Graphite and PTFE Self Lubricating Plastic
(U Description: Latilub self-lubricating plastic materials are more and more often designed to replace metals in applications such as gears, bushings, cams, slides, etc), for which, besides their intri.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 247 °C | 477 °F | ASTM D648 |
| Gromax CCP PET 9130-200 30% Glass Filled Product Description: PET glass/mineral 30% reinforced injection molding grade. Characteristics:Excellent electrical property Excellent mechanic and chemical property Excellent weatherability Excell.. |
|||