Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

Polymer Property : Deflection Temperature at 8.0 MPa = 248 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 8.0 MPa 120 - 140 °C
248 - 284 °F
ISO 75-C
Raschig Group 5553 DAP
Glass-fiber reinforced diallyl phthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensiona..
Deflection Temperature at 8.0 MPa 120 - 140 °C
248 - 284 °F
Injection; ISO 75-C
Raschig Group 5563 DAP
Glass-fiber reinforced diallyl phthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensiona..
Deflection Temperature at 8.0 MPa 120 - 140 °C
248 - 284 °F
Injection and Compression; ISO 75-C
Raschig Group MELOPLAS® 2500 MF
Cellulose-reinforced MF molding compound in white and colored shades. Very good electrical properties, high surface hardness, good abrasion- and UV-stability, very good resistance to chemicals - al..
Deflection Temperature at 8.0 MPa 120 - 140 °C
248 - 284 °F
Injection and Compression; ISO 75-C
Raschig Group MELOPLAS® 3025 MF
Cellulose-reinforced and inorganically filled MF molding compound in white and colored shades. High surface hardness, good UV and heat stability, very good resistance to chemicals - also to foodstu..
Deflection Temperature at 8.0 MPa 120 - 200 °C
248 - 392 °F
Average value: 165 °C Grade Count:8
Overview of materials for Diallyl Phthalate (DAP) Molding Compound, Short Glass Fiber Filled
This property data is a summary of similar materials in the MatWeb database for the category "Diallyl Phthalate (DAP) Molding Compound, Short Glass Fiber Filled". Each property range of values repor..
Deflection Temperature at 8.0 MPa 120 °C
248 °F
ISO 75-2
Hexion Bakelite™ 151733 Phenolic Formaldehyde Resin  (discontinued **)
Phenolic molding compound, mainly organically filled, standard molding compound for normal stress.Application areas: Contact strips.Information provided by Bak AGBak AG became a part of Hexion in 20..
Deflection Temperature at 8.0 MPa 120 °C
248 °F
ISO 75-1/-2
Lanxess Durethan® BKV 25 H2.0 LT 904040 Nylon 6, 25% Glass Fiber
PA 6, injection molding grade, 25% glass fibers, good heat-ageing resistance, laser-weldable
Deflection Temperature at 8.0 MPa 120 °C
248 °F
ISO 75-1/-2
EMS-Grivory Grivory® 2SV-30H black 9992 PA610-GF30
Product Description: GRILAMID XE 3976 black 9992 is a 30% glass fiber reinforced, heat stabilized polyamide 610 injection molding grade. This product is to a large extent based on renewable raw mate..
Deflection Temperature at 8.0 MPa 120 °C
248 °F
ISO 75-1/-2
EMS-Grivory Grivory® 2SV-30H nat PA610-GF30
Product Description: GRILAMID XE3976 natural 9992 is a 30% glass fiber reinforced, heat stabilized polyamide 610 injection molding grade. This product is to a large extent based on renewable raw mat..
Deflection Temperature at 8.0 MPa 120 °C
248 °F
ISO 75-1/-2
EMS-Grivory Grivory® BGZ-15 PA6-GF15
Information provided by EMS Grivory
Deflection Temperature at 8.0 MPa 120 °C
248 °F
ISO 75-1/-2
EMS-Grivory Grivory® XE 4108 black 9992 PA612-GF50
Product description: Grilamid XE 4108 black 9992 is a 50% glass fiber reinforced, heat stabilized polyamide 612 injection molding grade. The main features of Grilamid XE 4108 are: low water absorpti..
Deflection Temperature at 8.0 MPa 120 °C
248 °F
ISO 75-1/-2
EMS-Grivory Grivory® XE 4108 nat PA612-GF50
Product description: Grilamid XE 4108 natural is a 50% glass fiber reinforced, heat stabilized polyamide 612 injection molding grade. The main features of Grilamid XE 4108 are: low water absorptiong..
Deflection Temperature at 8.0 MPa 120 °C
248 °F
ISO 75-1/-2
EMS-Grivory Grivory® BGZ-40 PA6-GF40
Product description: Grilon BGZ-40 is a normal viscosity, heat stabilized and impact modified PA 6 injection molding type with 40% glass fibers. Grilon BGZ-40 has the following important properties:..
Deflection Temperature at 8.0 MPa 120 °C
248 °F
ISO 75-1/-2
EMS-Grivory Grivory® XE 5051 (BGZ-40 FC) PA6-GF40
Product description: Grilon XE 5051 is a impact modified, heat stabilized PA 6 injection molding grade with 40% glass fiber reinforcement. Grilon XE 5051 has the following important properties: High..
Deflection Temperature at 8.0 MPa 120 °C
248 °F
ISO 75-1/-2
EMS-Grivory Grivory® XE 4192 black 9992 PA610-GF30
Information provided by EMS Grivory
Deflection Temperature at 8.0 MPa 120 °C
248 °F
ISO 75-1/-2
Lanxess Pocan® TP 740-201 000000 PBT + ASA, 20% Glass Fiber  (discontinued **)
PBT+ASA, 20% glass fibers, injection molding, low tendency to warp, improved surface finish
Deflection Temperature at 8.0 MPa 120 °C
248 °F
ISO 75-2
Hexion Bakelite™ PF 2560 Phenolic Formaldehyde Resin, High Surface Quality, For Electrostatic Coating, UL Listed &n
Phenolic molding compound, inorganically/organically filled, average heat resistant, high surface quality, lower water absorption than PF 31, minimal distortion, UL listed molding compound 1.5 mm/V-..