- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 185 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 185 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C @Thickness 3.20 mm |
185 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycoloy® CY6120 PC+ABS Non-chlorinated and non-brominated flame retardant PC/ABS featuring good flow and impact properties. UL-94 V0 listed at 1.2mm intended for various thin wall applications. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 - 108 °C | 185 - 226 °F | Average value: 97.4 °C Grade Count:14 |
| Overview of materials for Acrylic, Heat Resistant, Molded This property data is a summary of similar materials in the MatWeb database for the category "Acrylic, Heat Resistant, Molded". Each property range of values reported is minimum and maximum values o.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ASTM D648 |
| Kolon KOPA® KN333HRBL Heat Resistant Nylon 66 Middle viscosity, BLACKApplications A variety of reservoir tanks and housingsInformation provided by API-Kolon. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ASTM D648 |
| Ineos Nova 5410 High Impact Polystyrene High impact, Good ESCR, Good printabilityApplications: Thermoformed containers and lids, Hot and cold beverages cups, Custom sheetProperties were determined on injection molded specimens at 23°C .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ISO 75 |
| GEHR Plastics PA 6.6 Nylon 6.6, Dry Polyamide shows both a high thermostability and high stiffness, hardness and toughness. These are some of the main characteristics. Due to the fact, that the good mechanical characteristics will be .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C @Thickness 12.7 mm |
185 °F @Thickness 0.500 in |
Unannealed; ASTM D648 |
| LG Chemical 25SPI GPPS High strength, Superior transparency and processability, good appearance, non-toxicity (Conforming to FDA CFR 177.1640), Excellent electrical properties, Heat resistance and chemical resistance, Sup.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | unannealed; ASTM D648 |
| KKPC Kuhmo HF400 Flame Retarded General Purpose HIPS Key features: Translucent Injection. Common Uses: TV and VCR housing.HIPS is a functional resin made by copolymerization of styrene monomer and PBR. It shows excellent balance between impact-resista.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRILOY R2000 PA 66 LNP* LUBRILOY* R2000 is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added feature of this material is: Wear Resistant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C @Thickness 3.20 mm |
185 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® 3706 PBT+PC Impact modified PBT+PC resin. Outdoor enclosure. Not available in all colors. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ASTM D648 |
| Spartech Acrylloy 7 Acrylic Sheet Description: Acrylic SheetInformation provided by Spartech. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | |
| Shinil Chemical SHINSTAT PMMA Electrostatic Control Polymer Injection Grade SHINSTAT is an Inherently Dissipative Polymer (IDP) compound which can discharge the electrostatic charge (ESD) effectively. Shinil has designed SHINSTAT using Shinil's patented IDP technology for .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | |
| Shinil Chemical SHINSTAT PP Electrostatic Control Polymer Sheet Grade SHINSTAT is an Inherently Dissipative Polymer (IDP) compound which can discharge the electrostatic charge (ESD) effectively. Shinil has designed SHINSTAT using Shinil's patented IDP technology for .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C @Thickness 3.20 mm |
185 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP AH0230A ABS (Europe-Africa-Middle East) LNP THERMOCOMP* AH0230A is a compound based on Acrylonitrile Butadiene Styrene resin. Added features of this material include: High Specific Gravity. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ASTM D648 |
| Techmer ES Plaslube® NY-1/TF/13/SI/2 Nylon 66, 13% PTFE, 2% Silicone Plaslube polytetrafluoroethylene (PTFE) lubricated nylon 66 grades offer the best wear and friction properties of any unreinforced, lubricated nylon compounds, making them ideal materials for bearin.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C @Thickness 6.35 mm |
185 °F @Thickness 0.250 in |
ASTM D648 |
| Samsung Cheil Industries Starex® SD-0150GP High Impact Grade ABS Information provided by Polymer Technology and Services, LLC (PTS). |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C @Thickness 6.40 mm |
185 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Starex® WR-9100 ASA, Unreinforced Information provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C @Thickness 3.20 mm |
185 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Stat-kon AD000Z ABS LNP* Stat-Kon AD000Z is a compound based on ABS resin with carbon powder. Grade characteristics: a statically conductive extrusion grade.This data was supplied by SABIC-IP for the Americas region... |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP STAT-KON FX98501 PE (Asia Pacific) LNP* Stat-kon* FX98501 is a compound based on Polyethylene resin containing Glass Fiber. Added features of this material include: Electrically Conductive. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C @Thickness 6.40 mm |
185 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Starex® BF-0679P MABS, Unreinforced Scratch Resistant Scratch resistant material that is used for the exterior material of flat TVInformation provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ASTM D648 |
| Tipco Tipcolene® FPT 30 BK CP - 30% Talc Polypropylene Homopolymer, Special Heat Stability 30% Talc Reinforced PP Homopolymer with Special AdditivesApplications: AutomotivesProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.,
India. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® TSS/4 LF 2 PA666 Product description: Grilon TSS/4 LF 2 is a heat stabilized, normal viscosity PA66 + PA6 injection molding grade with 2% lubricant (molybdenum disulphide). Grilon TSS/4 LF 2 has the following import.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | |
| Aclo Accutech Polypropylene Homopolymer HP0336M40CL Mica Reinforced Coupled |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ASTM D648 |
| Adell EQ-16 Homopolymer Polypropylene, 30% Mica Filled Data provided by Adell Plastics, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ASTM D648 |
| Asahi Kasei Xyron® 140V Modified Polyphenylene Ether Flame RetardantInformation provided by Asahi Kasei |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ASTM D648 |
| A. Schulman ComAlloy Comtuf® 618 Nylon 6, Mineral Reinforced, Impact Modified Data provided by the manufacturer, ComAlloy International Company.15% Mineral Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been i.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ASTM D648 |
| Asahi Kasei Thermofil P-20TC-Y118 20% Talc Reinforced, Heat Stabilized Information provided by Asahi Thermofil |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ASTM D648 |
| Ashley Polymers Ashlene® P268WO PPO An extrusion grade for general purpose application requiring flame retardancy and good impact resistance.Data provided by the manufacturer |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ASTM D648 |
| Ineos Nova 2581 General Purpose Crystal Polystyrene
(discontinued **) Good blending resin, Good balance of flow, strength and heat resistanceApplications: Consumer electronics, HousewaresExposure to gamma radiation in the 2.02-6.06 megarad range has no significant eff.. |
|||