Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | ASTM D648 |
Niche Polymer PPCG20BK Copolymer PP, 20% Glass Fiber Filled Information provided by Niche Polymer |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | ASTM D648 |
Quadrant EPP Acetron® MD Metal-detectable Copolymer Acetal (ASTM Product Data Sheet) Low moisture absorption High strength, stiffness Easy to machine No centerline porosity in Acetron® GP Many formulation options: Copolymer, Homopolymer, PTFE filled, and Internally lubricated/enha.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | ASTM D648 |
Polymer Resources PC-HM-FR1-[color]-3 Polycarbonate, 10% Glass Reinforced, Flame Retardant, UV-stabilized Polycarbonate, 10% Glass Reinforced, Flame Retardant, UV-stabilizedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test sampl.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
SABIC Innovative Plastics LNP LUBRICOMP DFL349 PC (Asia Pacific) LNP LUBRICOMP* DFL349 is a compound based on Polycarbonate resin containing Flame Retardant, Glass Fiber, PTFE. Added features of this material include: Flame Retardant. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
SABIC Innovative Plastics LNP LUBRICOMP DFL349EF PC LNP LUBRICOMP* DFL349EF is a compound based on Polycarbonate resin containing 20% Glass Fiber, 15% PTFE. Added features of this material include: Flame Retardant, Internally Lubricated. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
SABIC Innovative Plastics LNP LUBRICOMP DFL12 PC LNP* Lubricomp* DFL12 is a compound based on Polycarbonate resin containing 10% Glass Fiber and 5% PTFE. Added features include: Internally Lubricated. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
SABIC Innovative Plastics LNP LUBRICOMP DFL349 PC LNP LUBRICOMP* DFL349 is a compound based on Polycarbonate resin containing 20% Glass Fiber, 15% PTFE. Added features of this material include: Flame Retardant, Internally Lubricated. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 138 °C @Thickness 3.20 mm |
280 °F @Thickness 0.126 in |
ASTM D648 |
Kingfa JH720 G15 15% Glass Fiber Reinforced PC Features:Excellent balance propertiesHigh mechanical propertiesHigh stiffnessGood size stabilityGood surfaceApplications:Imaging equipment shellOA body frameElectrical equipmentComputer plug partsIn.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | >= 138 °C @Thickness 6.40 mm |
>= 280 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
LG Chemical LUPOY GN2101F PC+GF10%, Halogen Free, Flame Retardant, Heat Resistance Description: Injection Molding, PC+GF10%, Halogen Free Flame Retardant, Heat ResistanceApplication: IT/OA, Electric & Electronic Housing and ComponentsCAS: 103598-77-2 and 65997-17-3Information prov.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
SABIC Innovative Plastics LNP LUBRICOMP KZL16 Acetal Copolymer (Europe-Africa-Middle East) LNP* LUBRICOMP* KZL16 is a compound based on Acetal Copolymer resin containing milled Glass and PTFE. Added features include; Internally Lubricated. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 138 °C @Thickness 3.20 mm |
280 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics LNP STAT-KON DX01303C PC LNP STAT-KON* DX01303C is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | ASTM D648 |
Shuman 980-05V0 Grey Polycarbonate Glass Filled Easy processability, heat resistance, weatherability, color stability, self extinguishing5% glass fiber for foam moldingInformation provided by Shuman Plastics, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
SABIC Innovative Plastics LNP THERMOCOMP DF0029R PC (Europe-Africa-Middle East) LNP* Thermocomp* DF0029R is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: Mold Release, Flame Retardant. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
SABIC Innovative Plastics LNP Thermocomp DF008P PC LNP THERMOCOMP* DF008P is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Exceptional Processing.This data was supplied by SABIC-IP for the .. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 138 °C @Thickness 3.20 mm |
280 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics NORYL NH7112 PPE+HIPS Noryl* NH7112 resin is a 10% glass reinforced, modified PPE-PS blend. The material offers an exceptional balance of strength and dimensional stability while using non-halogenated flame retardants to.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
SABIC Innovative Plastics Noryl GFN1430V PPE+PS (Asia Pacific) Noryl* GFN1430V PolyPhenylene Oxide (PPO*) + Polystyrene (PS) resin is a 30 % Glass Reinforced, injection moldable grade with improved hydrolytic stability. This grade has been developed for potable.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | ASTM D648 |
A. Schulman ComAlloy® 510-3010 10% Glass Fiber Reinforced Polycarbonate Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | ASTM D648 |
A. Schulman SCHULADUR® A GB30 30% Glass Bead Reinforced PBT Information provided by A. Schulman. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | annealed; ASTM D648 |
Lubrizol ISOPLAST™ 202EZ Engineering Thermoplastic Polyurethane Resin NSF Standard 61 CertifiedAvailable in Americas, Europe, Middle East, Africa, India and AsiaInformation provided by LubrizolLubrizol acquired the Isoplast product line from Dow in 2009. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | ASTM D648 |
A. Schulman ComAlloy® 510-3010 10% Glass Fiber Reinforced Polycarbonate Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | ASTM D648 |
A. Schulman SCHULADUR® A GB30 30% Glass Bead Reinforced PBT Information provided by A. Schulman. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | |
Covestro Makrolon® 9125 Polycarbonate Medium viscosity, flame retardant extrusion and injection molding grade with 20% standard glass fibers and easy mold release agent.Information provided by Bayer.As of 1 September 2015, Bayer Materia.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | ASTM D648, ISO 75 |
EPICHEM Epilon PC UVR Polycarbonate, High Impact Characteristics: high fluidity, high impact, UV resistant |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | ASTM D648 |
A. Schulman ComAlloy Voloy® 113 Polypropylene, Glass Reinforced, Chemically Coupled, Flame Retardant, UL Data provided by the manufacturer, ComAlloy International Company.25% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | Annealed, 0.125 in bars; ASTM D648 |
PolyOne Lubri-Tech™ MP-10GF/10T Modified Polyphenylene Oxide (mPPO), Glass Filled, PTFE Lubricated
(discontin Description/Features:Glass Fiber ReinforcedPTFE LubricatedUL 94 HB (HEM TEST)PolyOne First ChoiceInformation provided by PolyOne Corporation. |