Polymer Property : Deflection Temperature at 8.0 MPa = 392 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Deflection Temperature at 8.0 MPa	>= 200 °C	>= 392 °F	ISO 75-C
Raschig Group 4552 Silicone Glass fiber reinforced silicone molding compound. Excellent thermal stability - up to +/- 300°C continuously, excellent electrical properties, good mechanical strength, very good dimensional stabi..
Deflection Temperature at 8.0 MPa	>= 200 °C	>= 392 °F	ISO 75-C
Raschig Group 4554 Silicone Glass fiber reinforced silicone molding compound. Excellent thermal stability - up to 300°C, exceptional electrical properties, good mechanical strength, very good dimensional stability. Processi..
Deflection Temperature at 8.0 MPa	>= 200 °C	>= 392 °F	ISO 75-C
Raschig Group 6501 DAIP Glass-fiber reinforced diallyl isophthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensi..
Deflection Temperature at 8.0 MPa	>= 200 °C	>= 392 °F	Injection; ISO 75-C
Raschig Group 6552 DAIP Glass-fiber reinforced diallyl isophthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensi..
Deflection Temperature at 8.0 MPa	<= 200 °C	<= 392 °F	Compression and Injection; ISO 75-C
Raschig Group RALUPOL® 4385 UP Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, very high arc resistance, very high mechanical values. This product meets the allowed upper limits for heavy..
Deflection Temperature at 8.0 MPa	>= 200 °C	>= 392 °F	Compression and Injection; ISO 75-C
Raschig Group RALUPOL® 4806 UP Glass-fiber reinforced polyester molding compound. Very low mold shrinkage and post-shrinkage, very good mechanical strength, very good electrical values, better performance values compared to UP 80..
Deflection Temperature at 8.0 MPa	>= 200 °C	>= 392 °F	Injection and Compression; ISO 75-C
Raschig Group SURAPLAST 54 UPA Glass fiber reinforced polyester molding compound. Minimal mold shrinkage and post-shrinkage, very good arc resistance, very good mechanical strength. This product meets the allowed upper limits for..
Deflection Temperature at 8.0 MPa	>= 200 °C	>= 392 °F	Injection; ISO 75-C
Raschig Group SURAPLAST UPA 63 UP Glass fiber reinforced polyester molding compound. Minimal mold shrinkage and post-shrinkage, very good arc resistance, very good mechanical strength. This product meets the allowed upper limits for..
Deflection Temperature at 8.0 MPa	200 Â°C	392 Â°F	ISO 75-2
Hexion UP 802 Unsaturated Polyester Resin, High Surface Quality, Low Shrinkage, High Arc Resistance Polyester molding compound, inorganically filled, glass fiber reinforced, styrene free, high dimensional stability, very slight post shrinkage, good mechanical properties, increased electrical value..
Deflection Temperature at 8.0 MPa	200 °C	392 °F	ISO 75-1/-2
EMS-Grivory Grivory® HT2V-3H PA6T/66-GF30 Product description: Grivory HT2V-3H is a 30 % glass fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamde. Polymer designation acc. to ISO: ..
Deflection Temperature at 8.0 MPa	200 °C	392 °F	ISO 75-1/-2
EMS-Grivory Grivory® HT2VZ-33H PA6T/66-GF33 Product description: Grivory HT2VZ-33H is a 33% glass fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. Grivory HT2VZ-33H is an injecti..
Deflection Temperature at 8.0 MPa	200 °C	392 °F	ISO 75-1/-2
EMS-Grivory Grivory® HTV-4H1 black 9205 PA6T/6I-GF40 Product description: Grivory HTV-4H1 black 9205 is a 40% glass fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. Acc. to ISO: PA 6T/6I...
Deflection Temperature at 8.0 MPa	200 °C	392 °F	ISO 75-1/-2
EMS-Grivory Grivory® TSG-50/4 FA PA666-GF50 Information provided by EMS Grivory
Deflection Temperature at 8.0 MPa	200 °C	392 °F	ISO 75-1/-2
EMS-Grivory Grivory® TSG-50/4 PA666-GF50 Product description: Grilon TSG-50/4 is a heat stabilized, normal viscosity PA66 + PA6 injection molding grade with 50% glass fibers. Grilon TSG-50/4 has the following important properties: High sti..
Deflection Temperature at 8.0 MPa	200 °C	392 °F	ISO 75-1/-2
EMS-Grivory Grivory® HT1V-4 FWA black 9225 PA6T/6I-GF40 Product description: Grivory HT1V-4 FWA black 9225 is a 40 wt.- % glass fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. Acc. to ISO: ..
Deflection Temperature at 8.0 MPa	200 °C	392 °F	ISO 75-1/-2
EMS-Grivory Grivory® HT1V-4 HY black 9205 PA6T/6I-GF40 Product description: Grivory HT1V-4 HY black 9205 is a 40% glass fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. Grivory HT1V-4 HY bl..
Deflection Temperature at 8.0 MPa	>= 200 °C	>= 392 °F	ISO 75-C
Raschig Group RALUPOL® 8605 UP Polyester Glass fiber reinforced polyester molding compound. Resistant to hydrolysis. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU dire..