Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 358 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 181 °C
358 °F
Unannealed; ASTM D648
Solvay Specialty Polymers Udel® GF-130 Polysulfone (PSU)  (Unverified Data**)
Udel GF-130, resin is a 30% glass fiber reinforced polysulfone compound. Glass fiber substantially increases the rigidity, tensile strength, creep resistance, dimensional stability and chemical resi..
Deflection Temperature at 1.8 MPa (264 psi) 181 °C
358 °F
Unannealed; ASTM D648
LNP Thermocomp® GF-1006 Polysulfone, Glass Fiber Reinforcement  (discontinued **)
Forms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names..
Deflection Temperature at 1.8 MPa (264 psi) 181 °C
358 °F
ISO 75-1/-2
Lanxess Durethan® DP BM 65 X FM30 901510 Nylon 6, 65% Mineral + Glass Fiber
PA, injection molding and hybrid grade based on PA 6, 65% mineral/glass fibers, UL 94V-0 at 1.2 mm, reduced cycle times (easy flow), Thin wall application, free from halogen and phosphorous, low smo..
Deflection Temperature at 1.8 MPa (264 psi) 181 °C

@Thickness 3.20 mm
358 °F

@Thickness 0.126 in
unannealed; ASTM D 648
SABIC Innovative Plastics LNP Lubricomp GFL14 PSU
LNP* Lubricomp* GFL14 is a compound based on Polysulfone containing Glass Fiber and PTFE Lubricant.This data was supplied by SABIC-IP for the Americas region.
Deflection Temperature at 1.8 MPa (264 psi) 181 °C
358 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP LUBRICOMP GFL36L PSU (Asia Pacific)
LNP* Lubricomp* GFL36L is a compound based on Polysulfone resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Low Extractible.
Deflection Temperature at 1.8 MPa (264 psi) 181 °C

@Thickness 3.20 mm
358 °F

@Thickness 0.126 in
Annealed; ASTM D648
Solvay Specialty Polymers AvaSpire® AV-630 Polyaryletherketone (PAEK)
AvaSpire® AV-630 is an unreinforced polyaryletherketone (PAEK) developed as an alternative to low melt flow PEEK for the extrusion of ultra-thin films. Films with thicknesses as low as 0.2 mils (..
Deflection Temperature at 1.8 MPa (264 psi) 181 °C
358 °F
Unannealed; ASTM D648
Solvay Specialty Polymers Udel® GF-130 Polysulfone (PSU), Glass Fiber
Udel® GF-130, resin is a 30% glass fiber reinforced polysulfone compound. Glass fiber substantially increases the rigidity, tensile strength, creep resistance, dimensional stability and chemical ..
Deflection Temperature at 1.8 MPa (264 psi) 181 °C
358 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP Thermocomp GC006XXZ PSU
LNP THERMOCOMP* GC006XXZ is a compound based on Polysulfone resin containing Carbon Fiber.This product is also known as Thermocomp* GC-1006.This data was supplied by SABIC-IP for the Americas region..
Deflection Temperature at 1.8 MPa (264 psi) 181 °C

@Thickness 3.20 mm
358 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP THERMOCOMP GF006 PSU
LNP THERMOCOMP* GF006 is a compound based on Polysulfone resin containing 30% Glass Fiber.
Deflection Temperature at 1.8 MPa (264 psi) 181 °C

@Thickness 3.20 mm
358 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP THERMOCOMP GF006XXZ PSU
LNP THERMOCOMP* GF006XXZ is a compound based on Polysulfone resin containing 30% Glass Fiber.
Deflection Temperature at 1.8 MPa (264 psi) 181 °C
358 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP STAT-LOY PF303 PA 6
LNP* STAT-LOY* PF303 is a Nylon 6 base resin containing 15% Glass Fiber. Added features of this grade includes: Antistat.
Deflection Temperature at 1.8 MPa (264 psi) 181 °C
358 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP THERMOCOMP IF003 PA 6/12
LNP THERMOCOMP* IF003 is a compound based on Nylon 6/12 resin containing 15% Glass Fiber.
Deflection Temperature at 1.8 MPa (264 psi) 181 °C
358 °F
Unannealed; ASTM D648
Techmer ES HiFill® TPX-HTN-03003 A 40% Mineral Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Mineral Filler, 40% Filler by WeightFeatures: Platable and High Temperature StrengthUL File Number: E157318Information provided by TP C..
Deflection Temperature at 1.8 MPa (264 psi) 181 °C
358 °F
ASTM D648
Plenco 5350 Phenolic, Granular, Injection Molded
PLENCO 05350 is a mineral and graphite filled phenolic molding compound, developed for seal applications. PLENCO 05350 offers excellent dimensional stability, lubricity, and low abrasion properties...
Deflection Temperature at 1.8 MPa (264 psi) 181 °C

@Thickness 3.20 mm
358 °F

@Thickness 0.126 in
Annealed; 2 hours at 200°C; ASTM D648
Solvay Specialty Polymers AvaSpire® AV-630 Polyaryletherketone (PAEK)  (Unverified Data**)
AvaSpire AV-630 is an unreinforced polyaryletherketone (PAEK) developed as an alternative to low melt flow PEEK for the extrusion of ultra-thin films. Films with thicknesses as low as 0.2 mils (5 mi..
Deflection Temperature at 1.8 MPa (264 psi) 181 °C
358 °F
ASTM D648
LATI LASULF G/30 30% Glass Reinforced Polysulfone (PSU)  (Unverified Data**)
Description: Lasulf products are composed of polysulfone (PSU). They feature good thermal and mechanical properties such as excellent toughness, even at low temperatures, excellent dimensional stabi..
Deflection Temperature at 1.8 MPa (264 psi) 181 °C
358 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP LUBRICOMP GFL36L PSU
LNP* Lubricomp* GFL36L is a compound based on Polysulfone resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Internally Lubricated, Low Extractible.