Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 534 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 279 °C
534 °F
Unannealed; ASTM D648
Solvay Specialty Polymers Amodel® A-1230 L Polyphthalamide (PPA)  (discontinued **)
Amodel A-1230 L is a 30% mineral filled polyphthalamide (PPA) that offers low warpage and excellent dimensional stability. This resin also has a high deflection temperature, flexural modulus and ten..
Deflection Temperature at 0.46 MPa (66 psi) 279 °C
534 °F
Unannealed; ASTM D648
Solvay Specialty Polymers Amodel® AT-1125 HS Polyphthalamide (PPA)  (Unverified Data**)
Amodel AT-1125 HS polyphthalamide (PPA) is a toughened, heat stabilized 25% glass reinforced resin, designed as a cost effective solution for applications requiring stiffness, good dimensional stabi..
Deflection Temperature at 0.46 MPa (66 psi) 279 °C

@Thickness 3.20 mm
534 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP LUBRICOMP OCL36EXP PPS - LINEAR
LNP* LUBRICOMP* OCL36EXP is a compound based on Linear PPS containing 30% Carbon Fiber, 15% PTFE. Added features of this grade include; Wear Resistant, Electrically Conductive.
Deflection Temperature at 0.46 MPa (66 psi) 279 °C

@Thickness 3.20 mm
534 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP LUBRICOMP OCP36 PPS
LNP* LUBRICOMP* OCP36 is a compound based on Polyphenylene Sulfide resin containing 30% Carbon Fiber, 15% PTFE/Silicone. Added features of this grade include: Wear Resistant, Bearing Grade, Electr..
Deflection Temperature at 0.46 MPa (66 psi) 279 °C
534 °F
Unannealed; ASTM D648
Solvay Specialty Polymers Amodel® AT-1125 HS Polyphthalamide (PPA), 25% Glass Fiber (Dry)
Amodel® AT-1125 HS polyphthalamide (PPA) is a toughened, heat stabilized 25% glass reinforced resin, designed as a cost effective solution for applications requiring stiffness, good dimensional s..
Deflection Temperature at 0.46 MPa (66 psi) 279 °C

@Thickness 3.20 mm
534 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP LUBRICOMP JCL36E PES
LNP* LUBRICOMP* JCL36E is a compound based on Polyethersulfone (PES) resin containing 30% Carbon Fiber, 15% PTFE. Added feature of this grade is: Wear Resistant.
Deflection Temperature at 0.46 MPa (66 psi) 279 °C

@Thickness 3.20 mm
534 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP STAT-KON OE004AE PPS - Branched
LNP STAT-KON* OE004AE is a compound based on PPS - Branched resin containing 20% Carbon Fiber. Added features of this material are: Easy Molding, Electrically Conductive.
Deflection Temperature at 0.46 MPa (66 psi) 279 °C
534 °F
ASTM D648
A. Schulman ComAlloy E-16769N Internally Lubricated, Glass Fiber Reinforced PPS
Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulma..
Deflection Temperature at 0.46 MPa (66 psi) 279 °C
534 °F
ASTM D648
LATI LARTON G/40 40% Glass Fiber Filled Polyphenylene sulfide (PPS)  (Unverified Data**)
Description: Larton thermoplastics are polyphenylene sulfide (PPS) products. They are distinguished by a group of very interesting properties combined with easy moldability. Larton parts feature: ex..