Thermal Properties | Metric | English | Comments |
---|---|---|---|
Brittleness Temperature | -40.0 °C | -40.0 °F | ASTM D746 |
PolyOne OnFlex™ HFFR 310-01 Thermoplastic Elastomer (TPE) OnFlex™ HFFR 310-01 is a non-halogen flame retardant material designed for cable jackets. New Product. Commercial specifications have not been established. - Non-halogen flame retardant - UL62 comp.. |
|||
Brittleness Temperature | -40.0 °C | -40.0 °F | Low temp embrittlement; ASTM D746 |
Rogers Corporation Poron® 4701-40-15 Cellular Urethane Foam Standard color is black (04); others are available. Passes flammability tests UL HBF (File E20305), MVSS 302, and CSA Component Acceptance HBF (File 188149). Passes fogging test SAE-J 1736 for 3 h.. |
|||
Brittleness Temperature | -40.0 °C | -40.0 °F | ASTM D746-98 |
Rogers Corporation Poron® 4701-50 Thin as Cast Urethane Foam, Firm, Thin as Cast Firm material used for managing high energy impact with gasketing needs. Standard available thickness range from 0.012" to 0.500" (0.30 mm to 12.7 mm).Features and Benefits of PORON Products: Exce.. |
|||
Brittleness Temperature | -40.0 °C | -40.0 °F | Low temp embrittlement; ASTM D746 |
Rogers Corporation Poron® 4701-50-30 Cellular Urethane Foam Standard color is black (04); others are available. Passes flammability test MVSS 302. Passes fogging test SAE-J 1736 for 3 hrs. at 100°C (212°F). Passes cold flexibility per MIL-P-12420D at -4.. |
|||
Brittleness Temperature | <= -40.0 °C | <= -40.0 °F | ASTM D 746 |
Karina 809D48/1-C-IS-LMP Black PVC Compound Heavy metal free PVC compound recommended for extrusion of coaxial cables jacket. Also recommended for extrusion of automotive flexible tube. Working temperature range: -40°C to +80°C.Inform.. |
|||
Brittleness Temperature | -40.0 °C | -40.0 °F | ASTM D746 |
SABIC Innovative Plastics NORYL WCA871A PPE (Europe-Africa-Middle East) Flame retardant performance and mechanical properties capable of meeting UL VW-1 requirement and 105C temperature rating as defined UL1581. UL1581 tests conducted on 1.0mmD wire with AWG28 conductor.. |
|||
Brittleness Temperature | <= -40.0 °C | <= -40.0 °F | ASTM D746 |
SABIC Innovative Plastics NORYL WCA901 PPE-TPE Non-Halogenated flame retardant, flexible Noryl resin intended for evaluation in wire and cable applications, capable of meeting VW-1 and 105°C end use temperature requirements as defined by UL.. |
|||
Brittleness Temperature | <= -40.0 °C | <= -40.0 °F | ASTM D746 |
SABIC Innovative Plastics NORYL WCD801A PPE-TPE (Europe-Africa-Middle East) Flexible, migration-improved, halogen free extrusion grade intended for evaluation in applications such as wire insulation and cable jacket. Flame performance capable of meeting UL VW1 requirements.. |
|||
Brittleness Temperature | <= -40.0 °C | <= -40.0 °F | ASTM D746 |
SABIC Innovative Plastics NORYL WCD861A PPE-TPE Flexible, migration-improved, halogen free extrusion grade intended for evaluation in applications such as wire insulation and cable jacket. Flame performance capable of meeting UL VW1 requirements.. |
|||
Brittleness Temperature | <= -40.0 °C | <= -40.0 °F | ASTM D746 |
SABIC Innovative Plastics NORYL WCD883 PPE-TPE (Asia Pacific) Flexible and non-halogenated flame retardant extrusion grade intended for evaluation in applications such as jacket of HD 21.14 flexible cables. Flame retardant performance capable of meeting EN 502.. |
|||
Brittleness Temperature | <= -40.0 °C | <= -40.0 °F | ASTM D746 |
SABIC Innovative Plastics NORYL WCD891B PPE-TPE (Asia Pacific) Non-halogenated flame retardant, flexible Noryl resin intended for evaluation in wire and cable applications. Strong flame retardant performance capable of meeting VW-1 and 80°C end use tempera.. |
|||
Brittleness Temperature | <= -40.0 °C | <= -40.0 °F | ASTM D746 |
SABIC Innovative Plastics NORYL WCD915 PPE-TPE (Asia Pacific) Flexible and non-halogenated flame retardant extrusion grade intended for evaluation in applications such as insulation materials. Flame retardant performance capable of meeting UL 1581 VW-1 require.. |
|||
Brittleness Temperature | <= -40.0 °C | <= -40.0 °F | ASTM D746 |
SABIC Innovative Plastics NORYL WCP700 PPE-TPE (Europe-Africa-Middle East) Flexible PPE-TPE injection grade suitable for over-molding applications such as plugs, strain relief's, and connectors. Good processability. 70 Shore A hardness. |
|||
Brittleness Temperature | <= -40.0 °C | <= -40.0 °F | ASTM D746 |
SABIC Innovative Plastics NORYL WCP921 PPE-TPE Flexible Noryl* injection molding grade. Low specific gravity with good non-halogenated flame retardant performance. Developed for evaluation in overmolding applications such as plugs, strain relief.. |
|||
Brittleness Temperature | <= -40.0 °C | <= -40.0 °F | ASTM D746 |
SABIC Innovative Plastics NORYL WCP921A PPE-TPE (Asia Pacific) Flexible Noryl* injection molding grade. Low specific gravity with good non-halogenated flame retardant performance. Developed for overmolding applications such as plugs, strain reliefs, and connect.. |
|||
Brittleness Temperature | <= -40.0 °C | <= -40.0 °F | |
Sibur NGP 40-32 Polyvinyl Chloride (PVC) Shall correspond to control sample, approved in accordance with the established procedure. Pores, which can be seen by eyes, are not allowed. Plastic shall no burn at stop of worm extruder for a p.. |
|||
Brittleness Temperature | <= -40.0 °C | <= -40.0 °F | |
Sibur O-40 Compound OM-40 Polyvinyl Chloride (PVC) Shall correspond to control sample, approved in accordance with the established procedure. Pores, which can be seen by eyes, are not allowed. Plastic shall no burn at stop of worm extruder for a p.. |
|||
Brittleness Temperature | -40.0 °C | -40.0 °F | ASTM D746 |
Teknor Apex APEX® 3801-70 Polyvinyl Chloride, Flexible Features: Non-DEHP Plasticizer; Ethylene Oxide Sterilizable; High Heat Resistance Uses: Medical/Healthcare Applications Processing Method: Extrusion Forms: PelletsInformation Provided by Teknor Apex.. |
|||
Brittleness Temperature | <= -40.0 °C | <= -40.0 °F | ASTM D746 |
SABIC Innovative Plastics NORYL WCD841U PPE-TPE (Asia Pacific) Flexible, UV stabilized, halogen free extrusion grade for applications such as wire insulation and cable jacket. Good color stability after UV weathering per ASTM D4459. Light color capable. Flame r.. |
|||
Brittleness Temperature | -40.0 °C | -40.0 °F | ASTM D746 |
UBE J3519 Polyethylene Description: UBE Polyethylene is polymerized at high pressure using a tubular reactor. Production conditions are strictly controlled ensuring the product's superior physical and mechanical prope.. |
|||
Brittleness Temperature | -40.0 °C | -40.0 °F | Cold Flex; ISO 458/2 |
Fainplast Compounds FAINGUM 6510 Flexible PVC, Injection Molding for Footwear Soles with rubber |
|||
Brittleness Temperature | -40.0 °C | -40.0 °F | Cold Flex; ISO 458/2 |
Fainplast Compounds GS 59/F Flexible PVC, Injection Molding for Footwear Sandals |
|||
Brittleness Temperature | -40.0 °C | -40.0 °F | Cold Flex; ISO 458/2 |
Fainplast Compounds GS 60/R1 Flexible PVC, Injection Molding for Footwear Anti-accident soles |
|||
Brittleness Temperature | -40.0 °C | -40.0 °F | Cold Flex; ISO 458/2 |
Fainplast Compounds PH 55 Flexible PVC, Transparent Extrusion Transparent profiles |
|||
Brittleness Temperature | <= -40.0 °C | <= -40.0 °F | ASTM D2137 |
Aearo E-A-R Specialty Composites VersaDamp™ V-2350 TPE VersaDamp TPEs are olefinic dynamic vulcanizates. The VersaDamp 2000 series materials provide predictable damping performance throughout a broad range of temperatures. They can be injection molded.. |
|||
Brittleness Temperature | -40.0 °C | -40.0 °F | ASTM D-746 |
Axiall 18753 Wire & Cable Flexible PVC Non-lead stabilized, fungus resistant 105 C rated jacket compound.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |
|||
Brittleness Temperature | -40.0 °C | -40.0 °F | ASTM D-746 |
Axiall 8751 Moldings & Extrusions Flexible PVC Clear, UV stabilized extrusion and molding compound.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |
|||
Brittleness Temperature | -40.0 °C | -40.0 °F | ASTM D-746 |
Axiall 10750 Wire & Cable Flexible PVC General purpose 75C jacket compound with good low temperature properties.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |
|||
Brittleness Temperature | -40.0 °C | -40.0 °F | |
Colorite Polymers 6812 Clear Injection Molding Vinyl Compound Description: Clear non-toxic vinyl compounds are utilized by the health and medical industries for injection molding of various components such as drip chambers, connectors, valves, etc. The vinyl c.. |
|||
Brittleness Temperature | <= -40.0 °C | <= -40.0 °F | ASTM D746 |
SABIC Innovative Plastics NORYL WCD835 PPE-TPE (Asia Pacific) Flexible, low odor, halogen free extrusion grade intended for evaluation in applications such as wire insulation and cable jacket. Flame performance capable of meeting UL VW1 requirements. 80C end.. |