Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 119 °C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 119 °C
246 °F
ASTM D648
Nylene® PA6 Mineral Filled 6240 HS Nylon 6
40% MR; Dry as molded.ALM, Nylene Canada, and Custom Resins are all operting companies of Polymeric Resources Corporation.
Deflection Temperature at 1.8 MPa (264 psi) 119 °C
246 °F
ASTM D648
Niche Polymer PPHM15BK Homopolymer PP
Information provided by Niche Polymer
Deflection Temperature at 1.8 MPa (264 psi) 119 °C
246 °F
ASTM D648
Niche Polymer PPHM6BK Homopolymer PP
Information provided by Niche Polymer
Deflection Temperature at 1.8 MPa (264 psi) 119 °C

@Thickness 3.20 mm
246 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics Cycoloy® XCM851 PC+ABS
High heat PC/ABS blend offering high modulus / low CTE and good practical impact
Deflection Temperature at 1.8 MPa (264 psi) 119 °C

@Thickness 3.20 mm
246 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics Cycoloy® XCM851 PC+ABS (Asia Pacific)
High heat PC/ABS blend offering high modulus / low CTE and good practical impact
Deflection Temperature at 1.8 MPa (264 psi) 119 °C
246 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
SABIC Innovative Plastics Lexan® 905 PC Copolymer (Asia Pacific)
Lexan 905 resin is a high flow, opaque, flame retardant polycarbonate resin blend. It is designed with non-chlorinated, non-brominated FR systems with UL-94 listing of both V0 and 5V ratings. Its ex..
Deflection Temperature at 1.8 MPa (264 psi) 119 °C
246 °F
ASTM D648
Parker Chomerics PREMIER™ A240-ST EMI Shielding Plastic
Description: PREMIER™ is the world’s first and most versatile commercially available conductive thermoplastic for real world EMI shielding solutions. It is a blend of PC/ABS thermoplastic polymer ..
Deflection Temperature at 1.8 MPa (264 psi) 119 °C

@Thickness 3.20 mm
246 °F

@Thickness 0.126 in
unannealed; ASTM D 648
SABIC Innovative Plastics Lexan® DMX1435 PC Copolymer
Lexan* DMX1435 is a UV stabilized standard flow polycarbonate copolymer resin with improved scratch resistance.This data was supplied by SABIC-IP for the Americas region.
Deflection Temperature at 1.8 MPa (264 psi) 119 °C

@Thickness 3.20 mm
246 °F

@Thickness 0.126 in
unannealed; ASTM D 648
SABIC Innovative Plastics Lexan® DMX2415 PC (Europe-Africa-Middle East)
Lexan* DMX2415 is a polycarbonate resin with improved scratch resistance. Lexan* DMX2415 is available in transparent, translucent, and opaque colors.This data was supplied by SABIC-IP for the Europe..
Deflection Temperature at 1.8 MPa (264 psi) 119 °C
246 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics Lexan® FXD1433T PC Copolymer (Asia Pacific)
Clear PC-siloxane copolymer with excellent processability in special light diffusion colors. Medium flow, UV stabilized. Improved toughness compared to standard PC in same color. Color package may ..
Deflection Temperature at 1.8 MPa (264 psi) 119 °C
246 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics Lexan® FXM1414T PC Copolymer (Asia Pacific)
PC-siloxane copolymer in special metallic colors. Medium flow. Improved toughness compared to medium flow standard PC in same color. Color package may affect performance.
Deflection Temperature at 1.8 MPa (264 psi) 119 °C

@Thickness 3.20 mm
246 °F

@Thickness 0.126 in
unannealed; ASTM D 648
SABIC Innovative Plastics Lexan® HPB3144G PC Copolymer
Standard flow, transparent, high purity polycarbonate copolymer resin with reduced oxygen permeability and water vapor transmission rate. For medical devices and pharmaceutical applications. Health..
Deflection Temperature at 1.8 MPa (264 psi) 119 °C

@Thickness 6.40 mm
246 °F

@Thickness 0.252 in
unannealed; ASTM D 648
SABIC Innovative Plastics Lexan® HPB3144G PC Copolymer
Standard flow, transparent, high purity polycarbonate copolymer resin with reduced oxygen permeability and water vapor transmission rate. For medical devices and pharmaceutical applications. Health..
Deflection Temperature at 1.8 MPa (264 psi) 119 °C

@Thickness 6.40 mm
246 °F

@Thickness 0.252 in
unannealed; ASTM D648
SABIC Innovative Plastics Lexan® ML6412 PC Copolymer (Asia Pacific)
ML6412 is an impact modified PC resin with non-brominated, non-chlorinated flame retardant system.
Deflection Temperature at 1.8 MPa (264 psi) 119 °C
246 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics Lexan® ML7647K PC (Asia Pacific)
Non FR Impact modified PC, excellent Fatigue performance with balanced Flow and impact. Available in Opaque only
Deflection Temperature at 1.8 MPa (264 psi) 119 °C
246 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics Lexan® ML7666 PC (Asia Pacific)
Non FR Impact modified PC, excellent Fatigue performance with balanced Flow and impact. Available in Opaque onlyThis data was supplied by SABIC-IP for the Asia Pacific region.
Deflection Temperature at 1.8 MPa (264 psi) 119 °C

@Thickness 3.20 mm
246 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics Lexan® DMX1435 PC Copolymer (Asia Pacific)
This product will be phased out per January 2015 -- Lexan* DMX1435 is a UV stabilized standard flow polycarbonate copolymer resin with improved scratch resistance.
Deflection Temperature at 1.8 MPa (264 psi) 119 °C

@Diameter 3.17 mm
246 °F

@Diameter 0.125 in
bar; ASTM D648
NOVA Chemicals Dylark® 480P20 High Performance Glass Filled Styrenic
Very high modulus, High heat resistance, Excellent flow characteristics, Excellent adhesion to urethaneApplications: Instrument panel substrates, consoles, Cluster housing, interior trimInjection Sp..
Deflection Temperature at 1.8 MPa (264 psi) 119 °C

@Thickness 3.20 mm
246 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics REMEX VR4831 PBT
15% Glass filled PBT, Flame retardant, UL Recognized, Utility grade, Black color only
Deflection Temperature at 1.8 MPa (264 psi) 119 °C
247 °F
Unannealed; ASTM D648
Techmer ES HiFill® PA6 CM40 HS 40% Mineral Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Mineral Filler, 40% Filler by WeightAdditive: Heat Stabilizer and LubricantFeatures: Heat Stabilized and LubricatedAppearance: Natural ..
Deflection Temperature at 1.8 MPa (264 psi) 119 °C
246 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics NORYL NH5020 PPE+PS
Noryl* NH5020 Resin is an unreinforced blend of Polyphenylene Ether(PPE) + Polystyrenre resin. The material offers a good balance of heat, flow, hydrolytic stability, and non-halogenated flame reta..
Deflection Temperature at 1.8 MPa (264 psi) 119 °C
246 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics NORYL NH5020 PPE+PS (Asia Pacific)
Noryl* NH5020 Resin is an unreinforced blend of Polyphenylene Ether(PPE) + Polystyrenre resin. The material offers a good balance of heat, flow, hydrolytic stability, and non-halogenated flame reta..
Deflection Temperature at 1.8 MPa (264 psi) 119 °C
246 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics NORYL NH5120C PPE+PS (Europe-Africa-Middle East)
Noryl* NH5120C resin is a modified PPE-PS blend that exhibits an excellent balance of nonhalogenated flame retardance, good chemical resistance, and low specifc gravity for light weight parts. The ..
Deflection Temperature at 1.8 MPa (264 psi) 119 °C

@Thickness 3.20 mm
246 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics NORYL FXN121BK PPE+HIPS
Noryl* FXN121BK is an unfilled modified polyphenylene ether resin suitable for injection molding. Designed to possess a unique low gloss surface appearance even when molded in polished tools, this r..
Deflection Temperature at 1.8 MPa (264 psi) 119 °C
246 °F
ISO 75-1, 2
Polyplastics TOPAS® 6013 Cyclic Olefin Copolymer (COC) (Asia/Pacific Grade)
Due to its high transparency, low levels of eluates, superior chemical resistance, and high heat deflection temperature, this grade is suitable for products such as pharmaceutical packaging and diag..
Deflection Temperature at 1.8 MPa (264 psi) 119 °C
246 °F
Absolute Drying; ASTM-D648
Toyobo GLAMIDE® NB-5550 Nylon/Olefin
GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Deflection Temperature at 1.8 MPa (264 psi) 119 °C
246 °F
unannealed; ISO 75
Chi Mei Wonderloy® PC-385 PC/ABS Alloy
Ultra-high Heat, Ultra-high Impact
Deflection Temperature at 1.8 MPa (264 psi) 119 °C
246 °F
ASTM D648
A. Schulman ComAlloy Hiloy® 262 Glass Reinforced, Modified SMA
Data provided by the manufacturer, ComAlloy International Company.20% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Deflection Temperature at 1.8 MPa (264 psi) 119 °C
246 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics Lexan® EXL1033C PC Copolymer
Lexan*EXL1033C polycarbonate (PC) siloxane copolymer resin is a low flow, UV stabilized grade designed for (co)-extrusion. This resin offers low temperature (-30C) ductility and excellent extrusion ..
Deflection Temperature at 1.8 MPa (264 psi) 119 °C
246 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics Lexan® FXG1413T PC Copolymer (Europe-Africa-Middle East)
PC-siloxane copolymer in special "Diamond Sparkle" colors. Medium flow. Improved toughness compared to medium flow standard PC in same color. Color package may affect performance.This data was supp..