- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 329 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 329 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | ISO 75, ASTM D648 |
| Nilit Nilamon A3 H K8 40% Mineral Reinforced PA66 Description: Nilamon A3 H K8 combines good stiffness with low warpage. It is used for applications which need a degree of rigidity, particularly at higher temperatures, but which need to stay flat a.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C @Thickness 3.20 mm |
329 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® XHT4141 PC Copolymer (Europe-Africa-Middle East) XHT4141 is a high flow, high heat polycarbonate copolymer. It is available in a range of opaque and limited transparent colors. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C @Thickness 3.20 mm |
329 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® XHT4143 PC Copolymer (Asia Pacific) XHT4143 is a high flow, UV stabilized, high heat polycarbonate copolymer blend with an HDT/Af of 162C. It is available in a range of opaque and limited transparent colors. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C @Thickness 3.20 mm |
329 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® XHT4143T PC Copolymer (Asia Pacific) XHT4143 is a high flow, UV stabilized, high heat polycarbonate copolymer blend with an HDT/Af of 162C. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | ISO 75-1/-2 |
| DuPont Performance Polymers Crastin® LW9320 BK851 PBT
(Unverified Data**) Crastin® LW9320 BK851 is a 20% glass fiber reinforced, black polybutylene terephthalate alloy for injection molding. It has improved surface aesthetics, excellent dimensional stability and low warp.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYform POM C M90 GF30 Polyoxymethylene Information provided by Polykemi AB |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | |
| Lehmann & Voss LUVOCOM® 80-7713 Polyacetal-copolymer, with carbon fiber and PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Electrically conductive, suita.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | |
| Lehmann & Voss LUVOCOM® 80-7713-NA Polyacetal-copolymer, with carbon fiber and PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Electrically conductive, suita.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C @Thickness 6.40 mm |
329 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical LUCEL GC240 POM+GF40%, High Rigidity Feature: Injection Molding, POM+GF40%, High RigidityApplication: Casings of Pump and Pivot BearingsCAS No. 66455-31-0 and 65997-17-3Information provided by LG Chemical |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP HF004 PA 11 LNP* Thermocomp* HF004 is a compound based on Nylon 11 resin containing 20% Glass Fiber. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C @Thickness 3.20 mm |
329 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL HH180 PPE+PS Noryl* HH180 is a high heat, unfilled modified polyphenylene ether resin with a Vicat B/120 temperature of 185 deg C. Noryl HH180 is only available in color 80365. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C @Thickness 3.20 mm |
329 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL HH180 PPE+PS (Asia Pacific) Noryl* HH180 is a high heat, unfilled modified polyphenylene ether resin with a Vicat B/120 temperature of 185 deg C. Noryl HH180 is only available in color 80365. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics NORYL HH180 PPE+PS (Europe-Africa-Middle East) Noryl* HH180 is a high heat, unfilled modified polyphenylene ether resin with a Vicat B/120 temperature of 185 deg C. Noryl HH180 is only available in color 80365. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C @Thickness 6.40 mm |
329 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Ultem ATX103R PEI+PCE (Europe-Africa-Middle East) 30% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing in recognized colors.This data was supplied by SABIC-IP for the Europe-Afr.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | ISO 75-93 |
| Wellman Wellamid® MR410 22H-GY1 40% Mineral Reinforced Nylon 66 Description: Mineral Reinforced Nylon 66Information provided by Wellman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® 1SBVX-30H LDS black PA1010-GF30 Product Description: Grilamid 1SBVX-30H LDS black is a 30% glass fiber reinforced Polyamide 1010 injection molding grade. This grade is specifically optimized for the laser Direct Structuring techno.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® LV-3 X ESD black PA12-GF30 Grilamid LV-3 X ESD black is an antistatic Polyamide 12 for injection molding with 30% glass fiber reinforcement. Main attributes are: antistatic with resistivity < 106 Ohmgood fuel and zinc chlorid.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® LV-50H FWA black 9225 PA12-GF50 Product description: Grilamid LV-50H FWA black 9225 is a 50 % glass fiber reinforced, heat stabilized polyamide 12 injection molding grade with the following special features: High stiffness combine.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | ISO 75-1/-2 |
| DuPont Performance Polymers Crastin® LW9320LM BK591 PBT+SAN
(Unverified Data**) 20% Glass Reinforced Polybutylene Terephthalate Blend with Low Warpage Characteristics Crastin LW9320LM is a 20% glass fiber reinforced polybutylene terephthalate blend for injection molding. It ha.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | ASTM D648, ISO 75 |
| EPICHEM PA 6/66 GF 30 Polyamide 6/66, 30% Glass Characteristics: 30% glass fibre filled |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Eurostar Star L PA66 D61 PA66, Injection Molded Star L PA66 D51 is a PTFE/Silicone Oil Lubricated, Unreinforced, Polyamide 66 Injection Molding ResinInformation provided by Eurostar. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Ae |
| Eurostar Staramide BT6 PA6, 30% Mineral Filled, Injection Molded Staramide BT6 is a 30% Mineral Filled, Polyamide 6, Injection Molding ResinInformation provided by Eurostar. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® LC-3H black PA12-CF30 Product description: Grilamid LC-3H BLACK is a Polyamide 12 injection molding product reinforced with 30 % carbon fibers. The product is inherently black and is only available in this color.Main Att.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | |
| Arkema Group Rilsan® AZM 23 G9 T6LD Nylon 12, 23% Glass Fiber Filled (Conditioned) Designation ISO 1874-PA12,MHLR,16-050,(G+C)(F+D)(23+05)Rigid grade with glass fiber (23%) and graphite filler for injection molding. Available color: steel black gray. Reinforced light and heat stab.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | ISO 75-1/-2 |
| BASF Ultramid® FRee B3U31G4 20% Glass Filled PA66 FR (Dry) Description: Halogen-free and phosphorus free flame retardant injection-molding grade with outstanding free-flow properties, good electrical properties and low smoke density; resistant to glow wire.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | ASTM D648 |
| Ashley Polymers Ashlene® D925LH-30G Nylon 12, 30% Glass Reinforced, Lubricated A 30% glass reinforced lubricated heat and light stabilized Nylon 12. Options: D925L-30G injection molding grade, without heat and light stabilizer; and D925L-30GB for injection molding, general pu.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | injection molded unannealed; ASTM D-648-95 |
| Multibase Multi-ABS 3245 FR Flame Retardant ABS Data provided by Multibase. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | ASTM D648 |
| E-Polymers SEPAZ® LH60 PP Homopolymer LFT Resin Long Fiber Thermoplastics: SEPAZ LFT products, injection moldable long fiber-reinforced thermoplastics (LFT), are made using a unique pultrusion that thoroughly wets out the glass fibers and deliver.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | ISO 75-2/Af |
| Radici Raditer® B RVA 200 Polybutylene Terephthalate with 20% Glass fiber Raditer® B RVA is a range of glass fiber reinforced Polybutylene terephthalate blends for injection molding, with excellent dimensional stability, low warpage and good surface aspect.Information pr.. |
|||