Polymer Property : Deflection Temperature at 8.0 MPa = 302 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 8.0 MPa 130 - 150 °C
266 - 302 °F
Injection; ISO 75-C
Raschig Group 2572 AMC
Glass fiber reinforced Polyester molding compound. Very good mechanical strength, very good electrical properties and dimensional stability, good abrasion stability, high flame retardance in combin..
Deflection Temperature at 8.0 MPa 130 - 150 °C
266 - 302 °F
Injection; ISO 75-C
Raschig Group 5562 DAP
Glass-fiber reinforced diallyl phthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensiona..
Deflection Temperature at 8.0 MPa 130 - 150 °C
266 - 302 °F
ISO 75-C
Raschig Group MELOPAS® 156 MF Melamine
Glass fiber reinforced Melamine molding compound. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 200..
Deflection Temperature at 8.0 MPa 125 - 150 °C
257 - 302 °F
ISO 75-C
Raschig Group RALUPOL® 4802 UP Polyester
Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, good electrical values, excellent heat resistance, outstanding pourability. This product meets the allowed u..
Deflection Temperature at 8.0 MPa 125 - 150 °C
257 - 302 °F
ISO 75-C
Raschig Group RALUPOL® 802 UP Polyester
Glass-fiber reinforced polyester molding compound. Low molding shrinkage and post-shrinkage, good electrical values, good mechanical strength, good heat resistance. This product meets the allowed up..
Deflection Temperature at 8.0 MPa 125 - 150 °C
257 - 302 °F
ISO 75-C
Raschig Group RALUPOL® 804 UP Polyester
Glass-fiber reinforced polyester molding compound. Low molding shrinkage and post-shrinkage, good electrical values, good mechanical strength. This product meets the allowed upper limits for heavy m..
Deflection Temperature at 8.0 MPa 130 - 150 °C
266 - 302 °F
ISO 75 C
Vyncolit 4221 XB Novolac Phenolic
Mineral and organic filled phenolic molding compound with good mechanical properties.Information provided by Vyncolit, a Sumitomo Bak Group
Deflection Temperature at 8.0 MPa 130 - 150 °C
266 - 302 °F
ISO 75 C
Vyncolit 4451 XB Novolac Phenolic
Organic and mineral filled phenolic molding compound with excellent mechanical properties (highest notched impact strength).USES: Fuse holders, brush holders, circuit breakers, automotive ignition a..
Deflection Temperature at 8.0 MPa 130 - 150 °C
266 - 302 °F
ISO 75 C
Vyncolit 2530 W Novolac Phenolic
Mineral and organic filled phenolic molding compound with excellent thermal properties.USES: Lamp sockets, special lamp holders, pan handles and knobs.Information provided by Vyncolit, a Sumitomo Ba..
Deflection Temperature at 8.0 MPa 130 - 150 °C
266 - 302 °F
ISO 75 C
Vyncolit 2723 W Novolac Phenolic
Mineral and organic filled phenolic molding compound with excellent mechanical, thermal and dielectric properties. I2/FO classified under NF F 16-101 (Fire & Smoke classification).USES: Circuit bre..
Deflection Temperature at 8.0 MPa 130 - 150 °C
266 - 302 °F
ISO 75 C
Vyncolit 2920 W Novolac Phenolic
Mineral and organic filled molding compound with good dimensional stability and heat resistance.USES: Carburettor and intake manifold thermal insulator.Information provided by Vyncolit, a Sumitomo B..
Deflection Temperature at 8.0 MPa 130 - 150 °C
266 - 302 °F
ISO 75 C
Vyncolit 3520 CG Novolac Phenolic
Graphite filled phenolic molding compound with excellent dimensional stability. Self-lubricating and has a low coefficient of friction. Not suitable for electrical applications.USES: Gas meter par..