Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | ASTM D648 |
Nylene® Norpex® AX300 PPE (Polyphenylene Ether); Premium Performance High Heat Properties for dry as molded samples.ALM, Nylene Canada, and Custom Resins are all operting companies of Polymeric Resources Corporation. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | ASTM D-648 |
PlastiComp Complet® LGF30 - PP Homopolymer Polypropylene, 30% Long Glass Fiber Reinforced Complēt® long-fiber reinforced pellets are manufactured to exceed expectation for quality and performance.Polypropylene with 30% long glass fiber reinforcementInformation provided by PlastiCom.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | Unannealed; ASTM D648 |
Oxford Polymers PC 30CF-925 Black PC, 30% Carbon Fiber Reinforced Product Description: Glass Fiber (30% Reinforced), PBT injection molding grade Processing and Delivery Form: Pellets and Injection MoldingAdditives: Release Agents Special Characteristics: High Str.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | Unannealed; ASTM D648 |
Ravago Manufacturing Americas Echo® RPC40G BK Polypropylene Homopolymer Available in North America Filler: Glass Fiber Reinforcement, 40% Filler by weight Recycled Content: YesFeatures: Homopolymer Color: Black Form: Pellets Information provided by Ravago |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 149 °C @Thickness 3.20 mm |
300 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
SABIC Innovative Plastics Lexan® FXM4701 PPC LEXAN FMX4701 is a high heat resistant poly(ester)carbonate injection molding resin. This grade is especially designed to visualize color effects.This data was supplied by SABIC-IP for the Americas .. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | ASTM D648 |
Plenco 204 Black General Purpose Woodflour/Mineral Filled Phenolic Molding Compound
(discontinued **) Plaslok 204 is a two-stage, woodflour and mineral-filled phenolic molding compound formulated to accommodate a wide range of molding situations. In addition, it is recommended for use in thin wall .. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | ASTM D648 |
Fiberfil® J-60/20/E8 Polypropylene Homopolymer, 20% Glass Reinforced, Chemically coupled Information provided by FIBERFIL Engineered Plastics |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | ASTM D648 |
Fiberfil® J-60/20/H Polypropylene Homopolymer, 20% Glass Reinforced, Chemically coupled Information provided by FIBERFIL Engineered Plastics |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
SABIC Innovative Plastics LNP LUBRICOMP WAL34I PBT (Europe-Africa-Middle East) LNP* LUBRICOMP* WAL34I is a compound based on Polybutylene Terephalate resin containing PTFE, Aramid Fiber. Added features include Internally Lubricated. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | Unannealed; ASTM D648 |
Techmer ES Electrablend® PC CF20 CR X 20% Carbon Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber Reinforcement, 20% Filler by WeightFeatures: Good Chemical Resistance and Semi ConductiveInformation provided by TP Compos.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | ASTM D648 |
Spartech PP5440 Glass Fiber Reinforced Homopolymer Provides the maximum strength and heat resistance among polypropylene compounds. Physical properties can approach those of more expensive engineering resins.Information provided by Spartech |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
SABIC Innovative Plastics LNP THERMOCOMP PH0460A PA 6 LNP* THERMOCOMP* PH0460A is a compound based on Nylon 6. Added feature of this material is: High Specific Gravity. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | Unannealed; ASTM D648 |
Teknor Apex Chemlon® 240 MH Nylon 6, 40% Short Glass Fiber Reinforced Features: Heat Stabilized; Warp Resistant Forms: Pellets Additive: Heat Stabilizer Automotive Specifications: GM GMP.PA6.011Information Provided by Teknor Apex |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
SABIC Innovative Plastics NORYL NH8006 PPE+HIPS Noryl* NH8006 resin is a 30% glass reinforced, modified PPE-PS blend. The material uses non-halogenated flame retardants to achieve a UL94 V0 flame rating (color specific) while offering an exceptio.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 149 °C @Thickness 3.20 mm |
300 °F @Thickness 0.126 in |
Unannealed; ASTM D648 |
Teknor Apex Sinpolene GPP1630 Polypropylene Availability: Africa & Middle East; Latin America; Asia Pacific; South America Additive: Glass Fiber Reinforcement, 30% Filler by Weight Features: Good Dimensional Stability; High Heat Resistance; .. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | ASTM D648 |
A. Schulman SCHULAMID® 66 MF40 Mineral Filled Nylon 66 Information provided by A. Schulman. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | ISO 75 |
Polyram Polytron P20B03 Polypropylene, 20% Long Glass Fiber A chemically coupled 20% long glass fibers reinforced black polypropylene, heat stabilized for injection molding applications.Information provided by Polyram. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | ASTM D648 |
Asahi Kasei Thermylene® P6-30FG-0699 30% Glass Fiber Reinforced, Heat Stabilized Information provided by Asahi Thermofil |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | ASTM D648 |
Ashley Polymers Ashlene® P266 PPO, 30% Glass Reinforced A general purpose, 30% glass reinforced PPO resin for injection molding applications.Data provided by the manufacturer |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | ASTM D648 |
A. Schulman SCHULAMID® 66 MF40 Mineral Filled Nylon 66 Information provided by A. Schulman. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 149 °C @Thickness 3.20 mm |
300 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics NORYL FE8000S PPE+PS (Europe-Africa-Middle East) Noryl* FE8000S resin is an unfilled modified polyphenylene ether resin designed for fluid handling applications. This resin is suitable for multiple conversion routes and will be available in custom.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 149 °C @Thickness 3.20 mm |
300 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics NORYL FE8000S PPE+PS Noryl* FE8000S resin is an unfilled modified polyphenylene ether resin designed for fluid handling applications. This resin is suitable for multiple conversion routes and will be available in custom.. |