Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 200 °C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	180 - 200 °C	356 - 392 °F	Injection; ISO 75-A
Raschig Group AMPLA® 2500 melamine-modified polyester Halogen-free, organically and inorganically filled melamine-modified Polyester molding compound. Excellent elasticity and shock resistance, low post-shrinkage, very good electrical values, high heat..
Deflection Temperature at 1.8 MPa (264 psi)	180 - 200 °C	356 - 392 °F	Injection; ISO 75-A
Raschig Group AMPLA® 7250 melamine-modified polyester Cellulose reinforced melamine-modified Polyester molding compound. Very good electrical values, excellent heat resistance, excellent surface quality, low post shrinkage. This product meets the allow..
Deflection Temperature at 1.8 MPa (264 psi)	180 - 200 °C	356 - 392 °F	Injection; ISO 75-A
Raschig Group AMPLA® 7500 melamine-modified polyester Organically and inorganically filled melamine modified Polyester molding compound. Low post-shrinkage, very good electrical values, excellent heat resistance, very good sliding behavior and wear sta..
Deflection Temperature at 1.8 MPa (264 psi)	70.0 - 200 °C	158 - 392 °F	Average value: 134 °C Grade Count:11
Overview of materials for PET + PBT Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "PET + PBT Unreinforced". Each property range of values reported is minimum and maximum values of appropr..
Deflection Temperature at 1.8 MPa (264 psi)	70.0 - 200 °C	158 - 392 °F	Average value: 129 °C Grade Count:20
Overview of materials for Nylon 6, 20% Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 20% Mineral Filled". Specific grades with primary filler content between 15% and 24% are includ..
Deflection Temperature at 1.8 MPa (264 psi)	56.0 - 200 °C	133 - 392 °F	Average value: 108 °C Grade Count:10
Overview of materials for Nylon 6, Mineral Reinforced, Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Mineral Reinforced, Impact Grade". Each property range of values reported is minimum and maximu..
Deflection Temperature at 1.8 MPa (264 psi)	180 - 200 °C	356 - 392 °F	ISO 75 Af
Vyncolit X658 Novolac Phenolic Glass fiber and mineral filled phenolic molding compound with excellent mechanical and thermal properties and a very good dimensional stability.USES: Complex precision parts.Information provided by ..